EN 10269 Grade X3CrNiCu18-9-4 – Solution Annealed Stainless Steel for High‑Temperature Applications

Trademark X3CrNiCu18-9-4 is comparable to X 3 CrNiCu 18 9 acc. to DIN 1654-5 : 1989-10. The austenitic stainless steel with a low C-content is used for special applications, such as wire for cold heading also at low temperatures. The steel is resistant to intercrystalline corrosion also in sensitized condition. Application for mounting elements at increased temperatures.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.9 - 7.92 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

206 GPa

20.0 °C

196 - 200 GPa

100.0 °C

190 - 194 GPa

200.0 °C

182 - 186 GPa

300.0 °C

174 - 179 GPa

400.0 °C

166 - 172 GPa

500.0 °C

158 - 165 GPa

600.0 °C

150 GPa

700.0 °C

142 GPa

800.0 °C

134 GPa

Elongation

20.0 °C

45 %

Poisson's ratio

20.0 °C

0.28 [-]

Shear modulus

23.0 °C

77 GPa

Typical for Austenitic Stainless Steel

Tensile strength

20.0 °C

450 - 650 MPa

Yield strength Rp0.2

20.0 °C

175 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.49E-5 1/K

20.0 °C

1.61E-5 1/K

100.0 °C

1.67E-5 1/K

200.0 °C

1.72E-5 1/K

300.0 °C

1.77E-5 1/K

400.0 °C

1.81E-5 1/K

500.0 °C

1.84E-5 1/K

600.0 °C

1.88E-5 1/K

700.0 °C

1.91E-5 1/K

800.0 °C

1.94E-5 1/K

Melting point

1230 - 1480 °C

Typical for Austenitic Stainless Steel

Specific heat capacity

-100.0 °C

440 J/(kg·K)

20.0 °C

472 J/(kg·K)

100.0 °C

487 J/(kg·K)

200.0 °C

503 J/(kg·K)

300.0 °C

512 J/(kg·K)

400.0 °C

520 J/(kg·K)

500.0 °C

530 J/(kg·K)

600.0 °C

541 J/(kg·K)

700.0 °C

551 J/(kg·K)

800.0 °C

559 J/(kg·K)

Thermal conductivity

-100.0 °C

11.7 W/(m·K)

20.0 °C

14.5 W/(m·K)

100.0 °C

16 W/(m·K)

200.0 °C

17.6 W/(m·K)

300.0 °C

19.1 W/(m·K)

400.0 °C

20.4 W/(m·K)

500.0 °C

21.9 W/(m·K)

600.0 °C

23.3 W/(m·K)

700.0 °C

24.7 W/(m·K)

800.0 °C

26.1 W/(m·K)

Thermal diffusivity

-100.0 °C

3.7 mm²/s

20.0 °C

3.9 mm²/s

100.0 °C

4.3 mm²/s

200.0 °C

4.3 mm²/s

300.0 °C

4.6 mm²/s

400.0 °C

4.7 mm²/s

500.0 °C

4.9 mm²/s

600.0 °C

5 mm²/s

700.0 °C

5.3 mm²/s

800.0 °C

5.7 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

-100.0 °C

5.86E-7 Ω·m

20.0 °C

6.92E-7 Ω·m

100.0 °C

7.58E-7 Ω·m

200.0 °C

8.36E-7 Ω·m

300.0 °C

9.07E-7 Ω·m

400.0 °C

9.73E-7 Ω·m

500.0 °C

1.02E-6 Ω·m

600.0 °C

1.06E-6 Ω·m

700.0 °C

1.1E-6 Ω·m

800.0 °C

1.13E-6 Ω·m

Chemical properties

PropertyValue

Carbon

0.04 %

Chromium

17 - 19 %

Copper

3 - 4 %

Manganese

2 %

Nickel

8.5 - 10.5 %

Nitrogen

0.1 - 0.11 %

Phosphorus

0.05 %

Silicon

1 %

Sulfur

0.015 - 0.03 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10269 X2CrNi18-9 Stainless Steel – Solution Annealed with Post-Annealing Treatment
    2. EN 10269 Grade X4CrNi18-12 – Solution Annealed with Enhanced Treatment
    3. EN 10269 X6CrNiTiB18-10 – Solution‑Annealed High‑Temperature Steel (AT)
    4. EN 10269 X2CrNiMoN17-13-3 – High‑Strength, Corrosion‑Resistant Austenitic Steel, Solution Annealed (+AT)
    5. EN 10269 X3CrNiMoBN17-13-3 Solution Annealed Steel for Power Plant Superheaters and High‑Temperature Components
    6. EN 10269 X5CrNiMo17-12-2 Solution Annealed (+AT) – Premium Austenitic Steel for Chemical & Pharma Applications
    7. EN 10269: X6CrNi18-10 Austenitic Steel – Solution Annealed & Post‑Annealing Treatment
    8. EN 10269 X6CrNiMoB17-12-2 Solution-Annealed Steel (+AT): High-Temperature Austenitic Steel for Power Plants & Chemical Applications
    9. EN 10269 X2CrNiMo17-12-2 Solution-Annealed Steel – Superior Corrosion Resistance & Formability
    10. EN 10088‑1 X3CrNiCu18‑9‑4 Austenitic Stainless Steel – Solution Annealed & AT Certified