DIN 1725-1 Grade 3.1255 T3: Premium Aluminum Alloy for Strength & Precision
DIN 3.1255 is an alloy with strength, machinability and welding capabilities, Aluminum Alloy DIN 3.1255 is an excellent option. It is a precipitation hardening alloy that maintains strength after heat treatment.
Properties
General
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Density | 2.8 g/cm³ | T3 | EN 573-3, EN 485, EN 754 | ||
20.0 °C | 2.8 g/cm³ | T3 | DIN 1725-1, EN 573-3, EN 573-4 | Sheet |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Elastic modulus | 73.0 GPa | T3 | EN 573-3, EN 485, EN 754 | |||
20.0 °C | 72.0 GPa | T3 | DIN 1725-1, EN 573-3, EN 573-4 | Sheet | ||
Elongation | 6.0 % | T3 | EN 573-3, EN 754 | A50 | ||
8.0 % | T3 | EN 573-3, EN 754 | A100 | |||
14.0 % | T3 | EN 573-3, EN 485 | A50 | |||
20.0 °C | 8.0 % | T3 | DIN 1725-1, EN 573-3, EN 573-4 | Sheet | ||
20.0 °C | 11.0 % | T3 | DIN 1725-1, EN 573-3, EN 573-4 | Sheet | ||
20.0 °C | 12.0 % | T3 | DIN 1725-1, EN 573-3, EN 573-4 | Sheet | ||
Hardness, Brinell | 111.0 [-] | T3 | EN 573-3, EN 485 | |||
112.0 [-] | T3 | EN 573-3, EN 485 | ||||
20.0 °C | 100.0 [-] | T3 | DIN 1725-1, EN 573-3, EN 573-4 | Sheet | ||
20.0 °C | 100.0 - 105.0 [-] | T3 | DIN 1725-1, EN 573-3, EN 573-4 | Sheet | ||
20.0 °C | 105.0 [-] | T3 | DIN 1725-1, EN 573-3, EN 573-4 | Sheet | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | ||||
Poisson's ratio | 0.33 [-] | Typical for Wrought 2000 Series Aluminium | ||||
Shear modulus | 27.4 GPa | T3 | EN 573-3, EN 485, EN 754 | |||
Tensile strength | 380.0 MPa | T3 | EN 573-3, EN 754 | |||
395.0 MPa | T3 | EN 573-3, EN 485 | ||||
400.0 MPa | T3 | EN 573-3, EN 485 | ||||
20.0 °C | 390.0 MPa | T3 | DIN 1725-1, EN 573-3, EN 573-4 | Sheet | ||
20.0 °C | 400.0 MPa | T3 | DIN 1725-1, EN 573-3, EN 573-4 | Sheet |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Coefficient of thermal expansion | -50 °C | 2.1e-05 1/K | T3 | EN 573-3, EN 485, EN 754, DIN 1725-1, EN 573-4 | Sheet | |
-50.0 °C | 2.1e-05 1/K | T3 | EN 573-3, EN 485, EN 754, DIN 1725-1, EN 573-4 | Sheet | ||
20 °C | 2.1e-05 1/K | T3 | EN 573-3, EN 485, EN 754, DIN 1725-1, EN 573-4 | Sheet | ||
20 °C | 2.28e-05 1/K | T3 | EN 573-3, EN 485, EN 754, DIN 1725-1, EN 573-4 | Sheet | ||
20 °C | 2.3e-05 1/K | T3 | EN 573-3, EN 485, EN 754 | |||
20 °C | 2.36e-05 1/K | T3 | EN 573-3, EN 485, EN 754, DIN 1725-1, EN 573-4 | Sheet | ||
20 °C | 2.46e-05 1/K | T3 | EN 573-3, EN 485, EN 754, DIN 1725-1, EN 573-4 | Sheet | ||
100 °C | 2.28e-05 1/K | T3 | EN 573-3, EN 485, EN 754, DIN 1725-1, EN 573-4 | Sheet | ||
100.0 °C | 2.28e-05 1/K | T3 | EN 573-3, EN 485, EN 754, DIN 1725-1, EN 573-4 | Sheet | ||
100 °C | 2.3e-05 1/K | T3 | EN 573-3, EN 485, EN 754 | |||
200 °C | 2.36e-05 1/K | T3 | EN 573-3, EN 485, EN 754, DIN 1725-1, EN 573-4 | Sheet | ||
200.0 °C | 2.36e-05 1/K | T3 | EN 573-3, EN 485, EN 754, DIN 1725-1, EN 573-4 | Sheet | ||
300 °C | 2.46e-05 1/K | T3 | EN 573-3, EN 485, EN 754, DIN 1725-1, EN 573-4 | Sheet | ||
