EN 10028-3 Grade P460N – Normalized & Stress-Relieved Sheet Steel Properties
Properties
General
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Density | 20 °C | 7.84 g/cm³ | normalized and stress-relieved | EN 10028-3 | Sheet |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Elastic modulus | -100 °C | 217 GPa | normalized and stress-relieved | EN 10028-3 | Sheet | |
20 °C | 200 - 212 GPa | normalized and stress-relieved | EN 10028-3 | Sheet | ||
20 °C | 200 GPa | normalized and stress-relieved | EN 10028-3 | Sheet | ||
20 °C | 212 GPa | normalized and stress-relieved | EN 10028-3 | Sheet | ||
100 °C | 207 GPa | normalized and stress-relieved | EN 10028-3 | Sheet | ||
200 °C | 199 GPa | normalized and stress-relieved | EN 10028-3 | Sheet | ||
300 °C | 192 GPa | normalized and stress-relieved | EN 10028-3 | Sheet | ||
400 °C | 184 GPa | normalized and stress-relieved | EN 10028-3 | Sheet | ||
500 °C | 175 GPa | normalized and stress-relieved | EN 10028-3 | Sheet | ||
600 °C | 164 GPa | normalized and stress-relieved | EN 10028-3 | Sheet | ||
Poisson's ratio | 20 °C | 0.29 [-] | normalized and stress-relieved | EN 10028-3 | Sheet | |
Shear modulus | 82 GPa | Typical for Low Carbon Steel |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Coefficient of thermal expansion | -100 °C | 1.05e-05 1/K | normalized and stress-relieved | EN 10028-3 | Sheet | |
20 °C | 1.15e-05 1/K | normalized and stress-relieved | EN 10028-3 | Sheet | ||
100 °C | 1.21e-05 1/K | normalized and stress-relieved | EN 10028-3 | Sheet | ||
200 °C | 1.27e-05 1/K | normalized and stress-relieved | EN 10028-3 | Sheet | ||
300 °C | 1.32e-05 1/K | normalized and stress-relieved | EN 10028-3 | Sheet | ||
400 °C | 1.36e-05 1/K | normalized and stress-relieved | EN 10028-3 | Sheet | ||
500 °C | 1.4e-05 1/K | normalized and stress-relieved | EN 10028-3 | Sheet | ||
600 °C | 1.44e-05 1/K | normalized and stress-relieved | EN 10028-3 | Sheet | ||
Max service temperature | 500 °C | Typical for Carbon Steel | ||||
Melting point | 1480 - 1526 °C | Typical for Low Carbon Steel | ||||
Specific heat capacity | -100 °C | 423 J/(kg·K) | normalized and stress-relieved | EN 10028-3 | Sheet | |
20 °C | 461 J/(kg·K) | normalized and stress-relieved | EN 10028-3 | Sheet | ||
100 °C | 479 J/(kg·K) | normalized and stress-relieved | EN 10028-3 | Sheet | ||
200 °C | 499 J/(kg·K) | normalized and stress-relieved | EN 10028-3 | Sheet | ||
300 °C | 517 J/(kg·K) | normalized and stress-relieved | EN 10028-3 | Sheet | ||
400 °C | 536 J/(kg·K) | normalized and stress-relieved | EN 10028-3 | Sheet | ||
500 °C | 558 J/(kg·K) | normalized and stress-relieved | EN 10028-3 | Sheet | ||
600 °C | 587 J/(kg·K) | normalized and stress-relieved | EN 10028-3 | Sheet | ||
Thermal conductivity | -100 °C | 34.7 W/(m·K) | normalized and stress-relieved | EN 10028-3 | Sheet | |
20 °C | 39.7 W/(m·K) | normalized and stress-relieved | EN 10028-3 | Sheet | ||
100 °C | 40.9 W/(m·K) | normalized and stress-relieved | EN 10028-3 | Sheet | ||
200 °C | 41 W/(m·K) | normalized and stress-relieved | EN 10028-3 | Sheet | ||
300 °C | 39.9 W/(m·K) | normalized and stress-relieved | EN 10028-3 | Sheet | ||
400 °C | 38.2 W/(m·K) | normalized and stress-relieved | EN 10028-3 | Sheet | ||
500 °C | 36.1 W/(m·K) | normalized and stress-relieved | EN 10028-3 | Sheet | ||
