EN 10277-5 Grade C60R: High-Strength Cold-Drawn, Quenched & Tempered Steel
Steel C60R is suitable for high loaded parts in vehicle, engine and machine engineering with enhanced workability at constant strength qualities (e.g. gear wheels, pinions, shafts). Lowest application temperature -25°C. As a bright steel product it is used in the form of bars, bright, straight, in various conditions (see DIN EN 10277 : 1999-10).
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 7.85 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 20.0 °C | 210 GPa | |
100.0 °C | 205 GPa | ||
200.0 °C | 195 GPa | ||
300.0 °C | 185 GPa | ||
400.0 °C | 175 GPa | ||
Elongation | 20.0 °C | 13 - 14 % | |
Poisson's ratio | 23.0 °C | 0.29 [-] | Typical for High Carbon Steel |
Shear modulus | 20.0 °C | 81 GPa | |
Tensile strength | 20.0 °C | 750 - 950 MPa | |
Yield strength Rp0.2 | 20.0 °C | 450 - 520 MPa | |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 100.0 °C | 1.11E-5 1/K | |
200.0 °C | 1.21E-5 1/K | ||
300.0 °C | 1.29E-5 1/K | ||
400.0 °C | 1.35E-5 1/K | ||
Max service temperature | 500 °C | Typical for Carbon Steel | |
Max service temperature, long | -25 - 0 °C | ||
Melting point | 1289 - 1478 °C | Typical for High Carbon Steel | |
Specific heat capacity | 23.0 °C | 486 J/(kg·K) | Typical for High Carbon Steel |
Thermal conductivity | 20.0 °C | 51 W/(m·K) | |
100.0 °C | 49.9 W/(m·K) | ||
200.0 °C | 47.8 W/(m·K) | ||
300.0 °C | 44.8 W/(m·K) | ||
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical resistivity | 20.0 °C | 1.3E-7 Ω·m |
Chemical properties
| Property | Value |
|---|---|
Carbon | 0.57 - 0.65 % |
Chromium | 0.4 % |
Manganese | 0.6 - 0.9 % |
Molybdenum | 0.1 % |
Nickel | 0.4 % |
Phosphorus | 0.03 - 0.04 % |
Silicon | 0.4 % |
Sulfur | 0.02 - 0.04 % |
Metal
- EN 10277-5 Grade 42CrMoS4 – Premium Cold‑Drawn, Quenched & Tempered Steel for High‑Load Automotive & Machinery
- EN 10277-5 Grade 34CrS4 Cold-Drawn, Quenched & Tempered Steel – Premium Performance for Automotive & Machinery
- 41CrS4 Cold‑Drawn, Quenched & Tempered Steel – EN 10277‑5 Specification for Automotive & Machine Components
- EN 10277‑5 Grade 51CrV4 Cold‑Drawn, Quenched & Tempered Steel (+C+QT) – High‑Performance Alloy for Aerospace & Heavy Machinery
- EN 10277-5 Grade C60R – Quenched, Tempered & Cold Drawn Steel for High-Load Applications
- EN 10277-5 25CrMoS4 Cold‑Drawn, Quenched & Tempered Steel for High‑Strength Applications
- Grade 34CrNiMo6 Cold Drawn, Quenched & Tempered Steel – EN 10277‑5
- EN 10277-5 Grade C50E: Cold‑Drawn, Quenched & Tempered Steel for Heavy Engineering Applications
- EN 10277-5 Grade C50R Cold Drawn, Quenched, and Tempered Steel (C+QT) – High Strength & Workability
- EN 10277-5 Grade C60E Steel – Cold Drawn, Quenched & Tempered (+C+QT)