DIN 1651 Grade 15S10 Untreated – Fully Killed Steel for High‑Toughness Thin‑Walled Parts

The fully killed machining steel 15 S 10 is applicated in the case hardened condition for thin walled parts with higher toughness demands. Application: automotive engineering, toolbuilding, apparatus engineering

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.85 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

210 - 212 GPa

100.0 °C

207 GPa

200.0 °C

193 - 199 GPa

300.0 °C

185 - 192 GPa

400.0 °C

175 - 184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Hardness, Brinell

20.0 °C

162 - 176 [-]

Poisson's ratio

20.0 °C

0.28 [-]

Shear modulus

20.0 °C

81 GPa

Tensile strength

20.0 °C

360 - 600 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.08E-5 1/K

20.0 °C

1.19E-5 1/K

100.0 °C

1.1E-5 - 1.25E-5 1/K

200.0 °C

1.18E-5 - 1.3E-5 1/K

300.0 °C

1.36E-5 1/K

400.0 °C

1.32E-5 - 1.41E-5 1/K

500.0 °C

1.45E-5 1/K

600.0 °C

1.49E-5 1/K

Max service temperature

500 °C

Typical for Carbon Steel

Melting point

1480 - 1526 °C

Typical for Low Carbon Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

460 - 461 J/(kg·K)

100.0 °C

479 - 480 J/(kg·K)

200.0 °C

499 - 520 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 - 600 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

52.4 - 57.5 W/(m·K)

100.0 °C

55.7 W/(m·K)

200.0 °C

51.9 W/(m·K)

300.0 °C

47.6 W/(m·K)

400.0 °C

43.4 W/(m·K)

500.0 °C

39.6 W/(m·K)

600.0 °C

36 W/(m·K)

Thermal diffusivity

20.0 °C

15.9 mm²/s

100.0 °C

14.3 mm²/s

200.0 °C

12.5 mm²/s

300.0 °C

10.8 mm²/s

400.0 °C

9.2 mm²/s

500.0 °C

7.6 mm²/s

600.0 °C

6.1 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

1.1E-7 Ω·m

100.0 °C

2.3E-7 Ω·m

200.0 °C

3.04E-7 Ω·m

300.0 °C

3.94E-7 Ω·m

400.0 °C

5.01E-7 Ω·m

500.0 °C

6.25E-7 Ω·m

600.0 °C

7.7E-7 Ω·m

Magnetic

PropertyValueComment

Curie temperature

770 °C

Typical for Low Carbon Steel

Chemical properties

PropertyValue

Carbon

0.12 - 0.18 %

Manganese

0.7 - 1.1 %

Phosphorus

0.06 %

Silicon

0.1 - 0.3 %

Sulfur

0.08 - 0.13 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. DIN 1651 Grade 9SMnPb28: Untreated, High-Performance Balanced Machining Steel
    2. DIN 1651 Grade 9SMnPb36 – Untreated High-Performance Machining Steel
    3. DIN 1651 Grade 10SPb20: Untreated, High-Performance Machining Steel
    4. DIN 1651 Grade 10S20 Untreated Steel – Superior Machinability & Toughness
    5. DIN 1651 Grade 15S10 Untreated – Fully Killed Steel for High‑Toughness Thin‑Walled Parts
    6. DIN 1651 9SMn28 Steel – Untreated, Premium Machining Grade
    7. DIN 1651 Grade 9SMn36 Untreated – High-Performance Balanced Machining Steel
    8. DIN 5512‑1 Grade S235JRG2Cu – Untreated Low‑Carbon Steel Specifications
    9. S235JRG2CuC Untreated Steel – DIN 5512‑1 Grade for Rail Vehicle Engineering
    10. DIN 1651 Grade 15S10 Cold‑Drawn Steel – High‑Performance, Case‑Hardened Material for Automotive & Tooling Applications