EN 10088-1 X39CrMo17-1: Premium Quenched & Tempered Steel (+QT750)

Material X39CrMo17-1 is comparable to X 35 CrMo 17 acc. to SEW 400 : 1991-02. It is a heat treatable Cr-steel with increased corrosion resistance, largely resistant to many organic and inorganic acids, relatively resistant to seawater. Excellent operating characateristics and wear resistance. Application for pump shafts, spindles, axles, fittings, beater bars. Improved resistance to crevice corrosion, increased thermal resistance up to 600 °C. The steel is mirror finishable. Different heat treatment grades have to be chosen for parts sliding on each other. Application temperature -40 to 550 °C (for the comparable DIN-material) No forming is designated.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.56 - 7.7 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

20.0 °C

215 - 218 GPa

100.0 °C

212 - 213 GPa

200.0 °C

205 - 206 GPa

300.0 °C

198 - 200 GPa

400.0 °C

190 GPa

500.0 °C

180 GPa

600.0 °C

167 GPa

700.0 °C

150 GPa

Elongation

20.0 °C

8 - 12 %

Poisson's ratio

23.0 °C

0.3 [-]

Typical for Martensitic Stainless Steel

Shear modulus

23.0 °C

77 GPa

Typical for Martensitic Stainless Steel

Tensile strength

20.0 °C

750 - 1050 MPa

Yield strength Rp0.2

20.0 °C

550 - 650 MPa

100.0 °C

540 MPa

150.0 °C

535 MPa

200.0 °C

530 MPa

250.0 °C

520 MPa

300.0 °C

510 MPa

350.0 °C

490 MPa

400.0 °C

470 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

20.0 °C

9.9E-6 1/K

100.0 °C

1.03E-5 - 1.04E-5 1/K

200.0 °C

1.08E-5 1/K

300.0 °C

1.12E-5 1/K

400.0 °C

1.16E-5 1/K

500.0 °C

1.19E-5 1/K

600.0 °C

1.21E-5 1/K

700.0 °C

1.24E-5 1/K

800.0 °C

1.29E-5 1/K

Max service temperature, long

-40 - 550 °C

Melting point

1370 - 1530 °C

Typical for Martensitic Stainless Steel

Specific heat capacity

20.0 °C

430 - 450 J/(kg·K)

100.0 °C

482 J/(kg·K)

200.0 °C

506 J/(kg·K)

300.0 °C

525 J/(kg·K)

400.0 °C

547 J/(kg·K)

500.0 °C

576 J/(kg·K)

600.0 °C

616 J/(kg·K)

Thermal conductivity

20.0 °C

15 - 16 W/(m·K)

100.0 °C

17.2 W/(m·K)

200.0 °C

18.6 W/(m·K)

300.0 °C

20 W/(m·K)

400.0 °C

21.2 W/(m·K)

500.0 °C

22.3 W/(m·K)

600.0 °C

23.3 W/(m·K)

700.0 °C

24.1 W/(m·K)

800.0 °C

25.5 W/(m·K)

900.0 °C

26.9 W/(m·K)

1000.0 °C

28.3 W/(m·K)

Thermal diffusivity

20.0 °C

4.7 mm²/s

100.0 °C

4.5 mm²/s

200.0 °C

4.5 mm²/s

300.0 °C

4.6 mm²/s

400.0 °C

4.4 mm²/s

500.0 °C

4.1 mm²/s

600.0 °C

3.6 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

8E-7 - 9.06E-7 Ω·m

100.0 °C

9.42E-7 Ω·m

200.0 °C

9.87E-7 Ω·m

300.0 °C

1.03E-6 Ω·m

400.0 °C

1.08E-6 Ω·m

500.0 °C

1.12E-6 Ω·m

600.0 °C

1.18E-6 Ω·m

700.0 °C

1.22E-6 Ω·m

800.0 °C

1.24E-6 Ω·m

900.0 °C

1.26E-6 Ω·m

1000.0 °C

1.27E-6 Ω·m

Chemical properties

PropertyValue

Carbon

0.33 - 0.45 %

Chromium

15.5 - 17.5 %

Manganese

1.5 %

Molybdenum

0.8 - 1.3 %

Nickel

1 %

Phosphorus

0.04 %

Silicon

1 %

Sulfur

0.015 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10088-1 Grade X3CrNiMo13-4 – High-Performance Quenched & Tempered (QT650) Stainless Steel
    2. EN 10088‑1 Certified X12CrS13 Quenched & Tempered Steel – Superior Machinability
    3. EN 10088-1 Grade X29CrS13 Quenched & Tempered (QT850) – Superior Martensitic Stainless Steel
    4. X12Cr13 Quenched & Tempered Steel (QT650) – EN 10088‑1 Certified, High‑Temperature Resistant
    5. EN 10088-1 X46Cr13 Steel – Quenched & Tempered (QT850) for Cutting Tools & High-Performance Components
    6. EN 10088‑1 Grade X30Cr13 – Quenched & Tempered (QT850) – Durable Cutting Tool Steel
    7. EN 10088-1 Grade X39Cr13 – Quenched & Tempered (QT800) Steel for Cutting Tools & Bearings
    8. EN 10088‑1 Grade X17CrNi16‑2 – Quenched & Tempered (QT800) – High‑Performance Stainless Steel
    9. EN 10088-1 Grade X20Cr13 Quenched & Tempered Steel – Durable, Corrosion-Resistant for High-Load Applications
    10. EN 10088-1 Grade X2CrNi12: High-Performance Quenched and Tempered Ferritic Steel