DIN 1725-1 Grade 3.3211 T6510 Aluminium Alloy – Properties & Applications
DIN 3.3211 is a readily available alloy that has good surface finish and ability to be anodized.Easy of weldability and brazability with nice surface finish. Resistance to corrosion from seawater and atmospheric conditions. Suitable for hot forging.
Properties
General
| Property | Value | Comment |
|---|---|---|
Density | 2.7 g/cm³ | Typical for Wrought 6000 Series Aluminium |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Elastic modulus | 70.0 GPa | Typical for Wrought 6000 Series Aluminium | ||||
Elongation | 20.0 °C | 9.0 % | T6510 | WL 3.3214-1, DIN 1725-1 | Rod | |
Hardness, Brinell | 20.0 °C | 90.0 [-] | T6510 | WL 3.3214-1, DIN 1725-1 | Rod | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 6000 Series Aluminium | ||||
Poisson's ratio | 0.33 [-] | Typical for Wrought 6000 Series Aluminium | ||||
Shear modulus | 26.0 - 26.5 GPa | Typical for Wrought 6000 Series Aluminium | ||||
Tensile strength | 20.0 °C | 270.0 MPa | T6510 | WL 3.3214-1, DIN 1725-1 | Rod |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 1.6e-05 - 2.4e-05 1/K | Typical for Wrought 6000 Series Aluminium |
Melting point | 555.0 - 655.0 °C | Typical for Wrought 6000 Series Aluminium |
Specific heat capacity | 887.0 - 963.0 J/(kg·K) | Typical for Wrought 6000 Series Aluminium |
Thermal conductivity | 170.0 - 220.0 W/(m·K) | Typical for Wrought 6000 Series Aluminium |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 21000000.0 - 34000000.0 S/m | Typical for Wrought 6000 Series Aluminium |
Electrical resistivity | 2.9e-08 - 5e-08 Ω·m | Typical for Wrought 6000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Chromium | 0.04 - 0.35 % | T6510 | WL 3.3214-1, DIN 1725-1 | Rod |
Copper | 0.15 - 0.4 % | T6510 | WL 3.3214-1, DIN 1725-1 | Rod |
Iron | 0.7 | T6510 | WL 3.3214-1, DIN 1725-1 | Rod |
Magnesium | 0.8 - 1.2 % | T6510 | WL 3.3214-1, DIN 1725-1 | Rod |
Manganese | 0.15 | T6510 | WL 3.3214-1, DIN 1725-1 | Rod |
Silicon | 0.4 - 0.8 % | T6510 | WL 3.3214-1, DIN 1725-1 | Rod |
Titanium | 0.15 | T6510 | WL 3.3214-1, DIN 1725-1 | Rod |
Zinc | 0.25 | T6510 | WL 3.3214-1, DIN 1725-1 | Rod |
Technological properties
| Property | ||
|---|---|---|
| Workability | Excellent workability. | |
Metal
- DIN 1725-1 Grade 3.3211 (T4510) – High-Performance Aluminium Alloy
- DIN 1725-1 Grade 3.3211 T4511 – High-Performance Anodizable Aluminium Alloy
- DIN 1725-1 Grade 3.3211 (T6511) – Premium Aluminium Alloy with Superior Weldability
- DIN 1725-1 Grade 3.3211 T451 Aluminium Alloy – Superior Corrosion Resistance & Anodization
- DIN 1725‑1 Grade 3.3211 T652 Aluminium Alloy – Performance & Applications
- DIN 1725‑1 Grade 3.3211 T651: High‑Performance Aluminium Alloy for Corrosion‑Resistant Applications
- DIN 1725-1 Grade 3.3211 T4 Aluminium – Corrosion‑Resistant, Anodizable & Weldable
- DIN 1725-1 Grade 3.3211 T42 Aluminium Alloy – High-Performance, Corrosion-Resistant
- DIN 1725-1 Grade 3.3211 T6 – Premium 6063 Aluminium Alloy for Corrosion-Resistant Applications
- DIN 1725-1 Grade 3.3211 T62 – High-Performance Aluminium Alloy for Anodizing and Corrosion Resistance