EN 12166 Grade CuZn39Pb3 (H04) – Leaded Brass Alloy Specifications

Material CuZn39Pb3, mat. No. CW614N, is an unhardenable wrought alloy. to the comparable make CuZn39Pb3, mat. No. 2.0401 acc. to DIN 17660 : 1983-12 applies: High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for unleaded brass of the same Zn-content. Machinability is improved by Pb-addition. Corrosion resistance to water, several saline solutions and organic liquids is also lower than for unleaded alloys of the same zinc-content. Processing properties: warm forming: very good cold forming: unfavorable machinability: very good hard soldering: moderately soft soldering: very good TIG-welding: unfavorable burnishing: very good Application: Main alloy of the brass materials for machining on automats. Use for all types of form turning parts, in precision engineering as well as in watch and electrical industry.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

8.4 - 8.47 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

20.0 °C

96 - 97 GPa

Elongation

20.0 °C

8 %

Elongation A10

20.0 °C

6 %

Elongation A100

20.0 °C

4 %

Hardness, Vickers

20.0 °C

145 - 185 [-]

Shear modulus

23.0 °C

40 GPa

Typical for Wrought Copper Brass

Tensile strength

20.0 °C

490 - 520 MPa

Yield strength Rp0.2

20.0 °C

390 - 400 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

100.0 °C

1.93E-5 1/K

200.0 °C

2.1E-5 1/K

300.0 °C

2.14E-5 1/K

800.0 °C

2.47E-5 1/K

Melting point

875 - 1075 °C

Typical for Wrought Copper Brass

Specific heat capacity

20.0 °C

377 J/(kg·K)

Thermal conductivity

-200.0 °C

50 W/(m·K)

20.0 °C

113 - 123 W/(m·K)

Electrical

PropertyTemperatureValue

Electrical conductivity

20.0 °C

1.46E+7 - 1.50E+7 S/m

200.0 °C

1.20E+7 S/m

Electrical resistivity

20.0 °C

6.6E-8 Ω·m

200.0 °C

8.3E-8 Ω·m

Specific Electrical conductivity

25.2 % IACS

Chemical properties

PropertyValue

Aluminium

0.05 %

Copper

57 - 59 %

Iron

0.3 %

Lead

2.5 - 3.5 %

Nickel

0.3 %

Tin

0.3 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 12166 CuNi10Zn42Pb2 H04 – High-Performance Wrought Copper Alloy
    2. EN 12166 Grade CuNi18Zn19Pb1 H04: High-Strength, Corrosion-Resistant Copper‑Nickel‑Zinc Alloy
    3. EN 12166 CuZn39Pb3 H145 Copper Alloy Wire – Properties & Specifications
    4. EN 12166 CuZn39Pb3 H095 – Copper Alloy Grade Specification & Key Properties
    5. EN 12166 CuSn5 H04 – Premium Copper‑Tin Alloy for Precision Tubes and Connectors
    6. EN 12166 Grade CuZn39Pb3 (H135) – Leaded Brass Alloy Specifications
    7. EN 12166 Copper Alloy Grade CuZn39Pb3 H115 – Key Properties & Applications
    8. EN 12166 Grade CuZn37 H04 – Premium Copper Alloy for Cold Forming & Corrosion Resistance
    9. EN 12166 CuZn36 H04 – Unhardenable Wrought Alloy for Precision Deep‑Drawing and Pressure Components
    10. EN 12166 CuSn6 H04 – Premium Copper‑Tin Alloy for High Corrosion Resistance and Superior Mechanical Performance