EN 10083-2 Grade C40E – Normalized or Normalized Formed Steel for High-Temperature Applications

Steel C40E is suitable for heat-resistant screws and larger forged parts as well as for parts of more complex form (e.g. gear wheels, camshafts) in vehicle manufacturing and machine engineering. As a bright steel product it is used in the form of bars, bright, straight, in different conditions (see DIN EN 10277).

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.82 - 7.85 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

210 - 212 GPa

100.0 °C

205 - 207 GPa

200.0 °C

195 - 199 GPa

300.0 °C

185 - 192 GPa

400.0 °C

175 - 184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Elongation

20.0 °C

16 - 17 %

Poisson's ratio

23.0 °C

0.29 [-]

Typical for Medium Carbon Steel

Shear modulus

20.0 °C

81 GPa

Tensile strength

20.0 °C

530 - 580 MPa

Yield strength

20.0 °C

260 - 320 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.08E-5 1/K

20.0 °C

1.19E-5 1/K

100.0 °C

1.11E-5 - 1.25E-5 1/K

200.0 °C

1.21E-5 - 1.3E-5 1/K

300.0 °C

1.29E-5 - 1.36E-5 1/K

400.0 °C

1.35E-5 - 1.41E-5 1/K

500.0 °C

1.45E-5 1/K

600.0 °C

1.49E-5 1/K

Max service temperature

500 °C

Typical for Carbon Steel

Melting point

1380 - 1514 °C

Typical for Medium Carbon Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 - 480 J/(kg·K)

100.0 °C

479 - 500 J/(kg·K)

200.0 °C

499 - 550 J/(kg·K)

300.0 °C

517 - 590 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

48 - 52 W/(m·K)

100.0 °C

48.9 - 50.6 W/(m·K)

200.0 °C

47.5 - 48.1 W/(m·K)

300.0 °C

44.7 - 45.7 W/(m·K)

400.0 °C

41.6 W/(m·K)

500.0 °C

38.6 W/(m·K)

600.0 °C

35.5 W/(m·K)

Thermal diffusivity

20.0 °C

13.3 mm²/s

100.0 °C

12.6 mm²/s

200.0 °C

11.5 mm²/s

300.0 °C

10.2 mm²/s

400.0 °C

8.9 mm²/s

500.0 °C

7.5 mm²/s

600.0 °C

6 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

1.2E-7 - 2.17E-7 Ω·m

100.0 °C

2.62E-7 Ω·m

200.0 °C

3.32E-7 Ω·m

300.0 °C

4.2E-7 Ω·m

400.0 °C

5.23E-7 Ω·m

500.0 °C

6.41E-7 Ω·m

600.0 °C

7.8E-7 Ω·m

Chemical properties

PropertyValue

Carbon

0.37 - 0.44 %

Chromium

0.4 %

Copper

0.3 %

Manganese

0.5 - 0.8 %

Molybdenum

0.1 %

Nickel

0.4 %

Phosphorus

0.03 %

Silicon

0.1 - 0.4 %

Sulfur

0.035 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10083‑2 Grade C60R: Normalized & Normalized‑Formed Steel for High‑Load Applications
    2. EN 10083-2 Grade 28Mn6: Normalized or Normalized Formed Steel for Automotive and Machine Components
    3. EN 10083-2 Grade C45R Normalized or Normalized Formed Steel (+N) – Ideal for Automotive & Machine Components
    4. EN 10083-2 Grade C50R: Normalized or Formed Steel for High Workability and Strength
    5. EN 10083-2 Grade C55R - Normalized or Normalized Formed Steel for High-Performance Applications
    6. EN 10083-2 Grade C55 Normalized Steel for High-Load, Wear-Resistant Applications
    7. EN 10083-2 Grade C60: Normalized or Normalized-Formed Steel for High-Strength Applications
    8. EN 10083-2 Grade C55E: Normalized/Normalized Formed Steel for Heavy‑Duty Applications
    9. EN 10083-2 Grade C60E – Normalized/Normalized Formed Steel for Heavy-Duty Applications
    10. EN 10083-2 Grade C35E – Normalized/Normalized Formed Steel for Vehicle & Machine Engineering