EN 10088‑1 X3CrNiCu18‑9‑4 Austenitic Stainless Steel – Solution Annealed & AT Certified

Material X3CrNiCu18-9-4 is comparable to X 3 CrNiCu 18 9 acc. to DIN 1654-5: 1989-10. The austenitic stainless steel with low C-content is used for special applications, such as for cold upsetting wire, also at low temperatures. The steel is resistant to intercrystalline corrosion also in sensitized condition.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.9 - 7.92 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

206 GPa

20.0 °C

196 - 200 GPa

100.0 °C

190 - 194 GPa

200.0 °C

182 - 186 GPa

300.0 °C

174 - 179 GPa

400.0 °C

166 - 172 GPa

500.0 °C

158 - 165 GPa

600.0 °C

150 GPa

700.0 °C

142 GPa

800.0 °C

134 GPa

Elongation

20.0 °C

20 - 45 %

Hardness, Brinell

20.0 °C

215 [-]

Poisson's ratio

20.0 °C

0.28 [-]

Shear modulus

23.0 °C

77 GPa

Typical for Austenitic Stainless Steel

Tensile strength

20.0 °C

450 - 1100 MPa

Yield strength Rp0.2

20.0 °C

175 - 400 MPa

Yield strength Rp1.0

20.0 °C

210 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.49E-5 1/K

20.0 °C

1.61E-5 1/K

100.0 °C

1.67E-5 1/K

200.0 °C

1.72E-5 1/K

300.0 °C

1.77E-5 1/K

400.0 °C

1.81E-5 1/K

500.0 °C

1.84E-5 1/K

600.0 °C

1.88E-5 1/K

700.0 °C

1.91E-5 1/K

800.0 °C

1.94E-5 1/K

Melting point

1230 - 1480 °C

Typical for Austenitic Stainless Steel

Specific heat capacity

-100.0 °C

440 J/(kg·K)

20.0 °C

472 J/(kg·K)

100.0 °C

487 J/(kg·K)

200.0 °C

503 J/(kg·K)

300.0 °C

512 J/(kg·K)

400.0 °C

520 J/(kg·K)

500.0 °C

530 J/(kg·K)

600.0 °C

541 J/(kg·K)

700.0 °C

551 J/(kg·K)

800.0 °C

559 J/(kg·K)

Thermal conductivity

-100.0 °C

11.7 W/(m·K)

20.0 °C

14.5 W/(m·K)

100.0 °C

16 W/(m·K)

200.0 °C

17.6 W/(m·K)

300.0 °C

19.1 W/(m·K)

400.0 °C

20.4 W/(m·K)

500.0 °C

21.9 W/(m·K)

600.0 °C

23.3 W/(m·K)

700.0 °C

24.7 W/(m·K)

800.0 °C

26.1 W/(m·K)

Thermal diffusivity

-100.0 °C

3.7 mm²/s

20.0 °C

3.9 mm²/s

100.0 °C

4.3 mm²/s

200.0 °C

4.3 mm²/s

300.0 °C

4.6 mm²/s

400.0 °C

4.7 mm²/s

500.0 °C

4.9 mm²/s

600.0 °C

5 mm²/s

700.0 °C

5.3 mm²/s

800.0 °C

5.7 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

-100.0 °C

5.86E-7 Ω·m

20.0 °C

6.92E-7 Ω·m

100.0 °C

7.58E-7 Ω·m

200.0 °C

8.36E-7 Ω·m

300.0 °C

9.07E-7 Ω·m

400.0 °C

9.73E-7 Ω·m

500.0 °C

1.02E-6 Ω·m

600.0 °C

1.06E-6 Ω·m

700.0 °C

1.1E-6 Ω·m

800.0 °C

1.13E-6 Ω·m

Chemical properties

PropertyValue

Carbon

0.04 %

Chromium

17 - 19 %

Copper

3 - 4 %

Manganese

2 %

Nickel

8.5 - 10.5 %

Nitrogen

0.11 %

Phosphorus

0.05 %

Silicon

1 %

Sulfur

0.015 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. Grade X3CrNiCuMo17-11-3-2 Austenitic Steel – EN 10088-1, Solution Annealed + AT
    2. EN 10269 Grade X3CrNiCu18-9-4 – Solution Annealed Stainless Steel for High‑Temperature Applications
    3. EN 10088-1 X3CrNiCu19-9-2 Austenitic Steel – Solution Annealed for Superior Corrosion Resistance
    4. EN 10088-1 X6CrNiCuS18-9-2 – Solution Annealed Austenitic Steel for Rods & Wire Rods
    5. EN 10088-1 Grade X7CrNiAl17-7: Solution-Annealed Stainless Steel with Enhanced Performance
    6. EN 10088-1 Grade X3CrNiMoN27-5-2: Solution‑Annealed (AT) – High‑Performance Ferritic Austenitic Steel
    7. X2CrNiMoN25-7-4 Solution-Annealed Stainless Steel – EN 10088‑1 Grade X2
    8. EN 10088-1 X2CrNiMoCuWN25-7-4: Solution‑Annealed Alloy for Superior Corrosion Resistance
    9. EN 10088-1 Grade X2CrNiMoN18-12-4: High-Performance Solution-Annealed Stainless Steel (+AT)
    10. EN 10088-1 X2CrNiMoCuN25-6-3 Solution Annealed Steel: Properties & Applications