EN 12163 CuZn30 R370 – Premium Copper Alloy for Precision Applications
CuZn30 (CW505L) is an unhardenable wrought alloy. High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for CuZn28. Corrosion resistance is similar to pure copper. Processing properties: warm forming: good cold forming: very good machinability: moderately hard and soft soldering: very good TIG-welding: good burnishing: very good CuZn30 is used for deep drawing components, musical instruments, hose tubes, springing elements, clockfaces and as cladding material. For the electrolytically tinned strip the coatings (Sn bright, Sn matt, Sn fuzed, SnPb) are listed by the application (better solderability, better corrosion resistance, reduction of the electrical contact resistance, better appearance) in the DIN EN 14436 : 2004-11 (Table 5)
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 8.5 - 8.55 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 20.0 °C | 114 GPa | |
100.0 °C | 112 GPa | ||
200.0 °C | 107 GPa | ||
300.0 °C | 103 GPa | ||
400.0 °C | 96 GPa | ||
500.0 °C | 88 GPa | ||
600.0 °C | 77 GPa | ||
700.0 °C | 67 GPa | ||
Elongation | 20.0 °C | 10 - 16 % | |
Elongation A10 | 20.0 °C | 8 % | |
Elongation A100 | 20.0 °C | 6 - 12 % | |
Elongation A11.3 | 20.0 °C | 14 % | |
Poisson's ratio | 20.0 °C | 0.34 [-] | |
Shear modulus | 23.0 °C | 40 GPa | Typical for Wrought Copper Brass |
Tensile strength | 20.0 °C | 370 MPa | |
Yield strength Rp0.2 | 20.0 °C | 230 - 320 MPa | |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 100.0 °C | 1.9E-5 1/K | |
150.0 °C | 1.9E-5 1/K | ||
300.0 °C | 2E-5 1/K | ||
Melting point | 875 - 1075 °C | Typical for Wrought Copper Brass | |
Specific heat capacity | 20.0 °C | 377 J/(kg·K) | |
100.0 °C | 398 J/(kg·K) | ||
200.0 °C | 410 J/(kg·K) | ||
300.0 °C | 419 J/(kg·K) | ||
400.0 °C | 431 J/(kg·K) | ||
500.0 °C | 444 J/(kg·K) | ||
600.0 °C | 452 J/(kg·K) | ||
700.0 °C | 456 J/(kg·K) | ||
Thermal conductivity | -200.0 °C | 50 W/(m·K) | |
20.0 °C | 121 - 126 W/(m·K) | ||
200.0 °C | 147 W/(m·K) | ||
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical conductivity | 20.0 °C | 1.60E+7 S/m |
Electrical resistivity | 200.0 °C | 7.7E-8 Ω·m |
500.0 °C | 1.08E-7 Ω·m | |
Specific Electrical conductivity | 28 % IACS | |
Chemical properties
| Property | Value |
|---|---|
Aluminium | 0.02 % |
Copper | 69 - 71 % |
Iron | 0.05 % |
Lead | 0.05 % |
Nickel | 0.3 % |
Tin | 0.1 % |
Metal
- EN 12163 CuZr TH Grade – High Strength Low‑Alloy Copper Alloy
- EN 12163 Grade CuBe2 M: High-Performance Hardenable Copper Alloy
- EN 12163 Grade CuZn10 M – High-Strength, Corrosion-Resistant Copper Alloy
- EN 12163 Grade CuZn30 H085 – Premium Unhardenable Copper Alloy for High-Strength Applications
- EN 12163 Grade CuZn30 H115 – Premium Copper Alloy for Precision Applications
- EN 12163 – CuCr1Zr R370: Premium Low‑Alloy Copper Alloy
- EN 12163 Grade CuZn28 R370 – High-Performance Unhardenable Copper Alloy
- EN 12163 CuZn33 R370 – Premium Copper Alloy for High-Performance Applications
- EN 12163 Grade CuZn30 (R460) – Premium Copper Alloy for Precision Applications
- EN 12163 CuZn36 (R370) – High‑Strength, Low‑Conductivity Copper Alloy