X2CrNiMoN22-5-3 Solution-Annealed Steel (Grade DIN 5512-3) – Ideal for Rail Vehicle Components
The steel is used for rail vehicle engineering acc. to the selected standard DIN 5512-3. The corresponding properties of EN 10088 shall be taken. Application examples: bearing components, reinforcing parts, skin panels Remarks: Remarkable tool wear in the case of machining. Resistant to intercrystalline corrosion in the delivery and the welded condition.
Quantity: 220,00€Additional services: Processing in our productsALLEIMA (FORMERLY SANDVIK MATERIALS TECHNOLOGY)
MANUFACTURER
Information and services
Additional services: To ensure our customers' processes and/or products attain – and even exceed – their performance expectations, we offer a wide range of services within both the technical area and delivery logistics. Our technical services include: • Material consultations through our worldwide sales network • Advice in process optimization based on an in-depth applications knowledge • Joint new product development supported by our extensive R&D program View product groups and servicesProperties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 7.8 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 20.0 °C | 200 - 212 GPa | |
100.0 °C | 194 - 206 GPa | ||
200.0 °C | 186 GPa | ||
300.0 °C | 180 GPa | ||
Elongation | 20.0 °C | 12 - 25 % | |
Elongation A80, transverse | 20.0 °C | 20 - 25 % | |
Elongation, transverse | 20.0 °C | 20 - 25 % | |
Hardness, Brinell | 20.0 °C | 270 [-] | |
Poisson's ratio | 23.0 °C | 0.3 [-] | Typical for Duplex Stainless Steel |
Shear modulus | 23.0 °C | 77 GPa | Typical for Duplex Stainless Steel |
Tensile strength | 20.0 °C | 650 - 1150 MPa | |
Tensile strength, transverse | 20.0 °C | 640 - 950 MPa | |
Yield strength Rp0.2 | 20.0 °C | 450 - 650 MPa | |
100.0 °C | 360 MPa | ||
150.0 °C | 335 MPa | ||
200.0 °C | 315 MPa | ||
250.0 °C | 300 MPa | ||
Yield strength Rp0.2, transverse | 20.0 °C | 460 - 500 MPa | |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 100.0 °C | 1.3E-5 - 1.33E-5 1/K | |
200.0 °C | 1.35E-5 1/K | ||
300.0 °C | 1.4E-5 1/K | ||
Max service temperature | 300 °C | Typical for Duplex Stainless Steel | |
Melting point | 1375 - 1450 °C | Typical for Duplex Stainless Steel | |
Specific heat capacity | 20.0 °C | 500 J/(kg·K) | |
Thermal conductivity | 20.0 °C | 13.4 - 15 W/(m·K) | |
100.0 °C | 14.9 W/(m·K) | ||
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical resistivity | 20.0 °C | 7.85E-7 - 8E-7 Ω·m |
100.0 °C | 8.44E-7 Ω·m | |
Chemical properties
| Property | Value |
|---|---|
Carbon | 0.03 % |
Chromium | 21 - 23 % |
Manganese | 2 % |
Molybdenum | 2.5 - 3.5 % |
Nickel | 4.5 - 6.5 % |
Nitrogen | 0.1 - 0.22 % |
Phosphorus | 0.04 % |
Silicon | 1 % |
Sulfur | 0.015 % |
Metal
- EN 10222-5 X2CrNiMo18-14-3 Solution‑Annealed Grade for Corrosion‑Resistant Applications
- EN 10222-5 X6CrNiMoTi17-12-2 (Solution Annealed) – High Corrosion‑Resistant Stainless Steel
- EN 10222-5 X6CrNiTi18-10 – Solution Annealed & AT: Premium Corrosion‑Resistant Steel for Chemical & Food Applications
- X2CrNiMo18-14-3 Solution Annealed – EN 10250-4 Grade, Superior Corrosion Resistance
- EN 10250-4 Grade X5CrNi18-10 Solution-Annealed Steel (+AT) – Premium Corrosion-Resistant Austenitic Alloy
- EN 10250-4 X6CrNiMoTi17-12-2 (Solution Annealed) – High-Performance Stainless Steel
- EN 10250‑4 X6CrNiTi18‑10: Ti‑Stabilized, Solution‑Annealed Stainless Steel for High‑Performance Welding
- EN 10217-7 X5CrNi18-10 Austenitic Steel – Solution Annealed (+AT) for Corrosion Resistance
- EN 10217-7 Grade X6CrNiMoTi17-12-2 Solution-Annealed Steel – High‑Temperature Corrosion Resistance & Structural Strength
- EN 10217-7 X6CrNiTi18-10 Solution-Annealed Austenitic Steel – Corrosion-Resistant & High-Temperature Performance