ISO 683-4 Grade 35S20 Steel – Quenched & Tempered (QT) for Automotive & Machinery

The free-cutting steel 35S20, suitable for quenching and tempering, is used for bulk parts of mean strength, especially for lower requirements to ductility in transversal direction opposite to comparable C-steels (e.g. C35). Increased cutting speed represents an advantage, the increased cracking risk at rising C-content has to be considered. Application in automotive engineering, as well as in apparatus equipment and machine engineering (e.g. screws, nuts, small-size parts).

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.8 - 7.85 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

210 - 212 GPa

100.0 °C

207 GPa

200.0 °C

193 - 199 GPa

300.0 °C

185 - 192 GPa

400.0 °C

175 - 184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Elongation

20.0 °C

15 - 17 %

Poisson's ratio

20.0 °C

0.28 [-]

Shear modulus

20.0 °C

81 GPa

Tensile strength

20.0 °C

550 - 780 MPa

Yield strength

20.0 °C

320 - 430 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.08E-5 1/K

20.0 °C

1.19E-5 1/K

100.0 °C

1.1E-5 - 1.25E-5 1/K

200.0 °C

1.18E-5 - 1.3E-5 1/K

300.0 °C

1.36E-5 1/K

400.0 °C

1.32E-5 - 1.41E-5 1/K

500.0 °C

1.45E-5 1/K

600.0 °C

1.49E-5 1/K

Max service temperature

500 °C

Typical for Carbon Steel

Melting point

1380 - 1514 °C

Typical for Medium Carbon Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

420 - 461 J/(kg·K)

100.0 °C

479 - 490 J/(kg·K)

200.0 °C

499 - 530 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 - 610 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

44.9 - 49 W/(m·K)

100.0 °C

46.2 W/(m·K)

200.0 °C

45.5 W/(m·K)

300.0 °C

43.1 W/(m·K)

400.0 °C

40.4 W/(m·K)

500.0 °C

37.7 W/(m·K)

600.0 °C

34.9 W/(m·K)

Thermal diffusivity

20.0 °C

12.5 mm²/s

100.0 °C

12 mm²/s

200.0 °C

11 mm²/s

300.0 °C

9.8 mm²/s

400.0 °C

8.6 mm²/s

500.0 °C

7.3 mm²/s

600.0 °C

5.9 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

1.2E-7 - 2.32E-7 Ω·m

100.0 °C

2.77E-7 Ω·m

200.0 °C

3.47E-7 Ω·m

300.0 °C

4.35E-7 Ω·m

400.0 °C

5.38E-7 Ω·m

500.0 °C

6.56E-7 Ω·m

600.0 °C

7.95E-7 Ω·m

Chemical properties

PropertyValue

Carbon

0.32 - 0.39 %

Manganese

0.7 - 1.1 %

Phosphorus

0.06 %

Silicon

0.4 %

Sulfur

0.15 - 0.25 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10137-2 Grade S890QL – High-Strength Quenched & Tempered Steel for Heavy-Duty Applications
    2. EN 10137-3 Grade S500A: Quenched & Tempered Fine‑Grained Steel for Structural Applications
    3. EN 10083-1 Grade 51CrV4: Quenched & Tempered Steel (QT)
    4. EN 10213 Grade G17CrMo9-10 – Quenched & Tempered (QT) Steel for High-Temperature Applications
    5. EN 10085 Grade 15 CrMoV 5.9: Quenched & Tempered Steel for Durable Machine Components
    6. EN 10085 Grade 31CrMo12 – High-Performance Quenched & Tempered Steel for Heavy‑Duty Applications
    7. ISO 683-4 Grade 35SPb20 – Quenched & Tempered Steel for Automotive & Machinery Parts
    8. ISO 683-4 Grade 38SMn28 Quenched & Tempered Steel: High-Strength Free-Cutting Material
    9. ISO 683-4 Grade 38SMnPb28: Quenched & Tempered Free‑Cutting Steel for Superior Machinability
    10. ISO 683-1 Grade C22E – High-Performance Quenched & Tempered Steel for Heavy-Duty Applications