EN 10216-5 X6CrNiNb18-10 Solution Annealed Steel (+AT) – Superior Corrosion Resistance & Weldability

Material X6CrNiNb18-10 is comparable to X 6 CrNiNb 18 10 acc. to DIN 17440: 1985-07. Its corrosion properties are comparable to 1.4541. The steel is resistant to intercrystalline corrosion also in sensitized condition, but it shows heat-crack susceptibility under certain welding conditions. Widely applicable for welded parts in chemical apparatus engineering, in food and luxury food industry, in film and photo industry as well as for household appliances. The steel is unsuitable for mirror finishing due to its Nb-content.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.93 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

-100.0 °C

206 GPa

20.0 °C

196 - 199.26 GPa

95.0 °C

194.43 GPa

100.0 °C

190 GPa

150.0 °C

189.61 GPa

200.0 °C

182 GPa

205.0 °C

184.78 GPa

260.0 °C

179.95 GPa

300.0 °C

174 GPa

315.0 °C

175.13 GPa

370.0 °C

170.99 GPa

400.0 °C

166 GPa

425.0 °C

166.16 GPa

485.0 °C

161.34 GPa

500.0 °C

158 GPa

540.0 °C

157.2 GPa

595.0 °C

151.69 GPa

600.0 °C

150 GPa

650.0 °C

147.54 GPa

700.0 °C

142 GPa

705.0 °C

142.72 GPa

760.0 °C

137.9 GPa

800.0 °C

134 GPa

815.0 °C

133.76 GPa

870.0 °C

128.93 GPa

900.0 °C

127 GPa

1000.0 °C

120 GPa

Elongation

20.0 °C

35 %

Elongation, transverse

20.0 °C

30 %

Poisson's ratio

20.0 °C

0.27 [-]

95.0 °C

0.28 [-]

150.0 °C

0.29 [-]

205.0 °C

0.29 [-]

260.0 °C

0.29 [-]

315.0 °C

0.3 [-]

370.0 °C

0.31 [-]

425.0 °C

0.31 [-]

485.0 °C

0.32 [-]

540.0 °C

0.33 [-]

595.0 °C

0.33 [-]

650.0 °C

0.32 [-]

705.0 °C

0.33 [-]

760.0 °C

0.35 [-]

815.0 °C

0.35 [-]

870.0 °C

0.36 [-]

