EN 10217-7 Grade X2CrNiMo17-12-2 Solution-Annealed Steel (+AT) – High-Performance Austenitic Steel for Corrosion & Temperature Resistance

The austenitic steel X2CrNiMo17-12-2 is available in the solution annealed condition. Welded circular tubes of this steel are used for compression load and for corrosive load at room temperature, low temperatures and elevated temperatures. The material is resistant to intercrystalline corrosion (up to 400 °C) also in the welded condition.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.96 - 8 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

206 GPa

20.0 °C

196 - 200 GPa

100.0 °C

190 - 194 GPa

200.0 °C

182 - 186 GPa

300.0 °C

174 - 179 GPa

400.0 °C

166 - 172 GPa

500.0 °C

158 - 165 GPa

600.0 °C

150 GPa

700.0 °C

142 GPa

800.0 °C

134 GPa

900.0 °C

127 GPa

1000.0 °C

120 GPa

Elongation

20.0 °C

40 %

Elongation, transverse

20.0 °C

30 %

Poisson's ratio

23.0 °C

0.3 [-]

Typical for Austenitic Stainless Steel

Shear modulus

23.0 °C

77 GPa

Typical for Austenitic Stainless Steel

Tensile strength

20.0 °C

490 - 690 MPa

Tensile strength, transverse

20.0 °C

490 - 690 MPa

Yield strength Rp0.2

20.0 °C

190 MPa

50.0 °C

182 MPa

100.0 °C

165 MPa

150.0 °C

150 MPa

200.0 °C

137 MPa

250.0 °C

127 MPa

300.0 °C

119 MPa

350.0 °C

113 MPa

400.0 °C

108 MPa

450.0 °C

103 MPa

500.0 °C

100 MPa

550.0 °C

98 MPa

Yield strength Rp0.2, transverse

20.0 °C

190 MPa

Yield strength Rp1.0

20.0 °C

225 MPa

50.0 °C

217 MPa

100.0 °C

200 MPa

150.0 °C

180 MPa

200.0 °C

165 MPa

250.0 °C

153 MPa

300.0 °C

145 MPa

350.0 °C

139 MPa

400.0 °C

135 MPa

450.0 °C

130 MPa

500.0 °C

128 MPa

550.0 °C

127 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.49E-5 1/K

20.0 °C

1.61E-5 1/K

100.0 °C

1.6E-5 - 1.67E-5 1/K

200.0 °C

1.65E-5 - 1.72E-5 1/K

300.0 °C

1.7E-5 - 1.77E-5 1/K

400.0 °C

1.75E-5 - 1.81E-5 1/K

500.0 °C

1.8E-5 - 1.84E-5 1/K

600.0 °C

1.88E-5 1/K

700.0 °C

1.91E-5 1/K

800.0 °C

1.94E-5 1/K

900.0 °C

1.97E-5 1/K

1000.0 °C

2E-5 1/K

Melting point

1230 - 1480 °C

Typical for Austenitic Stainless Steel

Specific heat capacity

-100.0 °C

440 J/(kg·K)

20.0 °C

472 - 500 J/(kg·K)

100.0 °C

487 J/(kg·K)

200.0 °C

503 J/(kg·K)

300.0 °C

512 J/(kg·K)

400.0 °C

520 J/(kg·K)

500.0 °C

530 J/(kg·K)

600.0 °C

541 J/(kg·K)

700.0 °C

551 J/(kg·K)

800.0 °C

559 J/(kg·K)

900.0 °C

565 J/(kg·K)

1000.0 °C

571 J/(kg·K)

Thermal conductivity

20.0 °C

13.3 - 15 W/(m·K)

100.0 °C

14.9 W/(m·K)

200.0 °C

16.5 W/(m·K)

300.0 °C

18.1 W/(m·K)

400.0 °C

19.5 W/(m·K)

500.0 °C

21 W/(m·K)

600.0 °C

22.4 W/(m·K)

700.0 °C

23.8 W/(m·K)

800.0 °C

25.2 W/(m·K)

Thermal diffusivity

20.0 °C

3.5 mm²/s

100.0 °C

3.8 mm²/s

200.0 °C

4 mm²/s

300.0 °C

4.3 mm²/s

400.0 °C

4.5 mm²/s

500.0 °C

4.7 mm²/s

600.0 °C

4.8 mm²/s

700.0 °C

5.1 mm²/s

800.0 °C

5.4 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

7.5E-7 - 7.91E-7 Ω·m

100.0 °C

8.45E-7 Ω·m

200.0 °C

9.19E-7 Ω·m

300.0 °C

9.77E-7 Ω·m

400.0 °C

1.03E-6 Ω·m

500.0 °C

1.08E-6 Ω·m

600.0 °C

1.12E-6 Ω·m

700.0 °C

1.15E-6 Ω·m

800.0 °C

1.18E-6 Ω·m

Chemical properties

PropertyValue

Carbon

0.03 %

Chromium

16.5 - 18.5 %

Manganese

2 %

Molybdenum

2 - 2.5 %

Nickel

10 - 13 %

Nitrogen

0.11 %

Phosphorus

0.05 %

Silicon

1 %

Sulfur

0.015 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10217-7 Grade X2CrNiMoCuWN25-7-4 – Solution Annealed Steel for Corrosion‑Resistant Tubes
    2. EN 10217-7 Grade X2CrNiMoN25-7-4 Solution-Annealed Steel (+AT) – High-Temperature Corrosion Resistance
    3. EN 10217-7 X2CrNiN23-4 Austenitic Ferritic Steel – Solution Annealed for Corrosion-Resistant Tubes
    4. EN 10269 X2CrNiMo17-12-2 Solution-Annealed Steel – Superior Corrosion Resistance & Formability
    5. EN 10217-7 Grade X1NiCrMoCuN25-20-7 – Solution‑Annealed Stainless Steel for High‑Temperature Corrosion Resistance
    6. EN 10222-5 Grade X2CrNiMo17-12-2 – Solution Annealed Steel for High-Performance Corrosion Resistance
    7. EN 10250-4 Grade X2CrNiMo17-12-2 Solution-Annealed Steel (+AT) – High Corrosion Resistance
    8. EN 10217-7 Grade X1CrNiMoCuN20-18-7 – Solution Annealed Steel for High-Performance Applications
    9. EN 10217-7 X2CrNi18-9 Solution-Annealed Austenitic Steel – High-Performance Tubing
    10. EN 10217-7 Grade X2CrNiMoN22-5-3 Solution‑Annealed Steel (+AT) – High‑Performance, Corrosion‑Resistant Tubing