EN 10084 Grade C10E Quenched Steel – Enhanced Wear Resistance & Low-Core Strength

Steel C10E is suitable for lower dimension parts of low core strength and increased wear load as well as for parts of higher dimension and complexer forms than standard mark C10 in vehicle manufacturing and machine engineering (e.g. levers, bushings, molded and stamped parts).

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.85 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

210 - 212 GPa

100.0 °C

205 - 207 GPa

200.0 °C

193 - 199 GPa

300.0 °C

185 - 192 GPa

400.0 °C

175 - 184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Poisson's ratio

23.0 °C

0.29 [-]

Typical for Low Carbon Steel

Shear modulus

20.0 °C

81 GPa

Tensile strength

20.0 °C

400 - 500 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.08E-5 1/K

20.0 °C

1.19E-5 1/K

100.0 °C

1.1E-5 - 1.25E-5 1/K

200.0 °C

1.18E-5 - 1.3E-5 1/K

300.0 °C

1.36E-5 1/K

400.0 °C

1.32E-5 - 1.41E-5 1/K

500.0 °C

1.45E-5 1/K

600.0 °C

1.49E-5 1/K

Max service temperature

500 °C

Typical for Carbon Steel

Melting point

1480 - 1526 °C

Typical for Low Carbon Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

460 - 461 J/(kg·K)

100.0 °C

479 - 480 J/(kg·K)

200.0 °C

499 - 520 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

57.5 - 58.7 W/(m·K)

100.0 °C

54.4 - 55.7 W/(m·K)

200.0 °C

50.2 - 51.9 W/(m·K)

300.0 °C

47.6 W/(m·K)

400.0 °C

43.4 - 44 W/(m·K)

500.0 °C

39.6 W/(m·K)

600.0 °C

36 W/(m·K)

Thermal diffusivity

20.0 °C

15.9 mm²/s

100.0 °C

14.3 mm²/s

200.0 °C

12.5 mm²/s

300.0 °C

10.8 mm²/s

400.0 °C

9.2 mm²/s

500.0 °C

7.6 mm²/s

600.0 °C

6.1 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

1.1E-7 Ω·m

100.0 °C

2.3E-7 Ω·m

200.0 °C

3.04E-7 Ω·m

300.0 °C

3.94E-7 Ω·m

400.0 °C

5.01E-7 Ω·m

500.0 °C

6.25E-7 Ω·m

600.0 °C

7.7E-7 Ω·m

Magnetic

PropertyValueComment

Curie temperature

770 °C

Typical for Low Carbon Steel

Chemical properties

PropertyValue

Carbon

0.07 - 0.13 %

Chromium

0.4 %

Copper

0.3 %

Manganese

0.3 - 0.6 %

Molybdenum

0.1 %

Nickel

0.4 %

Phosphorus

0.03 %

Silicon

0.15 - 0.4 %

Sulfur

0.035 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10084 Grade 22CrMoS3-5 – Quenched Steel for High-Durability Automotive & Machine Components
    2. EN 10084 Grade 20NiCrMoS2-2 Quenched Steel – High Performance for Automotive & Machine Components
    3. EN 10084 Grade 17Cr3 Quenched Steel – High Wear‑Resistant Parts for Automotive and Machinery
    4. EN 10084 Grade 20NiCrMo2-2 – Quenched (Q) High-Performance Steel for Automotive & Machinery
    5. EN 10084 Grade 20MoCr4 Steel – Quenched for Superior Wear Resistance
    6. EN 10084 Grade C10R Quenched Steel – Premium Gear Material
    7. EN 10084 C16R Quenched Steel – High‑Performance Material for Gears & Mechanical Components
    8. EN 10084 Grade C16E Quenched Steel: Superior Gear and Mechanical Engineering Performance
    9. EN 10084 C15R Steel – Quenched for High‑Strength, Wear‑Resistant Applications
    10. EN 10084 Grade C15E Quenched Steel (+Q) – Enhanced Strength & Durability for Automotive & Machinery Applications