600 °C | 33.8 W/(m·K) | normalized and stress-relieved | EN 10028-3 | Sheet | ||
Thermal diffusivity | -100 °C | 11.9 mm²/s | normalized and stress-relieved | EN 10028-3 | Sheet | |
20 °C | 11 mm²/s | normalized and stress-relieved | EN 10028-3 | Sheet | ||
100 °C | 10.5 mm²/s | normalized and stress-relieved | EN 10028-3 | Sheet | ||
200 °C | 9.9 mm²/s | normalized and stress-relieved | EN 10028-3 | Sheet | ||
300 °C | 9.1 mm²/s | normalized and stress-relieved | EN 10028-3 | Sheet | ||
400 °C | 8.1 mm²/s | normalized and stress-relieved | EN 10028-3 | Sheet | ||
500 °C | 6.9 mm²/s | normalized and stress-relieved | EN 10028-3 | Sheet | ||
600 °C | 5.7 mm²/s | normalized and stress-relieved | EN 10028-3 | Sheet |
Electrical
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Electrical resistivity | -100 °C | 1.97e-07 Ω·m | normalized and stress-relieved | EN 10028-3 | Sheet |
20 °C | 2.62e-07 Ω·m | normalized and stress-relieved | EN 10028-3 | Sheet | |
100 °C | 3.13e-07 Ω·m | normalized and stress-relieved | EN 10028-3 | Sheet | |
200 °C | 3.85e-07 Ω·m | normalized and stress-relieved | EN 10028-3 | Sheet | |
300 °C | 4.7e-07 Ω·m | normalized and stress-relieved | EN 10028-3 | Sheet | |
400 °C | 5.69e-07 Ω·m | normalized and stress-relieved | EN 10028-3 | Sheet | |
500 °C | 6.85e-07 Ω·m | normalized and stress-relieved | EN 10028-3 | Sheet | |
600 °C | 8.2e-07 Ω·m | normalized and stress-relieved | EN 10028-3 | Sheet |
Magnetic
| Property | Value | Comment |
|---|---|---|
Curie temperature | 770 °C | Typical for Low Carbon Steel |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Aluminium | 0.005 % | normalized and stress-relieved | EN 10028-3 | Sheet |
Carbon | 0.2 | normalized and stress-relieved | EN 10028-3 | Sheet |
Chromium | 0.3 | normalized and stress-relieved | EN 10028-3 | Sheet |
Copper | 0.2 | normalized and stress-relieved | EN 10028-3 | Sheet |
Manganese | 1 - 1.7 % | normalized and stress-relieved | EN 10028-3 | Sheet |
Molybdenum | 0.1 | normalized and stress-relieved | EN 10028-3 | Sheet |
Nickel | 0.4 | normalized and stress-relieved | EN 10028-3 | Sheet |
Nitrogen | 0.025 | normalized and stress-relieved | EN 10028-3 | Sheet |
Phosphorus | 0.03 | normalized and stress-relieved | EN 10028-3 | Sheet |
Silicon | 0.1 - 0.6 % | normalized and stress-relieved | EN 10028-3 | Sheet |
Sulfur | 0.02 | normalized and stress-relieved | EN 10028-3 | Sheet |
Vanadium | 0.1 - 0.2 % | normalized and stress-relieved | EN 10028-3 | Sheet |
Metal
- ASTM A757 Grade E3N: Normalized & Tempered Martensitic Stainless Steel
- ASTM A473 Grade S41500 Stainless Steel – Normalized & Tempered Properties
- ASTM A182 Grade F115 – Normalized & Tempered Austenitic Stainless Steel
- ASTM A182 Grade F6NM – High-Strength Normalized & Tempered Stainless Steel
- EN 10222-3 Grade 12Ni14 – High-Performance Nickel Alloy for Cryogenic Applications
- EN 10222-3 X8Ni9: High‑Performance Nickel Alloy for Cryogenic Applications
- ASTM A290 Grade 1 Class A: Normalized & Tempered Steel – Specifications & Properties
- EN 10028-3 Grade P275N – Fine‑Grained Steel for Boilers & Pressure Vessels (Normalized or Normalized Formed +N)
- EN 10217-3: P460N Fine-Grain Structural Steel – Normalized or Normalized Formed (+N)
- EN 10216‑3 P460N Steel – Normalized/Normalized‑Formed, Ideal for Pressure Vessels