EN 10277-5 Grade C60E Steel – Cold Drawn, Quenched & Tempered (+C+QT)

Steel C60E is suitable for larger parts (heavy forged parts) of high load in vehicle, engine and machine engineering. Surface hardenable (e.g. crankshafts, bolts, transmission parts). Lowest application temperature -25°C. As a bright steel product it is used in the form of bars, bright, straight, in various conditions (see DIN EN 10277 : 1999-10).

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.8 - 7.85 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

210 - 212 GPa

100.0 °C

205 - 207 GPa

200.0 °C

195 - 199 GPa

300.0 °C

185 - 192 GPa

400.0 °C

175 - 184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Elongation

20.0 °C

13 - 14 %

Poisson's ratio

23.0 °C

0.29 [-]

Typical for High Carbon Steel

Shear modulus

20.0 °C

81 GPa

Tensile strength

20.0 °C

750 - 950 MPa

Yield strength Rp0.2

20.0 °C

450 - 520 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.08E-5 1/K

20.0 °C

1.19E-5 1/K

100.0 °C

1.11E-5 - 1.25E-5 1/K

200.0 °C

1.21E-5 - 1.3E-5 1/K

300.0 °C

1.29E-5 - 1.36E-5 1/K

400.0 °C

1.35E-5 - 1.41E-5 1/K

500.0 °C

1.45E-5 1/K

600.0 °C

1.49E-5 1/K

Max service temperature

500 °C

Typical for Carbon Steel

Max service temperature, long

-25 - 0 °C

Melting point

1289 - 1478 °C

Typical for High Carbon Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

41.7 - 51 W/(m·K)

100.0 °C

43.4 - 49.9 W/(m·K)

200.0 °C

43.2 - 47.8 W/(m·K)

300.0 °C

41.4 - 44.8 W/(m·K)

400.0 °C

39.1 W/(m·K)

500.0 °C

36.7 W/(m·K)

600.0 °C

34.1 W/(m·K)

Thermal diffusivity

20.0 °C

11.6 mm²/s

100.0 °C

11.3 mm²/s

200.0 °C

10.5 mm²/s

300.0 °C

9.5 mm²/s

400.0 °C

8.3 mm²/s

500.0 °C

7.1 mm²/s

600.0 °C

5.8 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

1.3E-7 - 2.5E-7 Ω·m

100.0 °C

2.95E-7 Ω·m

200.0 °C

3.65E-7 Ω·m

300.0 °C

4.53E-7 Ω·m

400.0 °C

5.56E-7 Ω·m

500.0 °C

6.74E-7 Ω·m

600.0 °C

8.13E-7 Ω·m

Chemical properties

PropertyValue

Carbon

0.57 - 0.65 %

Chromium

0.4 %

Manganese

0.6 - 0.9 %

Molybdenum

0.1 %

Nickel

0.4 %

Phosphorus

0.03 - 0.04 %

Silicon

0.4 %

Sulfur

0.035 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10277-5 Grade 42CrMoS4 – Premium Cold‑Drawn, Quenched & Tempered Steel for High‑Load Automotive & Machinery
    2. EN 10277-5 Grade 34CrS4 Cold-Drawn, Quenched & Tempered Steel – Premium Performance for Automotive & Machinery
    3. 41CrS4 Cold‑Drawn, Quenched & Tempered Steel – EN 10277‑5 Specification for Automotive & Machine Components
    4. EN 10277‑5 Grade 51CrV4 Cold‑Drawn, Quenched & Tempered Steel (+C+QT) – High‑Performance Alloy for Aerospace & Heavy Machinery
    5. EN 10277-5 Grade C60R: High-Strength Cold-Drawn, Quenched & Tempered Steel
    6. EN 10277-5 25CrMoS4 Cold‑Drawn, Quenched & Tempered Steel for High‑Strength Applications
    7. Grade 34CrNiMo6 Cold Drawn, Quenched & Tempered Steel – EN 10277‑5
    8. EN 10277-5 Grade C50E: Cold‑Drawn, Quenched & Tempered Steel for Heavy Engineering Applications
    9. EN 10277-5 Grade C50R Cold Drawn, Quenched, and Tempered Steel (C+QT) – High Strength & Workability
    10. Grade C60E Steel – Quenched, Tempered & Cold‑Drawn for High‑Load Applications