Shear modulus

20.0 °C

78.6 GPa

95.0 °C

75.84 GPa

150.0 °C

73.77 GPa

205.0 °C

71.71 GPa

260.0 °C

69.64 GPa

315.0 °C

67.57 GPa

370.0 °C

65.5 GPa

425.0 °C

63.43 GPa

485.0 °C

61.36 GPa

540.0 °C

59.3 GPa

595.0 °C

57.23 GPa

650.0 °C

55.85 GPa

705.0 °C

53.78 GPa

760.0 °C

51.11 GPa

815.0 °C

49.64 GPa

870.0 °C

47.57 GPa

Tensile strength

20.0 °C

510 - 740 MPa

Tensile strength, transverse

20.0 °C

510 - 740 MPa

Yield strength Rp0.2

20.0 °C

205 MPa

50.0 °C

195 MPa

100.0 °C

175 MPa

150.0 °C

165 MPa

200.0 °C

155 MPa

250.0 °C

145 MPa

300.0 °C

136 MPa

350.0 °C

130 MPa

400.0 °C

125 MPa

450.0 °C

121 MPa

500.0 °C

119 MPa

550.0 °C

118 MPa

Yield strength Rp0.2, transverse

20.0 °C

205 MPa

Yield strength Rp1.0

20.0 °C

240 MPa

50.0 °C

232 MPa

100.0 °C

210 MPa

150.0 °C

195 MPa

200.0 °C

185 MPa

250.0 °C

175 MPa

300.0 °C

167 MPa

350.0 °C

161 MPa

400.0 °C

156 MPa

450.0 °C

152 MPa

500.0 °C

149 MPa

550.0 °C

147 MPa

Yield strength Rp1.0, transverse

20.0 °C

240 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.49E-5 1/K

20.0 °C

1.61E-5 1/K

100.0 °C

1.67E-5 1/K

200.0 °C

1.72E-5 1/K

300.0 °C

1.77E-5 1/K

400.0 °C

1.81E-5 1/K

425.0 °C

1.76E-5 1/K

485.0 °C

1.78E-5 1/K

500.0 °C

1.84E-5 1/K

540.0 °C

1.8E-5 1/K

595.0 °C

1.83E-5 1/K

600.0 °C

1.88E-5 1/K

650.0 °C

1.85E-5 1/K

700.0 °C

1.91E-5 1/K

705.0 °C

1.87E-5 1/K

800.0 °C

1.94E-5 1/K

900.0 °C

1.97E-5 1/K

1000.0 °C

2E-5 1/K

Melting point

1230 - 1480 °C

Typical for Austenitic Stainless Steel

Specific heat capacity

-100.0 °C

440 J/(kg·K)

20.0 °C

472 J/(kg·K)

100.0 °C

487 J/(kg·K)

200.0 °C

503 J/(kg·K)

300.0 °C

512 J/(kg·K)

400.0 °C

520 J/(kg·K)

500.0 °C

530 J/(kg·K)

600.0 °C

541 J/(kg·K)

700.0 °C

551 J/(kg·K)

800.0 °C

559 J/(kg·K)

900.0 °C

565 J/(kg·K)

1000.0 °C

571 J/(kg·K)

Thermal conductivity

20.0 °C

14.3 W/(m·K)

100.0 °C

15.8 W/(m·K)

200.0 °C

17.5 W/(m·K)

300.0 °C

19 W/(m·K)

400.0 °C

20.5 W/(m·K)

500.0 °C

21.9 W/(m·K)

600.0 °C

23.3 W/(m·K)

700.0 °C

24.6 W/(m·K)

800.0 °C

26 W/(m·K)

900.0 °C

27.4 W/(m·K)

1000.0 °C

28.8 W/(m·K)

Thermal diffusivity

20.0 °C

3.8 mm²/s

100.0 °C

4 mm²/s

200.0 °C

4.2 mm²/s

300.0 °C

4.6 mm²/s

400.0 °C

4.8 mm²/s

500.0 °C

4.9 mm²/s

600.0 °C

5 mm²/s

700.0 °C

5.3 mm²/s

800.0 °C

5.6 mm²/s

900.0 °C

5.9 mm²/s

1000.0 °C

6 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

7.1E-7 Ω·m

100.0 °C

7.76E-7 Ω·m

200.0 °C

8.49E-7 Ω·m

300.0 °C

9.14E-7 Ω·m

400.0 °C

9.71E-7 Ω·m

500.0 °C

1.02E-6 Ω·m

600.0 °C

1.07E-6 Ω·m

700.0 °C

1.1E-6 Ω·m

800.0 °C

1.14E-6 Ω·m

900.0 °C

1.17E-6 Ω·m

1000.0 °C

1.19E-6 Ω·m

Chemical properties

PropertyValue

Carbon

0.08 %

Chromium

17 - 19 %

Manganese

2 %

Nickel

9 - 12 %

Niobium

1 %

Phosphorus

0.04 %

Silicon

1 %

Sulfur

0.015 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10216-5 X2CrNiMoSi18-5-3 Solution-Annealed Stainless Steel – High-Performance Grade for Pressurized Tubes
    2. EN 10216-5 Grade X2CrNiMoCuWN25-7-4 – Solution Annealed (Plus AT) – Premium Austenitic‑Ferritic Alloy
    3. EN 10216-5 X2CrNiMoN25-7-4 Austenitic‑Ferritic Steel – Solution Annealed for Superior Corrosion Resistance
    4. EN 10216-5 X3CrNiN18-11: Solution-Annealed Austenitic Stainless Steel (+AT)
    5. EN 10222-5 X6CrNiNb18-10 – Solution Annealed Steel with Superior Corrosion Resistance
    6. EN 10216-5 Grade X10CrNiMoMnNbVB15-10-1 – Solution Annealed with Additional Treatment
    7. EN 10216‑5 Grade X6CrNiMo17‑13‑2 – Solution Annealed for High‑Temperature Performance
    8. EN 10250-4 Grade X6CrNiNb18-10 – Solution Annealed (+AT)
    9. EN 10216-5 X7CrNiTiB18-10: High‑Creep Resistant, Solution‑Annealed Steel (+AT)
    10. EN 10217-7 X6CrNiNb18-10: Solution-Annealed Austenitic Steel for High-Temperature, Corrosion-Resistant Applications