EN 10217-7 X6CrNiNb18-10: Solution-Annealed Austenitic Steel for High-Temperature, Corrosion-Resistant Applications

The austenitic steel X6CrNiNb18-10 is available in the solution annealed condition. Welded circular tubes of this steel are used for compression load and for corrosive load at room temperature, low temperatures and elevated temperatures. The material is resistant to intercrystalline corrosion (up to 400 °C) also in the welded condition.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.9 - 7.93 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

206 GPa

20.0 °C

196 - 200 GPa

100.0 °C

190 - 194 GPa

200.0 °C

182 - 186 GPa

300.0 °C

174 - 179 GPa

400.0 °C

166 - 172 GPa

500.0 °C

158 - 165 GPa

600.0 °C

150 GPa

700.0 °C

142 GPa

800.0 °C

134 GPa

900.0 °C

127 GPa

1000.0 °C

120 GPa

Elongation

20.0 °C

35 %

Elongation, transverse

20.0 °C

30 %

Poisson's ratio

23.0 °C

0.3 [-]

Typical for Austenitic Stainless Steel

Shear modulus

23.0 °C

77 GPa

Typical for Austenitic Stainless Steel

Tensile strength

20.0 °C

510 - 740 MPa

Tensile strength, transverse

20.0 °C

510 - 740 MPa

Yield strength Rp0.2

20.0 °C

205 MPa

50.0 °C

195 MPa

100.0 °C

175 MPa

150.0 °C

165 MPa

200.0 °C

155 MPa

250.0 °C

145 MPa

300.0 °C

136 MPa

350.0 °C

130 MPa

400.0 °C

125 MPa

450.0 °C

121 MPa

500.0 °C

119 MPa

550.0 °C

118 MPa

Yield strength Rp0.2, transverse

20.0 °C

205 MPa

Yield strength Rp1.0

20.0 °C

240 MPa

50.0 °C

232 MPa

100.0 °C

210 MPa

150.0 °C

195 MPa

200.0 °C

185 MPa

250.0 °C

175 MPa

300.0 °C

167 MPa

350.0 °C

161 MPa

400.0 °C

156 MPa

450.0 °C

152 MPa

500.0 °C

149 MPa

550.0 °C

147 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.49E-5 1/K

20.0 °C

1.61E-5 1/K

100.0 °C

1.6E-5 - 1.67E-5 1/K

200.0 °C

1.65E-5 - 1.72E-5 1/K

300.0 °C

1.7E-5 - 1.77E-5 1/K

400.0 °C

1.75E-5 - 1.81E-5 1/K

500.0 °C

1.8E-5 - 1.84E-5 1/K

600.0 °C

1.88E-5 1/K

700.0 °C

1.91E-5 1/K

800.0 °C

1.94E-5 1/K

900.0 °C

1.97E-5 1/K

1000.0 °C

2E-5 1/K

Melting point

1230 - 1480 °C

Typical for Austenitic Stainless Steel

Specific heat capacity

-100.0 °C

440 J/(kg·K)

20.0 °C

472 - 500 J/(kg·K)

100.0 °C

487 J/(kg·K)

200.0 °C

503 J/(kg·K)

300.0 °C

512 J/(kg·K)

400.0 °C

520 J/(kg·K)

500.0 °C

530 J/(kg·K)

600.0 °C

541 J/(kg·K)

700.0 °C

551 J/(kg·K)

800.0 °C

559 J/(kg·K)

900.0 °C

565 J/(kg·K)

1000.0 °C

571 J/(kg·K)

Thermal conductivity

20.0 °C

14.3 - 15 W/(m·K)

100.0 °C

15.8 W/(m·K)

200.0 °C

17.5 W/(m·K)

300.0 °C

19 W/(m·K)

400.0 °C

20.5 W/(m·K)

500.0 °C

21.9 W/(m·K)

600.0 °C

23.3 W/(m·K)

700.0 °C

24.6 W/(m·K)

800.0 °C

26 W/(m·K)

900.0 °C

27.4 W/(m·K)

1000.0 °C

28.8 W/(m·K)

Thermal diffusivity

20.0 °C

3.8 mm²/s

100.0 °C

4 mm²/s

200.0 °C

4.2 mm²/s

300.0 °C

4.6 mm²/s

400.0 °C

4.8 mm²/s

500.0 °C

4.9 mm²/s

600.0 °C

5 mm²/s

700.0 °C

5.3 mm²/s

800.0 °C

5.6 mm²/s

900.0 °C

5.9 mm²/s

1000.0 °C

6 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

7.1E-7 - 7.3E-7 Ω·m

100.0 °C

7.76E-7 Ω·m

200.0 °C

8.49E-7 Ω·m

300.0 °C

9.14E-7 Ω·m

400.0 °C

9.71E-7 Ω·m

500.0 °C

1.02E-6 Ω·m

600.0 °C

1.07E-6 Ω·m

700.0 °C

1.1E-6 Ω·m

800.0 °C

1.14E-6 Ω·m

900.0 °C

1.17E-6 Ω·m

1000.0 °C

1.19E-6 Ω·m

Chemical properties

PropertyValue

Carbon

0.08 %

Chromium

17 - 19 %

Manganese

2 %

Nickel

9 - 12 %

Niobium

1 %

Phosphorus

0.05 %

Silicon

1 %

Sulfur

0.015 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10217-7 Grade X2CrNiMoCuWN25-7-4 – Solution Annealed Steel for Corrosion‑Resistant Tubes
    2. EN 10217-7 Grade X2CrNiMoN25-7-4 Solution-Annealed Steel (+AT) – High-Temperature Corrosion Resistance
    3. EN 10217-7 X2CrNiN23-4 Austenitic Ferritic Steel – Solution Annealed for Corrosion-Resistant Tubes
    4. EN 10217-7 Grade X1NiCrMoCuN25-20-7 – Solution‑Annealed Stainless Steel for High‑Temperature Corrosion Resistance
    5. EN 10222-5 X6CrNiNb18-10 – Solution Annealed Steel with Superior Corrosion Resistance
    6. EN 10250-4 Grade X6CrNiNb18-10 – Solution Annealed (+AT)
    7. EN 10217-7 Grade X1CrNiMoCuN20-18-7 – Solution Annealed Steel for High-Performance Applications
    8. EN 10217-7 X2CrNi18-9 Solution-Annealed Austenitic Steel – High-Performance Tubing
    9. EN 10217-7 Grade X2CrNiMoN22-5-3 Solution‑Annealed Steel (+AT) – High‑Performance, Corrosion‑Resistant Tubing
    10. EN 10217‑7 Grade X2CrNiMoN17‑13‑3 – Solution Annealed Steel for Corrosion‑Resistant, High‑Temperature Applications