EN 10222‑2 Grade P305GH Steel – Normalized & Tempered for Pressure Vessels
The high-temperature steel P305GH, material number 1.0436 is used for pressure vessels.
Properties
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 23.0 °C | 7.8 - 7.9 g/cm³ | Typical for Low Carbon Steel |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 200 - 215 GPa | Typical for Low Carbon Steel |
Elongation | 20.0 °C | 20 - 22 % | |
Poisson's ratio | 23.0 °C | 0.29 [-] | Typical for Low Carbon Steel |
Shear modulus | 23.0 °C | 82 GPa | Typical for Low Carbon Steel |
Tensile strength | 20.0 °C | 490 - 610 MPa | |
Yield strength | 20.0 °C | 280 MPa | |
Yield strength Rp0.2 | 20.0 °C | 270 MPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.32E-5 - 1.38E-5 1/K | Typical for Low Carbon Steel |
Max service temperature | 500 °C | Typical for Carbon Steel | |
Melting point | 1480 - 1526 °C | Typical for Low Carbon Steel | |
Specific heat capacity | 23.0 °C | 465 J/(kg·K) | Typical for Low Carbon Steel |
Thermal conductivity | 23.0 °C | 25 - 93 W/(m·K) | Typical for Low Carbon Steel |
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Electrical resistivity | 23.0 °C | 1.43E-7 - 1.74E-7 Ω·m | Typical for Carbon Steel |
Magnetic
| Property | Value | Comment |
|---|---|---|
Curie temperature | 770 °C | Typical for Low Carbon Steel |
Chemical properties
| Property | Value |
|---|---|
Carbon | 0.15 - 0.2 % |
Chromium | 0.3 % |
Copper | 0.3 % |
Manganese | 0.9 - 1.6 % |
Molybdenum | 0.08 % |
Nickel | 0.3 % |
Niobium | 0.01 % |
Phosphorus | 0.03 % |
Silicon | 0.4 % |
Sulfur | 0.015 % |
Titanium | 0.03 % |
Vanadium | 0.02 % |
Metal
- EN 10222-3 Grade 12Ni14 – Normalized & Tempered Nickel Alloy for Cryogenic Applications
- EN 10222-3 Grade 13MnNi6-3: Normalized & Tempered Cryogenic Alloy for Pressure Vessels
- EN 10250-2 Grade C30 Steel – Normalized & Tempered (+NT) for High Ductility Applications
- EN 10250‑2 Grade C40 Steel – Normalized & Tempered (NT) – Key Properties & Applications
- EN 10250-2 Grade C50 Normalized & Tempered Steel – High Strength & Abrasion Resistance
- EN 10222-2 Grade X10CrMoVNb9-1: Normalized & Tempered High-Temperature Stainless Steel for Pressure Vessels
- EN 10222-2: Grade 13CrMo4-5 (Normalized & Tempered) – Industrial Grade Steel for Pressure Vessels
- EN 10222-2 Grade 14MoV6-3 – Normalized & Tempered (NT) High-Temperature Steel for Pressure Vessels
- EN 10222-2 Grade P245GH – High-Temperature Steel, Normalized & Tempered (NT)
- EN 10222-2 Grade P280GH: Normalized & Tempered Steel for Pressure Vessels