EN 10263-2 Grade QSt 36-3 Untreated and Turned – High-Strength Steel for Precision Parts

The steel QSt 36-3 can undergo cold extrusion pressing and is suitable for the manufacture of mass-produced parts in general engineering, motor and automobile construction with high demands on the strength, surface condition and exactness of dimensions. Because of its smooth surface and high internal stress in the cold-worked edge zone, the vibration fatigue strength is increased. The parts possess favourable run characteristics and have good resistance to wear (phosphate layer). The fibre texture which is adapted to the construction component avoids damaging notch effects. The steel possesses optimum cold formability in the soft-annealed condition -- melting in fine-grained quality to achieve higher resistance to aging.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.85 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

212 GPa

100.0 °C

207 GPa

200.0 °C

199 GPa

300.0 °C

192 GPa

400.0 °C

184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Poisson's ratio

20.0 °C

0.28 [-]

Reduction of area

20.0 °C

60 %

Shear modulus

23.0 °C

82 GPa

Typical for Low Carbon Steel

Tensile strength

20.0 °C

430 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.08E-5 1/K

20.0 °C

1.19E-5 1/K

100.0 °C

1.25E-5 1/K

200.0 °C

1.3E-5 1/K

300.0 °C

1.36E-5 1/K

400.0 °C

1.41E-5 1/K

500.0 °C

1.45E-5 1/K

600.0 °C

1.49E-5 1/K

Max service temperature

500 °C

Typical for Carbon Steel

Melting point

1480 - 1526 °C

Typical for Low Carbon Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

56.9 W/(m·K)

100.0 °C

56.4 W/(m·K)

200.0 °C

53.5 W/(m·K)

300.0 °C

49.4 W/(m·K)

400.0 °C

45.2 W/(m·K)

500.0 °C

41.3 W/(m·K)

600.0 °C

37.6 W/(m·K)

Thermal diffusivity

20.0 °C

15.7 mm²/s

100.0 °C

14.5 mm²/s

200.0 °C

12.9 mm²/s

300.0 °C

11.2 mm²/s

400.0 °C

9.6 mm²/s

500.0 °C

7.9 mm²/s

600.0 °C

6.3 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

1.83E-7 Ω·m

100.0 °C

2.27E-7 Ω·m

200.0 °C

2.95E-7 Ω·m

300.0 °C

3.8E-7 Ω·m

400.0 °C

4.81E-7 Ω·m

500.0 °C

5.99E-7 Ω·m

600.0 °C

7.38E-7 Ω·m

Magnetic

PropertyValueComment

Curie temperature

770 °C

Typical for Low Carbon Steel

Chemical properties

PropertyValue

Carbon

0.06 - 0.13 %

Manganese

0.25 - 0.45 %

Phosphorus

0.04 %

Silicon

0.1 %

Sulfur

0.04 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10277-2 Grade E295GC – Rolled, Turned, Heat-Treated Steel for High-Strength Applications
    2. EN 10277-2 E335GC Steel – Rolled, Turned, and Surface Hardened for High-Performance Applications
    3. EN 10277-3 Grade 35SPb20 – Rolled & Turned Steel with Hardening + SH
    4. EN 10277‑3 Grade 46SPb20 Rolled & Turned Steel (+SH) – High Strength, Low Ductility
    5. DIN 1654-5 X3CrNiCu18-9: High-Performance Austenitic Stainless Steel, Quenched & Cold-Worked
    6. EN 10277-5 Grade C60R Steel – Rolled & Turned with SH for High‑Load Applications
    7. EN 10277-3 Grade 35S20: Rolled & Turned Steel with Surface Hardening
    8. EN 10263-2 Grade QSt 32-3 – Untreated & Turned Steel for High-Performance Applications
    9. EN 10263-2 Grade QSt 34-3 – Untreated & Turned Steel for High-Strength, Precision Engineering
    10. EN 10263-2 Grade QSt 38-3 – Untreated & Turned Steel for High-Performance, Wear-Resistant Parts