EN 10216-5 Grade X8CrNiMoNb16-16 Solution-Annealed Steel: High-Temperature Resistance & Superior Creep Performance

Fully austenitic high temperature special steel which is resistant to scaling up to 750 degrees C and has a good creep resistance up to 700 degrees C. Used in steam and gas turbine construction (shovels, flanges, valves, nozzles, casings and bolts), for parts in the reactor technology and in the petrochemical industry.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

8.01 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

206 GPa

20.0 °C

196 GPa

100.0 °C

190 GPa

200.0 °C

182 GPa

300.0 °C

174 GPa

400.0 °C

166 GPa

500.0 °C

158 GPa

600.0 °C

150 GPa

700.0 °C

142 GPa

800.0 °C

134 GPa

Elongation

20.0 °C

35 %

Elongation, transverse

20.0 °C

22 %

Poisson's ratio

23.0 °C

0.3 [-]

Typical for Austenitic Stainless Steel

Shear modulus

23.0 °C

77 GPa

Typical for Austenitic Stainless Steel

Tensile strength

20.0 °C

530 - 690 MPa

Tensile strength, transverse

20.0 °C

530 - 690 MPa

Yield strength Rp0.2

20.0 °C

215 MPa

100.0 °C

195 MPa

200.0 °C

177 MPa

300.0 °C

157 MPa

400.0 °C

147 MPa

500.0 °C

137 MPa

550.0 °C

137 MPa

600.0 °C

132 MPa

Yield strength Rp0.2, transverse

20.0 °C

215 MPa

Yield strength Rp1.0

20.0 °C

255 MPa

100.0 °C

225 MPa

200.0 °C

206 MPa

300.0 °C

186 MPa

400.0 °C

177 MPa

500.0 °C

167 MPa

550.0 °C

167 MPa

600.0 °C

162 MPa

Yield strength Rp1.0, transverse

20.0 °C

255 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.49E-5 1/K

20.0 °C

1.61E-5 1/K

100.0 °C

1.67E-5 1/K

200.0 °C

1.72E-5 1/K

300.0 °C

1.77E-5 1/K

400.0 °C

1.81E-5 1/K

500.0 °C

1.84E-5 1/K

600.0 °C

1.88E-5 1/K

700.0 °C

1.91E-5 1/K

800.0 °C

1.94E-5 1/K

900.0 °C

1.97E-5 1/K

1000.0 °C

2E-5 1/K

Melting point

1230 - 1480 °C

Typical for Austenitic Stainless Steel

Specific heat capacity

-100.0 °C

440 J/(kg·K)

20.0 °C

472 J/(kg·K)

100.0 °C

487 J/(kg·K)

200.0 °C

503 J/(kg·K)

300.0 °C

512 J/(kg·K)

400.0 °C

520 J/(kg·K)

500.0 °C

530 J/(kg·K)

600.0 °C

541 J/(kg·K)

700.0 °C

551 J/(kg·K)

800.0 °C

559 J/(kg·K)

900.0 °C

565 J/(kg·K)

1000.0 °C

571 J/(kg·K)

Thermal conductivity

20.0 °C

13.5 W/(m·K)

100.0 °C

14.9 W/(m·K)

200.0 °C

16.7 W/(m·K)

300.0 °C

18.3 W/(m·K)

400.0 °C

19.8 W/(m·K)

500.0 °C

21.3 W/(m·K)

600.0 °C

22.7 W/(m·K)

700.0 °C

24.2 W/(m·K)

800.0 °C

25.6 W/(m·K)

Thermal diffusivity

20.0 °C

3.6 mm²/s

100.0 °C

3.7 mm²/s

200.0 °C

4 mm²/s

300.0 °C

4.4 mm²/s

400.0 °C

4.6 mm²/s

500.0 °C

4.7 mm²/s

600.0 °C

4.9 mm²/s

700.0 °C

5.2 mm²/s

800.0 °C

5.5 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

7.75E-7 Ω·m

100.0 °C

8.42E-7 Ω·m

200.0 °C

9.04E-7 Ω·m

300.0 °C

9.62E-7 Ω·m

400.0 °C

1.01E-6 Ω·m

500.0 °C

1.06E-6 Ω·m

600.0 °C

1.1E-6 Ω·m

700.0 °C

1.13E-6 Ω·m

800.0 °C

1.16E-6 Ω·m

Chemical properties

PropertyValue

Carbon

0.04 - 0.1 %

Chromium

15.5 - 17.5 %

Manganese

1.5 %

Molybdenum

1.6 - 2 %

Nickel

15.5 - 17.5 %

Niobium

1.2 %

Phosphorus

0.04 %

Silicon

0.3 - 0.6 %

Sulfur

0.015 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10216-5 X2CrNiMoSi18-5-3 Solution-Annealed Stainless Steel – High-Performance Grade for Pressurized Tubes
    2. EN 10216-5 Grade X2CrNiMoCuWN25-7-4 – Solution Annealed (Plus AT) – Premium Austenitic‑Ferritic Alloy
    3. EN 10216-5 X2CrNiMoN25-7-4 Austenitic‑Ferritic Steel – Solution Annealed for Superior Corrosion Resistance
    4. EN 10216-5 X3CrNiN18-11: Solution-Annealed Austenitic Stainless Steel (+AT)
    5. EN 10216-5 Grade X10CrNiMoMnNbVB15-10-1 – Solution Annealed with Additional Treatment
    6. EN 10216‑5 Grade X6CrNiMo17‑13‑2 – Solution Annealed for High‑Temperature Performance
    7. EN 10216-5 X7CrNiTiB18-10: High‑Creep Resistant, Solution‑Annealed Steel (+AT)
    8. EN 10216-5 X2CrNi18-9 Solution-Annealed AISI 304 Steel – Superior Corrosion Resistance
    9. EN 10216-5 Grade X3CrNiMo17-13-3: Solution-Annealed Steel for Superior Corrosion Resistance
    10. EN 10216-5 Grade X6CrNi18-10 Austenitic Steel – Solution Annealed with Additional Treatment