EN 10084 Grade C10R Quenched Steel – Premium Gear Material
The case-hardening steel is mainly used for gear parts, but also in the mechanical engineering.
Properties
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 23.0 °C | 7.8 - 7.9 g/cm³ | Typical for Low Carbon Steel |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 200 - 215 GPa | Typical for Low Carbon Steel |
Poisson's ratio | 23.0 °C | 0.29 [-] | Typical for Low Carbon Steel |
Shear modulus | 23.0 °C | 82 GPa | Typical for Low Carbon Steel |
Tensile strength | 20.0 °C | 400 - 500 MPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.32E-5 - 1.38E-5 1/K | Typical for Low Carbon Steel |
Max service temperature | 500 °C | Typical for Carbon Steel | |
Melting point | 1480 - 1526 °C | Typical for Low Carbon Steel | |
Specific heat capacity | 23.0 °C | 465 J/(kg·K) | Typical for Low Carbon Steel |
Thermal conductivity | 23.0 °C | 25 - 93 W/(m·K) | Typical for Low Carbon Steel |
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Electrical resistivity | 23.0 °C | 1.43E-7 - 1.74E-7 Ω·m | Typical for Carbon Steel |
Magnetic
| Property | Value | Comment |
|---|---|---|
Curie temperature | 770 °C | Typical for Low Carbon Steel |
Chemical properties
| Property | Value |
|---|---|
Carbon | 0.07 - 0.13 % |
Chromium | 0.4 % |
Copper | 0.3 % |
Manganese | 0.3 - 0.6 % |
Molybdenum | 0.1 % |
Nickel | 0.4 % |
Phosphorus | 0.03 % |
Silicon | 0.15 - 0.4 % |
Sulfur | 0.02 - 0.04 % |
Metal
- EN 10084 Grade 22CrMoS3-5 – Quenched Steel for High-Durability Automotive & Machine Components
- EN 10084 Grade 20NiCrMoS2-2 Quenched Steel – High Performance for Automotive & Machine Components
- EN 10084 Grade 17Cr3 Quenched Steel – High Wear‑Resistant Parts for Automotive and Machinery
- EN 10084 Grade 20NiCrMo2-2 – Quenched (Q) High-Performance Steel for Automotive & Machinery
- EN 10084 Grade 20MoCr4 Steel – Quenched for Superior Wear Resistance
- EN 10084 C16R Quenched Steel – High‑Performance Material for Gears & Mechanical Components
- EN 10084 Grade C16E Quenched Steel: Superior Gear and Mechanical Engineering Performance
- EN 10084 C15R Steel – Quenched for High‑Strength, Wear‑Resistant Applications
- EN 10084 Grade C10E Quenched Steel – Enhanced Wear Resistance & Low-Core Strength
- EN 10084 Grade C15E Quenched Steel (+Q) – Enhanced Strength & Durability for Automotive & Machinery Applications