EN 12452 Grade CuZn20Al2As – Seawater‑Resistant, Dezincification‑Immune Copper Alloy

CuZn20Al2As (CW702R former identification: CuZn20Al2) is an unhardenable copper alloy. High hardness and strength values are achievable by cold forming only. Strength properties, corrosion resistance and oxidation resistance are increasable by Al-addition. CuZn20Al2As is seawater and dezincification resistant, and insensitive to stress corrosion in stress-relieved condition. Processing properties: warm forming: moderately cold forming: moderately machinability: moderately hard soldering: moderately soft soldering: unfavorable TIG-welding: good burnishing: very good The material is predominantly suitable for smooth and ribbed tubes and for heat-exchanger in condenser construction as well as for seawater pipelines. It is due to its favorable corrosion and erosion behaviour a reliable material in cooling water with salinities of more than 0,2%, e.g. in brack and seawater at water speed up to 2,5 m/s. In the case of a natural protective oxide film damage occurs a self-healing process.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

8.33 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

20.0 °C

110 - 112 GPa

50.0 °C

110 - 130 GPa

100.0 °C

108 - 128 GPa

150.0 °C

107 - 126 GPa

200.0 °C

106 - 123 GPa

250.0 °C

105 - 120 GPa

300.0 °C

118 GPa

350.0 °C

115 GPa

400.0 °C

112 GPa

450.0 °C

109 GPa

500.0 °C

105 GPa

Elongation

20.0 °C

40 - 55 %

100.0 °C

50 - 56 %

150.0 °C

56 %

200.0 °C

43 - 50 %

250.0 °C

22 %

300.0 °C

42 %

400.0 °C

23 %

500.0 °C

35 %

Hardness, Brinell

20.0 °C

65 - 95 [-]

Hardness, Vickers

20.0 °C

60 - 110 [-]

Reduction of area

100.0 °C

69 %

150.0 °C

63 %

200.0 °C

37 %

250.0 °C

23 %

Shear modulus

20.0 °C

42 GPa

Tensile strength

20.0 °C

340 - 420 MPa

100.0 °C

395 - 410 MPa

150.0 °C

385 MPa

200.0 °C

365 - 375 MPa

250.0 °C

310 MPa

300.0 °C

355 MPa

400.0 °C

280 MPa

500.0 °C

130 MPa

Yield strength Rp0.2

20.0 °C

89 - 150 MPa

100.0 °C

180 MPa

150.0 °C

180 MPa

200.0 °C

65 - 175 MPa

250.0 °C

170 MPa

300.0 °C

60 MPa

400.0 °C

55 MPa

Yield strength Rp1.0

100.0 °C

195 MPa

150.0 °C

195 MPa

200.0 °C

195 MPa

250.0 °C

190 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

200.0 °C

1.85E-5 1/K

Melting point

875 - 1075 °C

Typical for Wrought Copper Brass

Specific heat capacity

20.0 °C

377 J/(kg·K)

Thermal conductivity

20.0 °C

100 W/(m·K)

Electrical

PropertyTemperatureValue

Electrical conductivity

20.0 °C

1.34E+7 S/m

Electrical resistivity

20.0 °C

7.5E-8 Ω·m

Chemical properties

PropertyValue

Aluminium

1.8 - 2.3 %

Arsenic

0.02 - 0.06 %

Copper

76 - 79 %

Iron

0.07 %

Lead

0.05 - 0.5 %

Magnesium

5E-3 %

Manganese

0.1 %

Nickel

0.1 %

Phosphorus

0.01 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 12166 Grade CuNi10Zn27 O60: High-Performance Copper-Nickel-Zinc Wire
    2. EN 12163 Grade Cu‑FRTP O60 – Premium 99.9% Oxygenated Copper for Industrial Use
    3. EN 12451 CuZn30As O60 – Copper Brass Seamless Tube Grade
    4. EN 12166 Grade CuSn5 O60 – High‑Conductivity Copper Tin Alloy for Precision Tubes and Connectors
    5. EN 12167 Grade O60 CuZn39Pb3 Leaded Brass Alloy – High Hardness & Machinability
    6. EN 12166 Grade CuZn39Pb3 – Leaded Brass with Enhanced Machinability
    7. EN 12168: CuZn40Pb2 O60 – Lead-Enhanced Brass for Superior Machinability
    8. EN 1652 CuZn20Al2As R330: Advanced Corrosion-Resistant Copper Alloy
    9. EN 12166 Grade CuNi12Zn24 O60 – High-Strength, Corrosion-Resistant Copper-Nickel-Zinc Alloy
    10. EN 1652 Grade CuZn20Al2As (R390) – Superior Unhardenable Copper Alloy for Marine Applications