300.0 °C | 2.46e-05 1/K | T3 | EN 573-3, EN 485, EN 754, DIN 1725-1, EN 573-4 | Sheet | ||
Melting point | 505.0 - 635.0 °C | T3 | EN 573-3, EN 485, EN 754 | |||
510.0 - 640.0 °C | T3 | EN 573-3, EN 485, EN 754 | ||||
Specific heat capacity | 816.0 - 963.0 J/(kg·K) | Typical for Wrought 2000 Series Aluminium | ||||
Thermal conductivity | 134.0 - 193.0 W/(m·K) | T3 | EN 573-3, EN 485, EN 754 | |||
20.0 °C | 140.0 - 200.0 W/(m·K) | T3 | DIN 1725-1, EN 573-3, EN 573-4, EN 485, EN 754 | Sheet |
Electrical
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Electrical conductivity | 21000000.0 - 24000000.0 S/m | T3 | EN 573-3, EN 485, EN 754 | ||
20.0 °C | 20000000.0 - 29000000.0 S/m | T3 | DIN 1725-1, EN 573-3, EN 573-4, EN 485, EN 754 | Sheet | |
Electrical resistivity | 3.45e-08 - 5e-08 Ω·m | T3 | EN 573-3, EN 485, EN 754 | ||
4.17e-08 - 4.76e-08 Ω·m | T3 | EN 573-3, EN 485, EN 754 |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Chromium | 0.1 % | T3 | DIN 1725-1, EN 573-3, EN 573-4, EN 485, EN 754 | Sheet |
Copper | 3.9 - 5.0 % | T3 | DIN 1725-1, EN 573-3, EN 573-4, EN 485, EN 754 | Sheet |
Iron | 0.7 % | T3 | DIN 1725-1, EN 573-3, EN 573-4 | Sheet |
0.70 % | T3 | EN 573-3, EN 485, EN 754 | ||
Magnesium | 0.2 - 0.8 % | T3 | DIN 1725-1, EN 573-3, EN 573-4, EN 485, EN 754 | Sheet |
Manganese | 0.4 - 1.2 % | T3 | DIN 1725-1, EN 573-3, EN 573-4, EN 485, EN 754 | Sheet |
Silicon | 0.5 - 1.2 % | T3 | DIN 1725-1, EN 573-3, EN 573-4, EN 485, EN 754 | Sheet |
Titanium | 0.15 % | T3 | DIN 1725-1, EN 573-3, EN 573-4, EN 485, EN 754 | Sheet |
Zinc | 0.25 % | T3 | DIN 1725-1, EN 573-3, EN 573-4, EN 485, EN 754 | Sheet |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | decorative: not suitable, Protective: acceptable | |
| Brazing | hard brazing (with flux/ without flux): not suitable / not suitable, friction soldering: acceptable, soft brazing with flux: not suitable | |
| Corrosion properties | Seawater: sufficient, weathering: acceptable | |
| Workability | Bending / Spinning (cold): gut (O) / ungeeignet, Impact extrusion (cold): not suitable, Deep drawing / upsetting (Condition) acceptable (O) / not suitable | |
Metal
- DIN 1725-1 Grade 3.4415 – High-Performance Al–Zn Alloy for Corrosion Protection
- DIN 1725-1 Grade 3.2315 T5 Aluminum Tube – Technical Specifications
- DIN 1725-1 F46 Aluminum Alloy (Grade 3.1255) – High Strength, Machinable, Weldable
- DIN 1725-1 Grade 3.4365 T5 – High‑Strength 7075 Aluminum Alloy for Aerospace
- DIN 1725‑1 Grade 3.4365 O – Premium High‑Strength Aluminum Alloy for Aerospace
- DIN 1725-1 Grade 3.4335 T5 Aluminum Alloy – High-Performance Wrought Grade
- DIN 1725-1 Grade 3.3211 T8 Alloy: Superior Corrosion Resistance & Finish
- DIN 1725-1 Grade 3.0615 T8: High-Performance Free-Cutting Alloy
- DIN 1725-1 Grade 3.1255 T8 Aluminum Alloy – High Strength & Precision Machining
- DIN 1725-1 Grade 3.0615 T3 – High‑Performance AlMgSiPb Free‑Cutting Alloy