EN 10216-5 X2CrNiMoN17‑13‑3: Solution Annealed Steel for High-Performance Corrosion Resistance

Material X2CrNiMoN17-13-3 is comparable to X 2 CrNiMoN 17 13 3 acc. to DIN 17440 : 1985-07. It is a fully austenitic steel that is suitable for mirror finishing. It shows higher strength owing to nitrogen alloying and owing to more molybdenum addition higher corrosion resistance especially to non oxidizing acids and halogenated media than 1.4406. Resistance to intercrystalline corrosion in delivery condition as well as in sensitized condition. The material shows higher resistance to selective corrosion than 1.4435 and excellent limiting fatigue stres behavior also under chemical load. Furthermore it shows good cryogenic toughness. It is therefore suitable for refrigeration up to -270 deg.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

8 - 8.01 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

-100.0 °C

206 GPa

20.0 °C

196 - 200 GPa

100.0 °C

190 - 194 GPa

200.0 °C

182 - 186 GPa

300.0 °C

174 - 179 GPa

400.0 °C

166 - 172 GPa

500.0 °C

158 - 165 GPa

600.0 °C

150 GPa

700.0 °C

142 GPa

800.0 °C

134 GPa

Elongation

20.0 °C

35 %

Elongation, transverse

20.0 °C

30 %

Poisson's ratio

20.0 °C

0.28 [-]

Shear modulus

20.0 °C

77.3 GPa

Tensile strength

20.0 °C

580 - 800 MPa

Tensile strength, transverse

20.0 °C

580 - 800 MPa

Yield strength Rp0.2

20.0 °C

295 MPa

50.0 °C

255 MPa

100.0 °C

215 MPa

150.0 °C

195 MPa

200.0 °C

175 MPa

250.0 °C

165 MPa

300.0 °C

155 MPa

350.0 °C

150 MPa

400.0 °C

145 MPa

450.0 °C

140 MPa

500.0 °C

138 MPa

550.0 °C

136 MPa

Yield strength Rp0.2, transverse

20.0 °C

295 MPa

Yield strength Rp1.0

20.0 °C

330 MPa

50.0 °C

290 MPa

100.0 °C

245 MPa

150.0 °C

225 MPa

200.0 °C

205 MPa

250.0 °C

195 MPa

300.0 °C

185 MPa

350.0 °C

180 MPa

400.0 °C

175 MPa

450.0 °C

170 MPa

500.0 °C

168 MPa

550.0 °C

166 MPa

Yield strength Rp1.0, transverse

20.0 °C

330 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.49E-5 1/K

20.0 °C

1.61E-5 1/K

100.0 °C

1.6E-5 - 1.67E-5 1/K

200.0 °C

1.65E-5 - 1.72E-5 1/K

300.0 °C

1.7E-5 - 1.77E-5 1/K

400.0 °C

1.75E-5 - 1.81E-5 1/K

500.0 °C

1.8E-5 - 1.84E-5 1/K

600.0 °C

1.88E-5 1/K

700.0 °C

1.91E-5 1/K

800.0 °C

1.94E-5 1/K

900.0 °C

1.97E-5 1/K

1000.0 °C

2E-5 1/K

Melting point

1230 - 1480 °C

Typical for Austenitic Stainless Steel

Specific heat capacity

-100.0 °C

440 J/(kg·K)

20.0 °C

472 - 500 J/(kg·K)

100.0 °C

487 J/(kg·K)

200.0 °C

503 J/(kg·K)

300.0 °C

512 J/(kg·K)

400.0 °C

520 J/(kg·K)

500.0 °C

530 J/(kg·K)

600.0 °C

541 J/(kg·K)

700.0 °C

551 J/(kg·K)

800.0 °C

559 J/(kg·K)

900.0 °C

565 J/(kg·K)

1000.0 °C

571 J/(kg·K)

Thermal conductivity

20.0 °C

13.5 - 15 W/(m·K)

100.0 °C

14.9 W/(m·K)

200.0 °C

16.7 W/(m·K)

300.0 °C

18.3 W/(m·K)

400.0 °C

19.8 W/(m·K)

500.0 °C

21.3 W/(m·K)

600.0 °C

22.7 W/(m·K)

700.0 °C

24.2 W/(m·K)

800.0 °C

25.6 W/(m·K)

Thermal diffusivity

20.0 °C

3.6 mm²/s

100.0 °C

3.7 mm²/s

200.0 °C

4 mm²/s

300.0 °C

4.4 mm²/s

400.0 °C

4.6 mm²/s

500.0 °C

4.7 mm²/s

600.0 °C

4.9 mm²/s

700.0 °C

5.2 mm²/s

800.0 °C

5.5 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

7.5E-7 - 7.75E-7 Ω·m

100.0 °C

8.42E-7 Ω·m

200.0 °C

9.04E-7 Ω·m

300.0 °C

9.62E-7 Ω·m

400.0 °C

1.01E-6 Ω·m

500.0 °C

1.06E-6 Ω·m

600.0 °C

1.1E-6 Ω·m

700.0 °C

1.13E-6 Ω·m

800.0 °C

1.16E-6 Ω·m

Chemical properties

PropertyValue

Carbon

0.03 %

Chromium

16.5 - 18.5 %

Manganese

2 %

Molybdenum

2.5 - 3 %

Nickel

11 - 14 %

Nitrogen

0.12 - 0.22 %

Phosphorus

0.04 %

Silicon

1 %

Sulfur

0.015 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10216-5 X2CrNiMoSi18-5-3 Solution-Annealed Stainless Steel – High-Performance Grade for Pressurized Tubes
    2. EN 10216-5 Grade X2CrNiMoCuWN25-7-4 – Solution Annealed (Plus AT) – Premium Austenitic‑Ferritic Alloy
    3. EN 10216-5 X2CrNiMoN25-7-4 Austenitic‑Ferritic Steel – Solution Annealed for Superior Corrosion Resistance
    4. EN 10216-5 X3CrNiN18-11: Solution-Annealed Austenitic Stainless Steel (+AT)
    5. EN 10269 X2CrNiMoN17-13-3 – High‑Strength, Corrosion‑Resistant Austenitic Steel, Solution Annealed (+AT)
    6. EN 10222-5 Grade X2CrNiMoN17-13-3 – Solution Annealed Steel with Superior Corrosion Resistance
    7. EN 10216-5 Grade X10CrNiMoMnNbVB15-10-1 – Solution Annealed with Additional Treatment
    8. EN 10216‑5 Grade X6CrNiMo17‑13‑2 – Solution Annealed for High‑Temperature Performance
    9. EN 10250-4 X2CrNiMoN17-13-3 Steel – Solution Annealed, Enhanced Corrosion Resistance