EN 10083-2 Grade C35E – Normalized/Normalized Formed Steel for Vehicle & Machine Engineering

Steel C35E is suitable for slightly higher loaded components with higher dimensions (large forged parts) and more complex form as well as higher demands on uniformity of qualities and surface appearance in vehicle manufacturing and machine engineering (e.g. transmissin parts, crankshafts). As a bright steel product it is used in the form of bars, bright, straight, in different conditions (see DIN EN 10277).

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.82 - 7.85 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

210 - 212 GPa

100.0 °C

205 - 207 GPa

200.0 °C

195 - 199 GPa

300.0 °C

185 - 192 GPa

400.0 °C

175 - 184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Elongation

20.0 °C

18 - 22 %

Elongation, transverse

20.0 °C

12 - 15 %

Poisson's ratio

23.0 °C

0.29 [-]

Typical for Medium Carbon Steel

Shear modulus

20.0 °C

81 GPa

Tensile strength

20.0 °C

490 - 610 MPa

Yield strength

20.0 °C

245 - 300 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.08E-5 1/K

20.0 °C

1.19E-5 1/K

100.0 °C

1.11E-5 - 1.25E-5 1/K

200.0 °C

1.21E-5 - 1.3E-5 1/K

300.0 °C

1.29E-5 - 1.36E-5 1/K

400.0 °C

1.35E-5 - 1.41E-5 1/K

500.0 °C

1.45E-5 1/K

600.0 °C

1.49E-5 1/K

Max service temperature

500 °C

Typical for Carbon Steel

Max service temperature, long

-25 - 480 °C

Melting point

1380 - 1514 °C

Typical for Medium Carbon Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

460 - 461 J/(kg·K)

100.0 °C

479 - 480 J/(kg·K)

200.0 °C

499 - 520 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 - 610 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

48 - 50 W/(m·K)

100.0 °C

48.9 - 51 W/(m·K)

200.0 °C

47.5 - 48.2 W/(m·K)

300.0 °C

44.7 - 45.6 W/(m·K)

400.0 °C

41.6 W/(m·K)

500.0 °C

38.6 W/(m·K)

600.0 °C

35.5 W/(m·K)

Thermal diffusivity

20.0 °C

13.3 mm²/s

100.0 °C

12.6 mm²/s

200.0 °C

11.5 mm²/s

300.0 °C

10.2 mm²/s

400.0 °C

8.9 mm²/s

500.0 °C

7.5 mm²/s

600.0 °C

6 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

1.2E-7 - 2.17E-7 Ω·m

100.0 °C

2.62E-7 Ω·m

200.0 °C

3.32E-7 Ω·m

300.0 °C

4.2E-7 Ω·m

400.0 °C

5.23E-7 Ω·m

500.0 °C

6.41E-7 Ω·m

600.0 °C

7.8E-7 Ω·m

Chemical properties

PropertyValue

Carbon

0.32 - 0.39 %

Chromium

0.4 %

Copper

0.3 %

Manganese

0.5 - 0.8 %

Molybdenum

0.1 %

Nickel

0.4 %

Phosphorus

0.03 %

Silicon

0.1 - 0.4 %

Sulfur

0.035 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10083‑2 Grade C60R: Normalized & Normalized‑Formed Steel for High‑Load Applications
    2. EN 10083-2 Grade 28Mn6: Normalized or Normalized Formed Steel for Automotive and Machine Components
    3. EN 10083-2 Grade C40E – Normalized or Normalized Formed Steel for High-Temperature Applications
    4. EN 10083-2 Grade C45R Normalized or Normalized Formed Steel (+N) – Ideal for Automotive & Machine Components
    5. EN 10083-2 Grade C50R: Normalized or Formed Steel for High Workability and Strength
    6. EN 10083-2 Grade C55R - Normalized or Normalized Formed Steel for High-Performance Applications
    7. EN 10083-2 Grade C55 Normalized Steel for High-Load, Wear-Resistant Applications
    8. EN 10083-2 Grade C60: Normalized or Normalized-Formed Steel for High-Strength Applications
    9. EN 10083-2 Grade C55E: Normalized/Normalized Formed Steel for Heavy‑Duty Applications
    10. EN 10269 Grade C35E – Normalized or Normalized Formed Steel for Heavy‑Duty Applications