DIN 1651 Grade 9SMn36 Untreated – High-Performance Balanced Machining Steel

The balanced machining steel 9 SMn 36 is used for higher demands on the cutting capacity and surface condition. The steel shows a elevated crack sensitivity. Application: limited in the automotive engineering, toolbuilding, apparatus engineering

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.83 - 7.85 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

210 - 212 GPa

100.0 °C

207 GPa

200.0 °C

193 - 199 GPa

300.0 °C

185 - 192 GPa

400.0 °C

175 - 184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Hardness, Brinell

20.0 °C

156 - 174 [-]

Poisson's ratio

23.0 °C

0.29 [-]

Typical for Low Carbon Steel

Shear modulus

20.0 °C

81 GPa

Tensile strength

20.0 °C

360 - 590 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.08E-5 1/K

20.0 °C

1.19E-5 1/K

100.0 °C

1.1E-5 - 1.25E-5 1/K

200.0 °C

1.18E-5 - 1.3E-5 1/K

300.0 °C

1.36E-5 1/K

400.0 °C

1.32E-5 - 1.41E-5 1/K

500.0 °C

1.45E-5 1/K

600.0 °C

1.49E-5 1/K

Max service temperature

500 °C

Typical for Carbon Steel

Melting point

1480 - 1526 °C

Typical for Low Carbon Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

460 - 461 J/(kg·K)

100.0 °C

479 - 480 J/(kg·K)

200.0 °C

499 - 520 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 - 610 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

-100.0 °C

37.6 W/(m·K)

20.0 °C

42.2 - 54.4 W/(m·K)

100.0 °C

43.2 W/(m·K)

200.0 °C

42.9 W/(m·K)

300.0 °C

41.2 W/(m·K)

400.0 °C

39.1 W/(m·K)

500.0 °C

36.6 W/(m·K)

600.0 °C

34.1 W/(m·K)

Thermal diffusivity

-100.0 °C

12.9 mm²/s

20.0 °C

11.7 mm²/s

100.0 °C

11.2 mm²/s

200.0 °C

10.3 mm²/s

300.0 °C

9.4 mm²/s

400.0 °C

8.3 mm²/s

500.0 °C

7.1 mm²/s

600.0 °C

5.7 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

-100.0 °C

1.82E-7 Ω·m

20.0 °C

1.1E-7 - 2.47E-7 Ω·m

100.0 °C

2.96E-7 Ω·m

200.0 °C

3.68E-7 Ω·m

300.0 °C

4.55E-7 Ω·m

400.0 °C

5.56E-7 Ω·m

500.0 °C

6.75E-7 Ω·m

600.0 °C

8.13E-7 Ω·m

Magnetic

PropertyValueComment

Curie temperature

770 °C

Typical for Low Carbon Steel

Chemical properties

PropertyValue

Carbon

0.15 %

Manganese

1.1 - 1.5 %

Phosphorus

0.1 %

Silicon

0.05 %

Sulfur

0.34 - 0.4 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. DIN 1651 Grade 9SMn36: Cold-Drawn, Stress-Relieved Steel for Precision Cutting Applications
    2. DIN 1651 Grade 9SMnPb28: Untreated, High-Performance Balanced Machining Steel
    3. DIN 1651 Grade 9SMnPb36 – Untreated High-Performance Machining Steel
    4. DIN 1651 Grade 10SPb20: Untreated, High-Performance Machining Steel
    5. DIN 1651 Grade 10S20 Untreated Steel – Superior Machinability & Toughness
    6. DIN 1651 Grade 15S10 Untreated – Fully Killed Steel for High‑Toughness Thin‑Walled Parts
    7. DIN 1651 9SMn28 Steel – Untreated, Premium Machining Grade
    8. DIN 5512‑1 Grade S235JRG2Cu – Untreated Low‑Carbon Steel Specifications
    9. S235JRG2CuC Untreated Steel – DIN 5512‑1 Grade for Rail Vehicle Engineering
    10. DIN 1651 9SMn36 Cold Drawn Steel – High Performance, Precision Machining