EN 10250-2 Grade C55E: High-Performance Quenched & Tempered Steel for Heavy-Duty Applications

Steel C55E is usable for larger parts in vehicle, engine and machine engineering undergoing a surface hardening (e.g. gear wheels, screws, shafts).

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.8 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

212 GPa

100.0 °C

207 GPa

200.0 °C

199 GPa

300.0 °C

192 GPa

400.0 °C

184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Elongation

20.0 °C

15 - 17 %

Elongation, transverse

20.0 °C

10 - 11 %

Poisson's ratio

23.0 °C

0.29 [-]

Typical for Medium Carbon Steel

Shear modulus

23.0 °C

75 - 80 GPa

Typical for Carbon Steel

Tensile strength

20.0 °C

610 - 700 MPa

Tensile strength, transverse

20.0 °C

610 - 630 MPa

Yield strength

20.0 °C

330 - 420 MPa

Yield strength, transverse

20.0 °C

330 - 360 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.08E-5 1/K

20.0 °C

1.19E-5 1/K

100.0 °C

1.25E-5 1/K

200.0 °C

1.3E-5 1/K

300.0 °C

1.36E-5 1/K

400.0 °C

1.41E-5 1/K

500.0 °C

1.45E-5 1/K

600.0 °C

1.49E-5 1/K

Max service temperature

500 °C

Typical for Carbon Steel

Melting point

1380 - 1514 °C

Typical for Medium Carbon Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

41.7 W/(m·K)

100.0 °C

43.4 W/(m·K)

200.0 °C

43.2 W/(m·K)

300.0 °C

41.4 W/(m·K)

400.0 °C

39.1 W/(m·K)

500.0 °C

36.7 W/(m·K)

600.0 °C

34.1 W/(m·K)

Thermal diffusivity

20.0 °C

11.6 mm²/s

100.0 °C

11.3 mm²/s

200.0 °C

10.5 mm²/s

300.0 °C

9.5 mm²/s

400.0 °C

8.3 mm²/s

500.0 °C

7.1 mm²/s

600.0 °C

5.8 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

2.5E-7 Ω·m

100.0 °C

2.95E-7 Ω·m

200.0 °C

3.65E-7 Ω·m

300.0 °C

4.53E-7 Ω·m

400.0 °C

5.56E-7 Ω·m

500.0 °C

6.74E-7 Ω·m

600.0 °C

8.13E-7 Ω·m

Chemical properties

PropertyValue

Carbon

0.52 - 0.6 %

Chromium

0.4 %

Manganese

0.6 - 0.9 %

Molybdenum

0.1 %

Nickel

0.4 %

Phosphorus

0.04 %

Silicon

0.4 %

Sulfur

0.035 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10137-2 Grade S890QL – High-Strength Quenched & Tempered Steel for Heavy-Duty Applications
    2. EN 10137-3 Grade S500A: Quenched & Tempered Fine‑Grained Steel for Structural Applications
    3. EN 10083-1 Grade 51CrV4: Quenched & Tempered Steel (QT)
    4. EN 10213 Grade G17CrMo9-10 – Quenched & Tempered (QT) Steel for High-Temperature Applications
    5. EN 10132-3 Grade C55E: Quenched & Tempered Cold‑Rolled Steel for High‑Performance Applications
    6. EN 10250-2 Grade 28Mn6 Quenched & Tempered Steel – Ideal for High-Performance Automotive and Machine Parts
    7. EN 10083-2 Grade C55E Steel – Quenched, Tempered, and Surface Hardened for Heavy‑Duty Automotive & Industrial Parts
    8. EN 10250-2 Grade C55E: High-Performance Quenched & Tempered Steel for Heavy-Duty Applications
    9. EN 10250-2 Grade 20Mn5 Quenched & Tempered – High-Temperature Steel for Machine Engineering
    10. EN 10250-2 Grade C25E Steel – Quenched & Tempered (QT) for High-Performance Applications