EN 10084 Grade 17Cr3 Quenched Steel – High Wear‑Resistant Parts for Automotive and Machinery

Steel 17Cr3 is suitable for parts of lower dimension in vehicle manufacturing and machine engineering requiring a high wear resistance (e.g. camshafts, piston bolts, cylinder).

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.82 - 7.85 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

210 - 212 GPa

100.0 °C

207 GPa

200.0 °C

195 - 199 GPa

300.0 °C

185 - 192 GPa

400.0 °C

184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Poisson's ratio

23.0 °C

0.29 [-]

Typical for Chromium Steel

Shear modulus

20.0 °C

81 GPa

Tensile strength

20.0 °C

600 - 800 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.08E-5 1/K

20.0 °C

1.19E-5 1/K

100.0 °C

1.1E-5 - 1.25E-5 1/K

200.0 °C

1.12E-5 - 1.3E-5 1/K

300.0 °C

1.25E-5 - 1.36E-5 1/K

400.0 °C

1.41E-5 1/K

500.0 °C

1.45E-5 1/K

600.0 °C

1.49E-5 1/K

Melting point

1382 - 1529 °C

Typical for Chromium Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

460 - 461 J/(kg·K)

100.0 °C

479 - 480 J/(kg·K)

200.0 °C

499 - 520 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

39.6 - 44 W/(m·K)

100.0 °C

41 - 41.9 W/(m·K)

200.0 °C

39.8 - 41 W/(m·K)

300.0 °C

39.9 W/(m·K)

400.0 °C

38.1 W/(m·K)

500.0 °C

35.9 W/(m·K)

600.0 °C

33.6 W/(m·K)

Thermal diffusivity

20.0 °C

11 mm²/s

100.0 °C

10.6 mm²/s

200.0 °C

9.9 mm²/s

300.0 °C

9 mm²/s

400.0 °C

8.1 mm²/s

500.0 °C

6.9 mm²/s

600.0 °C

5.7 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

1.6E-7 - 2.63E-7 Ω·m

100.0 °C

3.12E-7 Ω·m

200.0 °C

3.85E-7 Ω·m

300.0 °C

4.7E-7 Ω·m

400.0 °C

5.71E-7 Ω·m

500.0 °C

6.88E-7 Ω·m

600.0 °C

8.25E-7 Ω·m

Chemical properties

PropertyValue

Carbon

0.14 - 0.2 %

Chromium

0.7 - 1 %

Copper

0.4 %

Manganese

0.6 - 0.9 %

Phosphorus

0.03 %

Silicon

0.15 - 0.4 %

Sulfur

0.035 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10084 Grade 22CrMoS3-5 – Quenched Steel for High-Durability Automotive & Machine Components
    2. EN 10084 Grade 20NiCrMoS2-2 Quenched Steel – High Performance for Automotive & Machine Components
    3. EN 10084 Grade 20NiCrMo2-2 – Quenched (Q) High-Performance Steel for Automotive & Machinery
    4. EN 10084 Grade 20MoCr4 Steel – Quenched for Superior Wear Resistance
    5. EN 10084 Grade C10R Quenched Steel – Premium Gear Material
    6. EN 10084 C16R Quenched Steel – High‑Performance Material for Gears & Mechanical Components
    7. EN 10084 Grade C16E Quenched Steel: Superior Gear and Mechanical Engineering Performance
    8. EN 10084 C15R Steel – Quenched for High‑Strength, Wear‑Resistant Applications
    9. EN 10084 Grade C10E Quenched Steel – Enhanced Wear Resistance & Low-Core Strength
    10. EN 10084 Grade C15E Quenched Steel (+Q) – Enhanced Strength & Durability for Automotive & Machinery Applications