DIN 17460 Grade X6CrNi18-11 – Solution-Annealed High-Temperature Steel for Reactor and Chemical Applications

-100.0 °C

206 GPa

20.0 °C

196 - 198 GPa

100.0 °C

190 - 192 GPa

200.0 °C

182 - 184 GPa

300.0 °C

174 - 175 GPa

400.0 °C

166 - 167 GPa

500.0 °C

158 - 159 GPa

600.0 °C

150 GPa

700.0 °C

142 GPa

800.0 °C

134 GPa

900.0 °C

127 GPa

1000.0 °C

120 GPa

20.0 °C

185 MPa

100.0 °C

157 MPa

200.0 °C

127 MPa

300.0 °C

108 MPa

400.0 °C

98 MPa

500.0 °C

88 MPa

550.0 °C

83 MPa

600.0 °C

78 MPa

20.0 °C

225 MPa

100.0 °C

191 MPa

200.0 °C

157 MPa

300.0 °C

137 MPa

400.0 °C

127 MPa

500.0 °C

118 MPa

550.0 °C

113 MPa

600.0 °C

108 MPa

-100.0 °C

1.49E-5 1/K

20.0 °C

1.61E-5 1/K

100.0 °C

1.63E-5 - 1.67E-5 1/K

200.0 °C

1.69E-5 - 1.72E-5 1/K

300.0 °C

1.73E-5 - 1.77E-5 1/K

400.0 °C

1.78E-5 - 1.81E-5 1/K

500.0 °C

1.82E-5 - 1.84E-5 1/K

600.0 °C

1.85E-5 - 1.88E-5 1/K

700.0 °C

1.87E-5 - 1.91E-5 1/K

800.0 °C

1.94E-5 1/K

900.0 °C

1.97E-5 1/K

1000.0 °C

2E-5 1/K

-100.0 °C

440 J/(kg·K)

20.0 °C

450 - 472 J/(kg·K)

100.0 °C

487 J/(kg·K)

200.0 °C

503 J/(kg·K)

300.0 °C

512 J/(kg·K)

400.0 °C

520 J/(kg·K)

500.0 °C

530 J/(kg·K)

600.0 °C

541 J/(kg·K)

700.0 °C

551 J/(kg·K)

800.0 °C

559 J/(kg·K)

900.0 °C

565 J/(kg·K)

1000.0 °C

571 J/(kg·K)

20.0 °C

14.3 - 17 W/(m·K)

100.0 °C

15.8 W/(m·K)

200.0 °C

17.5 W/(m·K)

300.0 °C

19 W/(m·K)

400.0 °C

20.5 W/(m·K)

500.0 °C

21.9 W/(m·K)

600.0 °C

23.3 W/(m·K)

700.0 °C

24.6 W/(m·K)

800.0 °C

26 W/(m·K)

900.0 °C

27.4 W/(m·K)

1000.0 °C

28.8 W/(m·K)

20.0 °C

3.8 mm²/s

100.0 °C

4 mm²/s

200.0 °C

4.2 mm²/s

300.0 °C

4.6 mm²/s

400.0 °C

4.8 mm²/s

500.0 °C

4.9 mm²/s

600.0 °C

5 mm²/s

700.0 °C

5.3 mm²/s

800.0 °C

5.6 mm²/s

900.0 °C

5.9 mm²/s

1000.0 °C

6 mm²/s