DIN 1725-1 Grade 3.3354 H32 Aluminium Alloy – Superior Corrosion Resistance & Rivet Performance
Non-heat-treatable aluminium alloy used for rivets in joints of Mg alloys and AlMg alloys. The material has a better corrosion resistance, particularly sea-water resistance, than other Al riveted joints and is capable of being permanently headed.
Properties
General
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Density | 20.0 °C | 2.64 g/cm³ | H32 | WL 3.3354, DIN 1725-1 | Wire |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Elastic modulus | 20.0 °C | 71.0 GPa | H32 | WL 3.3354, DIN 1725-1 | Wire | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||||
Poisson's ratio | 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||||
Shear modulus | 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | ||||
Shear strength | 20.0 °C | 170.0 MPa | H32 | WL 3.3354, DIN 1725-1 | Wire | Transverse |
20.0 °C | 170.0 - 193.0 MPa | H32 | WL 3.3354, DIN 1725-1 | Transverse | ||
20.0 °C | 170.0 MPa | H32 | WL 3.3354, DIN 1725-1 | Wire | ||
20.0 °C | 193.0 MPa | H32 | WL 3.3354, DIN 1725-1 | Transverse | ||
Tensile strength | 20.0 °C | 300.0 - 360.0 MPa | H32 | WL 3.3354, DIN 1725-1 | Wire |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Coefficient of thermal expansion | 2.2e-05 - 2.5e-05 1/K | Typical for Wrought 5000 Series Aluminium | ||||
Max service temperature | 150.0 °C | Typical for Wrought 5000 Series Aluminium | ||||
Melting point | 560.0 - 655.0 °C | Typical for Wrought 5000 Series Aluminium | ||||
Specific heat capacity | 20.0 °C | 904.0 J/(kg·K) | H32 | WL 3.3354, DIN 1725-1 | Wire | |
Thermal conductivity | 20.0 °C | 110.0 - 140.0 W/(m·K) | H32 | WL 3.3354, DIN 1725-1 | Wire |
Electrical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Electrical conductivity | 20.0 °C | 15000000.0 - 19000000.0 S/m | H32 | WL 3.3354, DIN 1725-1 | Wire | |
Electrical resistivity | 3.3e-08 - 5e-08 Ω·m | Typical for Wrought 5000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Chromium | 0.2 | H32 | WL 3.3354, DIN 1725-1 | Wire |
Copper | 0.1 | H32 | WL 3.3354, DIN 1725-1 | Wire |
Iron | 0.5 | H32 | WL 3.3354, DIN 1725-1 | Wire |
Magnesium | 4.5 - 5.6 % | H32 | WL 3.3354, DIN 1725-1 | Wire |
Manganese | 0.1 - 0.6 % | H32 | WL 3.3354, DIN 1725-1 | Wire |
Silicon | 0.4 | H32 | WL 3.3354, DIN 1725-1 | Wire |
Zinc | 0.2 | H32 | WL 3.3354, DIN 1725-1 | Wire |
Technological properties
| Property | ||
|---|---|---|
| Workability | Good workability. | |
Metal
- DIN 1725-1 Grade 3.4415 – High-Performance Al–Zn Alloy for Corrosion Protection
- DIN 1725-1 Grade 3.2315 T5 Aluminum Tube – Technical Specifications
- DIN 1725-1 Grade 3.4365 T5 – High‑Strength 7075 Aluminum Alloy for Aerospace
- DIN 1725‑1 Grade 3.4365 O – Premium High‑Strength Aluminum Alloy for Aerospace
- DIN 1725-1 Grade 3.4335 T5 Aluminum Alloy – High-Performance Wrought Grade
- DIN 1725-1 Grade 3.3211 T8 Alloy: Superior Corrosion Resistance & Finish
- DIN 1725-1 Grade 3.0615 T8: High-Performance Free-Cutting Alloy
- DIN 1725-1 Grade 3.1255 T8 Aluminum Alloy – High Strength & Precision Machining
- DIN 1725-1 Grade 3.0615 T3 – High‑Performance AlMgSiPb Free‑Cutting Alloy
- DIN 1725-1 Grade 3.3354 H14: High-Strength Magnesium Alloy with Excellent Corrosion Resistance