EN 10222-2 Grade P305GH: High‑Temperature Quenched & Tempered Steel for Pressure Vessels
The high-temperature steel P305GH, material number 1.0436 is used for pressure vessels.
Properties
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 23.0 °C | 7.8 - 7.9 g/cm³ | Typical for Low Carbon Steel |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 200 - 215 GPa | Typical for Low Carbon Steel |
Elongation | 20.0 °C | 20 - 22 % | |
Poisson's ratio | 23.0 °C | 0.29 [-] | Typical for Low Carbon Steel |
Shear modulus | 23.0 °C | 82 GPa | Typical for Low Carbon Steel |
Tensile strength | 20.0 °C | 510 - 630 MPa | |
Yield strength | 20.0 °C | 285 MPa | |
Yield strength Rp0.2 | 20.0 °C | 275 MPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.32E-5 - 1.38E-5 1/K | Typical for Low Carbon Steel |
Max service temperature | 500 °C | Typical for Carbon Steel | |
Melting point | 1480 - 1526 °C | Typical for Low Carbon Steel | |
Specific heat capacity | 23.0 °C | 465 J/(kg·K) | Typical for Low Carbon Steel |
Thermal conductivity | 23.0 °C | 25 - 93 W/(m·K) | Typical for Low Carbon Steel |
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Electrical resistivity | 23.0 °C | 1.43E-7 - 1.74E-7 Ω·m | Typical for Carbon Steel |
Magnetic
| Property | Value | Comment |
|---|---|---|
Curie temperature | 770 °C | Typical for Low Carbon Steel |
Chemical properties
| Property | Value |
|---|---|
Carbon | 0.15 - 0.2 % |
Chromium | 0.3 % |
Copper | 0.3 % |
Manganese | 0.9 - 1.6 % |
Molybdenum | 0.08 % |
Nickel | 0.3 % |
Niobium | 0.01 % |
Phosphorus | 0.03 % |
Silicon | 0.4 % |
Sulfur | 0.015 % |
Titanium | 0.03 % |
Vanadium | 0.02 % |
Metal
- EN 10137-2 Grade S890QL – High-Strength Quenched & Tempered Steel for Heavy-Duty Applications
- EN 10137-3 Grade S500A: Quenched & Tempered Fine‑Grained Steel for Structural Applications
- EN 10083-1 Grade 51CrV4: Quenched & Tempered Steel (QT)
- EN 10213 Grade G17CrMo9-10 – Quenched & Tempered (QT) Steel for High-Temperature Applications
- EN 10085 Grade 15 CrMoV 5.9: Quenched & Tempered Steel for Durable Machine Components
- EN 10085 Grade 31CrMo12 – High-Performance Quenched & Tempered Steel for Heavy‑Duty Applications
- EN 10216-2 Grade 11CrMo9-10 Quenched & Tempered Seamless Tubes – High‑Temperature, High‑Pressure Applications
- EN 10222-2 Grade 13CrMo4-5 – High-Strength Quenched & Tempered Steel for Pressure Vessels
- EN 10222-2 Grade 16Mo3 Quenched & Tempered Steel (+QT) – High-Temperature, Pressure Vessel Grade
- EN 10222-2 Grade X20CrMoV11-1 – High‑Temperature Quenched & Tempered Steel (+QT)