EN 10216-5 Grade X2CrNiN18-10 – Solution Annealed with Aging Treatment

The austenitic CrNi-steel X2CrNiN18-10, comparable to X 2 CrNiN 18 10 acc. to DIN 17440 : 1985-07 (invalid), shows a higher yield point by nitrogen alloying which survives also at higher temperatures. This is used in pressure vessel and leightweight construction. Improvement of the corrosion resistance by its N-content. The material is resistant to intercrystalline corrosion also in sensitized condition. Suitability for chemical apparatus engineering owing to resistance to nitric acid and other oxidizing media. This steel is well cold formable and suitable for mirror finishing. Excellent applicability for refrigeration up to -270 deg. due to its cryogenic toughness (for the comparable DIN-mark).

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.9 - 7.93 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

206 GPa

20.0 °C

196 - 200 GPa

100.0 °C

190 - 194 GPa

200.0 °C

182 - 186 GPa

300.0 °C

174 - 179 GPa

400.0 °C

166 - 172 GPa

500.0 °C

158 - 165 GPa

600.0 °C

150 GPa

700.0 °C

142 GPa

800.0 °C

134 GPa

900.0 °C

127 GPa

1000.0 °C

120 GPa

Elongation

20.0 °C

35 %

Elongation, transverse

20.0 °C

30 %

Poisson's ratio

23.0 °C

0.3 [-]

Typical for Austenitic Stainless Steel

Shear modulus

23.0 °C

77 GPa

Typical for Austenitic Stainless Steel

Tensile strength

20.0 °C

550 - 760 MPa

Tensile strength, transverse

20.0 °C

550 - 760 MPa

Yield strength Rp0.2

20.0 °C

270 MPa

50.0 °C

255 MPa

100.0 °C

205 MPa

150.0 °C

175 MPa

200.0 °C

157 MPa

250.0 °C

145 MPa

300.0 °C

136 MPa

350.0 °C

130 MPa

400.0 °C

125 MPa

450.0 °C

121 MPa

500.0 °C

119 MPa

550.0 °C

118 MPa

Yield strength Rp0.2, transverse

20.0 °C

270 MPa

Yield strength Rp1.0

20.0 °C

305 MPa

50.0 °C

282 MPa

100.0 °C

240 MPa

150.0 °C

210 MPa

200.0 °C

187 MPa

250.0 °C

175 MPa

300.0 °C

167 MPa

350.0 °C

160 MPa

400.0 °C

156 MPa

450.0 °C

152 MPa

500.0 °C

149 MPa

550.0 °C

147 MPa

Yield strength Rp1.0, transverse

20.0 °C

305 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.49E-5 1/K

20.0 °C

1.61E-5 1/K

100.0 °C

1.6E-5 - 1.67E-5 1/K

200.0 °C

1.65E-5 - 1.72E-5 1/K

300.0 °C

1.7E-5 - 1.77E-5 1/K

400.0 °C

1.75E-5 - 1.81E-5 1/K

500.0 °C

1.8E-5 - 1.84E-5 1/K

600.0 °C

1.88E-5 1/K

700.0 °C

1.91E-5 1/K

800.0 °C

1.94E-5 1/K

900.0 °C

1.97E-5 1/K

1000.0 °C

2E-5 1/K

Melting point

1230 - 1480 °C

Typical for Austenitic Stainless Steel

Specific heat capacity

-100.0 °C

440 J/(kg·K)

20.0 °C

472 - 500 J/(kg·K)

100.0 °C

487 J/(kg·K)

200.0 °C

503 J/(kg·K)

300.0 °C

512 J/(kg·K)

400.0 °C

520 J/(kg·K)

500.0 °C

530 J/(kg·K)

600.0 °C

541 J/(kg·K)

700.0 °C

551 J/(kg·K)

800.0 °C

559 J/(kg·K)

900.0 °C

565 J/(kg·K)

1000.0 °C

571 J/(kg·K)

Thermal conductivity

20.0 °C

14.3 - 15 W/(m·K)

100.0 °C

15.8 W/(m·K)

200.0 °C

17.5 W/(m·K)

300.0 °C

19 W/(m·K)

400.0 °C

20.5 W/(m·K)

500.0 °C

21.9 W/(m·K)

600.0 °C

23.3 W/(m·K)

700.0 °C

24.6 W/(m·K)

800.0 °C

26 W/(m·K)

900.0 °C

27.4 W/(m·K)

1000.0 °C

28.8 W/(m·K)

Thermal diffusivity

20.0 °C

3.8 mm²/s

100.0 °C

4 mm²/s

200.0 °C

4.2 mm²/s

300.0 °C

4.6 mm²/s

400.0 °C

4.8 mm²/s

500.0 °C

4.9 mm²/s

600.0 °C

5 mm²/s

700.0 °C

5.3 mm²/s

800.0 °C

5.6 mm²/s

900.0 °C

5.9 mm²/s

1000.0 °C

6 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

7.1E-7 - 7.3E-7 Ω·m

100.0 °C

7.76E-7 Ω·m

200.0 °C

8.49E-7 Ω·m

300.0 °C

9.14E-7 Ω·m

400.0 °C

9.71E-7 Ω·m

500.0 °C

1.02E-6 Ω·m

600.0 °C

1.07E-6 Ω·m

700.0 °C

1.1E-6 Ω·m

800.0 °C

1.14E-6 Ω·m

900.0 °C

1.17E-6 Ω·m

1000.0 °C

1.19E-6 Ω·m

Chemical properties

PropertyValue

Carbon

0.03 %

Chromium

17 - 19.5 %

Manganese

2 %

Nickel

8.5 - 11.5 %

Nitrogen

0.12 - 0.22 %

Phosphorus

0.04 %

Silicon

1 %

Sulfur

0.015 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10216-5 X2CrNiMoSi18-5-3 Solution-Annealed Stainless Steel – High-Performance Grade for Pressurized Tubes
    2. EN 10216-5 Grade X2CrNiMoCuWN25-7-4 – Solution Annealed (Plus AT) – Premium Austenitic‑Ferritic Alloy
    3. EN 10216-5 X2CrNiMoN25-7-4 Austenitic‑Ferritic Steel – Solution Annealed for Superior Corrosion Resistance
    4. EN 10216-5 X3CrNiN18-11: Solution-Annealed Austenitic Stainless Steel (+AT)
    5. EN 10222-5 X2CrNiN18-10 – Solution Annealed + AT: High‑Performance Austenitic Stainless Steel
    6. EN 10216-5 Grade X10CrNiMoMnNbVB15-10-1 – Solution Annealed with Additional Treatment
    7. EN 10216‑5 Grade X6CrNiMo17‑13‑2 – Solution Annealed for High‑Temperature Performance
    8. EN 10250-4 Grade X2CrNiN18-10: Solution‑Annealed Stainless Steel (+AT)
    9. EN 10216-5 X7CrNiTiB18-10: High‑Creep Resistant, Solution‑Annealed Steel (+AT)
    10. EN 10217-7 Grade X2CrNiN18-10: Solution-Annealed Stainless Steel for High-Performance Applications