EN 10216-4 26CrMo4-2 High-Grade Quenched & Tempered Steel Tubes for Cryogenic & Heavy-Duty Applications

Tubes made from cryogenic alloyed high-grade steel 26CrMo4-2 are predominantly used in apparatus, tank, line construction as well as in general machine and equipment engineering. Weldability is available.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.83 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

212 GPa

100.0 °C

207 GPa

200.0 °C

199 GPa

300.0 °C

192 GPa

400.0 °C

184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Elongation

20.0 °C

18 %

Elongation, transverse

20.0 °C

16 %

Poisson's ratio

23.0 °C

0.29 [-]

Typical for Chromium Molybdenum Steel

Tensile strength

20.0 °C

560 - 740 MPa

Tensile strength, transverse

20.0 °C

560 - 740 MPa

Yield strength Rp0.2

20.0 °C

440 MPa

100.0 °C

320 MPa

200.0 °C

300 MPa

250.0 °C

290 MPa

300.0 °C

280 MPa

Yield strength Rp0.2, transverse

20.0 °C

440 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.05E-5 1/K

20.0 °C

1.15E-5 1/K

100.0 °C

1.21E-5 1/K

200.0 °C

1.27E-5 1/K

300.0 °C

1.32E-5 1/K

400.0 °C

1.36E-5 1/K

500.0 °C

1.4E-5 1/K

600.0 °C

1.44E-5 1/K

Melting point

1382 - 1529 °C

Typical for Chromium Molybdenum Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

41 W/(m·K)

100.0 °C

42.7 W/(m·K)

200.0 °C

42.8 W/(m·K)

300.0 °C

41.6 W/(m·K)

400.0 °C

39.9 W/(m·K)

500.0 °C

37.8 W/(m·K)

600.0 °C

35.6 W/(m·K)

Thermal diffusivity

20.0 °C

11.4 mm²/s

100.0 °C

11 mm²/s

200.0 °C

10.3 mm²/s

300.0 °C

9.5 mm²/s

400.0 °C

8.5 mm²/s

500.0 °C

7.3 mm²/s

600.0 °C

6 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

2.54E-7 Ω·m

100.0 °C

3E-7 Ω·m

200.0 °C

3.69E-7 Ω·m

300.0 °C

4.51E-7 Ω·m

400.0 °C

5.45E-7 Ω·m

500.0 °C

6.54E-7 Ω·m

600.0 °C

7.78E-7 Ω·m

Chemical properties

PropertyValue

Carbon

0.22 - 0.29 %

Chromium

0.9 - 1.2 %

Copper

0.3 %

Manganese

0.5 - 0.8 %

Molybdenum

0.15 - 0.3 %

Phosphorus

0.03 %

Silicon

0.35 %

Sulfur

0.01 - 0.02 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10137-2 Grade S890QL – High-Strength Quenched & Tempered Steel for Heavy-Duty Applications
    2. EN 10137-3 Grade S500A: Quenched & Tempered Fine‑Grained Steel for Structural Applications
    3. EN 10083-1 Grade 51CrV4: Quenched & Tempered Steel (QT)
    4. EN 10213 Grade G17CrMo9-10 – Quenched & Tempered (QT) Steel for High-Temperature Applications
    5. EN 10085 Grade 15 CrMoV 5.9: Quenched & Tempered Steel for Durable Machine Components
    6. EN 10085 Grade 31CrMo12 – High-Performance Quenched & Tempered Steel for Heavy‑Duty Applications
    7. DIN 17173 Grade 26CrMo4-2: Quenched & Tempered Steel Properties
    8. EN 10216-2 Grade 11CrMo9-10 Quenched & Tempered Seamless Tubes – High‑Temperature, High‑Pressure Applications
    9. EN 10132-3: 42CrMo4 Quenched & Tempered Alloy Steel – Premium Cold-Rolled Strips
    10. EN 10216-4 Grade P255QL Quenched & Tempered Steel Tubes – High Strength & Excellent Weldability