EN 10277-2 Grade E295GC – Rolled, Turned, Heat-Treated Steel for High-Strength Applications
E295GC is applicated as cold drawing grade. The steel is used for wear and strength loaded parts (bolts, shafts, spindles, wedges). As a bright steel product it is used in the form of bars, bright, straight, in various conditions (see DIN EN 10277 : 1999-10).
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 7.85 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 20.0 °C | 210 GPa | |
100.0 °C | 205 GPa | ||
200.0 °C | 195 GPa | ||
300.0 °C | 185 GPa | ||
400.0 °C | 175 GPa | ||
Hardness, Brinell | 20.0 °C | 140 - 181 [-] | |
Poisson's ratio | 23.0 °C | 0.29 [-] | Typical for Medium Carbon Steel |
Shear modulus | 20.0 °C | 81 GPa | |
Tensile strength | 20.0 °C | 470 - 610 MPa | |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 100.0 °C | 1.11E-5 1/K | |
200.0 °C | 1.21E-5 1/K | ||
300.0 °C | 1.29E-5 1/K | ||
400.0 °C | 1.35E-5 1/K | ||
Max service temperature | 500 °C | Typical for Carbon Steel | |
Melting point | 1380 - 1514 °C | Typical for Medium Carbon Steel | |
Specific heat capacity | 20.0 °C | 450 J/(kg·K) | |
Thermal conductivity | 20.0 °C | 54 W/(m·K) | |
100.0 °C | 50.7 W/(m·K) | ||
200.0 °C | 46.9 W/(m·K) | ||
300.0 °C | 41.5 W/(m·K) | ||
400.0 °C | 39.4 W/(m·K) | ||
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical resistivity | 20.0 °C | 2E-7 Ω·m |
Chemical properties
| Property | Value |
|---|---|
Nitrogen | 9E-3 % |
Phosphorus | 0.05 % |
Sulfur | 0.045 % |
Metal
- EN 10277-2 E335GC Steel – Rolled, Turned, and Surface Hardened for High-Performance Applications
- EN 10277-2 Grade C35 Steel: Rolled & Turned (+SH) for High-Strength Applications
- EN 10277-2 Grade C40 Steel – Rolled & Turned (+SH) for Heavy‑Duty Applications
- EN 10277-2 Grade C45 Steel – Rolled & Turned (+SH) for High-Performance Applications
- EN 10277-2 Grade C50 Steel – Rolled & Turned Bright Steel for High‑Strength Applications
- Grade C60 Steel – EN 10277-2 Rolled and Turned (Shrouded) for High-Strength Applications
- EN 10277-2 Grade C16 Rolled & Turned Steel Bars (+SH) – High-Quality Low-Carbon Performance
- EN 10277-2 Grade S355J2G3C – Rolled & Turned Steel for High‑Tensile Applications
- EN 10277-2 Grade C10 Steel: Rolled & Turned (+SH) – Ideal for Low-Strength, Wear-Resistant Vehicle & Machine Parts
- EN 10277-2 Grade C15 Rolled & Turned Steel (SH) – High Core Strength & Wear Resistance