EN 10277-5 Grade 30CrMoV9: Cold-Drawn, Turned, Quenched & Tempered Steel for High-Strength Applications

Steel 30 CrMoV 9 is suitable for parts of high strength and ductility requirements at mean and higher heat-treatment sections in vehicle manufacturing, engine and machine engineering (e.g. crankshafts, jointed shafts, spindles). Furthermore application to nitride steel. Lowest application temp. -40 °C.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.8 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

212 GPa

100.0 °C

207 GPa

200.0 °C

199 GPa

300.0 °C

192 GPa

400.0 °C

184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Elongation

20.0 °C

9 - 10 %

Poisson's ratio

23.0 °C

0.29 [-]

Typical for Chromium Molybdenum Steel

Reduction of area

20.0 °C

35 - 40 %

Tensile strength

20.0 °C

1100 - 1450 MPa

Yield strength

20.0 °C

900 - 1050 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.05E-5 1/K

20.0 °C

1.15E-5 1/K

100.0 °C

1.21E-5 1/K

200.0 °C

1.27E-5 1/K

300.0 °C

1.32E-5 1/K

400.0 °C

1.36E-5 1/K

500.0 °C

1.4E-5 1/K

600.0 °C

1.44E-5 1/K

Max service temperature, long

-40 - 0 °C

Melting point

1382 - 1529 °C

Typical for Chromium Molybdenum Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

33.7 W/(m·K)

100.0 °C

36.2 W/(m·K)

200.0 °C

37.8 W/(m·K)

300.0 °C

37.2 W/(m·K)

400.0 °C

35.7 W/(m·K)

500.0 °C

34 W/(m·K)

600.0 °C

32 W/(m·K)

Thermal diffusivity

20.0 °C

9.4 mm²/s

100.0 °C

9.4 mm²/s

200.0 °C

9.2 mm²/s

300.0 °C

8.5 mm²/s

400.0 °C

7.6 mm²/s

500.0 °C

6.6 mm²/s

600.0 °C

5.4 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

3.09E-7 Ω·m

100.0 °C

3.54E-7 Ω·m

200.0 °C

4.18E-7 Ω·m

300.0 °C

5.05E-7 Ω·m

400.0 °C

6.09E-7 Ω·m

500.0 °C

7.27E-7 Ω·m

600.0 °C

8.67E-7 Ω·m

Chemical properties

PropertyValue

Carbon

0.26 - 0.34 %

Chromium

2.3 - 2.7 %

Manganese

0.4 - 0.7 %

Molybdenum

0.15 - 0.25 %

Phosphorus

0.04 %

Silicon

0.4 %

Sulfur

0.03 %

Vanadium

0.1 - 0.2 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. High-Strength 25CrMo4 Steel – EN 10277-5 Cold-Drawn, Turned, Quenched & Tempered
    2. EN 10277‑5: 25CrMoS4 Cold‑Drawn, Quenched & Tempered – Premium High‑Strength Steel for Automotive & Engine Parts
    3. EN 10277-5 Grade 28Cr4: High‑Strength Cold Drawn or Turned Steel, Quenched and Tempered
    4. EN 10277-5 Grade 34CrS4 Cold-Drawn or Turned Steel – Quenched & Tempered for Vehicle and Engine Applications
    5. EN 10277-5 Grade 36CrNiMo4 – Cold-Drawn, Turned, Quenched & Tempered Steel for High-Performance Applications
    6. EN 10277-5 Grade 37Cr4: Premium Cold-Drawn & Quenched Steel for High-Performance Automotive & Machine Parts
    7. EN 10277-5 Grade 37CrS4: High-Performance Cold-Drawn, Quenched, and Tempered Steel for Automotive & Machinery Applications
    8. EN 10277-5 Grade 38Cr2 – Cold‑Drawn, Quenched & Tempered Steel for High‑Strength Automotive Components
    9. EN 10277-5 Grade 38CrS2: High-Strength Cold-Drawn, Turned, Quenched & Tempered Steel
    10. EN 10277‑5 Grade 41Cr4 Steel – Cold‑Drawn, Turned, Quenched & Tempered