EN 10088-4 X2CrTi12 Soft-Annealed Steel (+A) – Properties & Specs

Properties are in DIN EN 10088-2 : 2005-09 / Material variant DIN EN 10088-1 :2005-09

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.7 - 7.73 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

20.0 °C

217 - 220 GPa

100.0 °C

215 GPa

200.0 °C

188 - 210 GPa

300.0 °C

164 - 205 GPa

400.0 °C

195 GPa

Elongation

20.0 °C

25 %

Elongation A80

20.0 °C

25 %

Elongation A80, transverse

20.0 °C

25 %

Elongation, transverse

20.0 °C

25 %

Poisson's ratio

20.0 °C

0.29 [-]

Shear modulus

20.0 °C

84.82 GPa

Tensile strength

20.0 °C

380 - 560 MPa

Tensile strength, transverse

20.0 °C

380 - 560 MPa

Yield strength Rp0.2

20.0 °C

210 MPa

100.0 °C

200 MPa

150.0 °C

195 MPa

200.0 °C

190 MPa

250.0 °C

186 MPa

300.0 °C

180 MPa

350.0 °C

160 MPa

Yield strength Rp0.2, transverse

20.0 °C

220 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

20.0 °C

1.02E-5 1/K

100.0 °C

1.05E-5 1/K

200.0 °C

1.09E-5 - 1.1E-5 1/K

300.0 °C

1.13E-5 - 1.15E-5 1/K

400.0 °C

1.16E-5 - 1.2E-5 1/K

500.0 °C

1.2E-5 1/K

600.0 °C

1.22E-5 1/K

Melting point

1425 - 1530 °C

Typical for Ferritic Stainless Steel

Specific heat capacity

20.0 °C

439 - 460 J/(kg·K)

100.0 °C

474 J/(kg·K)

200.0 °C

498 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

538 J/(kg·K)

500.0 °C

564 J/(kg·K)

600.0 °C

598 J/(kg·K)

Thermal conductivity

20.0 °C

25 - 25.9 W/(m·K)

100.0 °C

25.3 W/(m·K)

200.0 °C

25.2 W/(m·K)

300.0 °C

25.2 W/(m·K)

400.0 °C

25.4 W/(m·K)

500.0 °C

25.7 W/(m·K)

600.0 °C

25.9 W/(m·K)

Thermal diffusivity

20.0 °C

7.6 mm²/s

100.0 °C

6.6 mm²/s

200.0 °C

6.1 mm²/s

300.0 °C

5.8 mm²/s

400.0 °C

5.3 mm²/s

500.0 °C

4.8 mm²/s

600.0 °C

4.1 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

5.59E-7 - 6E-7 Ω·m

100.0 °C

6.4E-7 Ω·m

200.0 °C

7.32E-7 Ω·m

300.0 °C

8.17E-7 Ω·m

400.0 °C

8.97E-7 Ω·m

500.0 °C

9.74E-7 Ω·m

600.0 °C

1.05E-6 Ω·m

Chemical properties

PropertyValue

Carbon

0.03 %

Chromium

10.5 - 12.5 %

Manganese

1 %

Phosphorus

0.04 %

Silicon

1 %

Sulfur

0.015 %

Titanium

0.65 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10088-1 X70CrMo15: Soft Annealed Grade for Cutting Tools & Industrial Applications
    2. X105CrMo17 Soft Annealed Steel (EN 10088-1) – High Hardening & Wear Resistance
    3. EN 10083-2 Grade C50R Soft Annealed Steel (+A) – High Strength & Workability
    4. EN 10083-2 Grade C55R Soft Annealed Steel – Enhanced Workability for Automotive and Engineering Applications
    5. EN 10269 Grade 40CrMoV4-6 Soft-Annealed Steel – Ideal for High‑Temperature Fasteners
    6. EN 10269 Grade 42CrMo4 Soft-Annealed Steel – High Strength & Wear Resistance
    7. EN 10269 25CrMo4 Soft-Annealed Steel – High Strength & Toughness for Automotive & Industrial Applications
    8. EN 10269 Grade 30CrNiMo8 Soft-Annealed Steel (+A) – Ideal for High‑Stress, Low‑Temperature Applications
    9. EN 10312 X2CrTi12 Soft-Annealed Grade (+A) – High-Temperature Ferritic Steel for Automotive Silencers & Gas Detoxification
    10. X2CrTi12 Soft-Annealed Ferritic Steel – DIN 17456 Grade for High-Temperature Applications