DIN 1725-1 Grade 3.3523 T6 – High-Performance Aluminum Alloy

Aluminum DIN 3.3523 is a non-heat treatable alloy with excellent finishing qualities. DIN 3.3523 offers better corrosion resistance than most aluminum alloys, especially to salt water and marine atmospheres. This alloy can be readily welded using most common techniques and is in fact offers some of the best welding characteristics of all aluminum alloys.

Properties

General

PropertyTemperatureValueConditionRelated StandardsShape

Density

20.0 °C

2.68 g/cm³

T6

DIN 1725-1, EN 573-3, EN 573-4, WL 3.3524-1

Sheet, Strip, Wire

Mechanical

PropertyTemperatureValueConditionRelated StandardsShapeComment

Elastic modulus

20.0 °C

72.0

T6

DIN 1725-1, EN 573-3, EN 573-4, WL 3.3524-1

Sheet, Strip, Wire

Elongation

20.0 °C

5.0 %

T6

DIN 1725-1, EN 573-3, EN 573-4, WL 3.3524-1

Wire

A100

20.0 °C

6.0 %

T6

DIN 1725-1, EN 573-3, EN 573-4, WL 3.3524-1

Sheet, Strip

A10

20.0 °C

7.0 %

T6

DIN 1725-1, EN 573-3, EN 573-4, WL 3.3524-1

Sheet, Strip

20.0 °C

9.0 %

T6

DIN 1725-1, EN 573-3, EN 573-4, WL 3.3524-1

Wire

A10

Hardness, Brinell

20.0 °C

65.0 [-]

T6

DIN 1725-1, EN 573-3, EN 573-4, WL 3.3524-1

Wire

20.0 °C

80.0 [-]

T6

DIN 1725-1, EN 573-3, EN 573-4, WL 3.3524-1

Sheet, Strip

Plane-Strain Fracture Toughnes

22.0 - 35.0 MPa·√m

Typical for Wrought 5000 Series Aluminium

Poisson's ratio

0.33 [-]

Typical for Wrought 5000 Series Aluminium

Shear modulus

20.0 °C

27.0

T6

DIN 1725-1, EN 573-3, EN 573-4, WL 3.3524-1

Sheet, Strip, Wire

Shear strength

20.0 °C

125.0 MPa

T6

DIN 1725-1, EN 573-3, EN 573-4, WL 3.3524-1

Wire

Tensile strength

20.0 °C

240.0 MPa

T6

DIN 1725-1, EN 573-3, EN 573-4, WL 3.3524-1

Wire

20.0 °C

250.0 - 290.0 MPa

T6

DIN 1725-1, EN 573-3, EN 573-4, WL 3.3524-1

Sheet, Strip

Thermal

PropertyTemperatureValueConditionRelated StandardsShapeComment

Coefficient of thermal expansion

-50.0 °C

2.21e-05 1/K

T6

DIN 1725-1, EN 573-3, EN 573-4, WL 3.3524-1

Sheet, Strip, Wire

100.0 °C

2.38e-05 1/K

T6

DIN 1725-1, EN 573-3, EN 573-4, WL 3.3524-1

Sheet, Strip, Wire

200.0 °C

2.48e-05 1/K

T6

DIN 1725-1, EN 573-3, EN 573-4, WL 3.3524-1

Sheet, Strip, Wire

300.0 °C

2.57e-05 1/K

T6

DIN 1725-1, EN 573-3, EN 573-4, WL 3.3524-1

Sheet, Strip, Wire

Max service temperature

150.0 °C

Typical for Wrought 5000 Series Aluminium

Melting point

560.0 - 655.0 °C

Typical for Wrought 5000 Series Aluminium

Specific heat capacity

20.0 °C

900.0 J/(kg·K)

T6

DIN 1725-1, EN 573-3, EN 573-4, WL 3.3524-1

Sheet, Strip, Wire

Thermal conductivity

20.0 °C

150.0

T6

DIN 1725-1, EN 573-3, EN 573-4, WL 3.3524-1

Sheet, Strip, Wire

Electrical

PropertyTemperatureValueConditionRelated StandardsShapeComment

Electrical conductivity

20.0 °C

21000000.0

T6

DIN 1725-1, EN 573-3, EN 573-4, WL 3.3524-1

Sheet, Strip, Wire

Electrical resistivity

3.3e-08 - 5e-08 Ω·m

Typical for Wrought 5000 Series Aluminium

Chemical properties

PropertyValueConditionRelated StandardsShape

Chromium

0.15 - 0.35 %

T6

DIN 1725-1, EN 573-3, EN 573-4, WL 3.3524-1

Sheet, Strip, Wire

Copper

0.1

T6

DIN 1725-1, EN 573-3, EN 573-4, WL 3.3524-1

Sheet, Strip, Wire

Iron

0.4

T6

DIN 1725-1, EN 573-3, EN 573-4, WL 3.3524-1

Sheet, Strip, Wire

Magnesium

2.2 - 2.8 %

T6

DIN 1725-1, EN 573-3, EN 573-4, WL 3.3524-1

Sheet, Strip, Wire

Manganese

0.1

T6

DIN 1725-1, EN 573-3, EN 573-4, WL 3.3524-1

Sheet, Strip, Wire

Silicon

0.25

T6

DIN 1725-1, EN 573-3, EN 573-4, WL 3.3524-1

Sheet, Strip, Wire

Zinc

0.1

T6

DIN 1725-1, EN 573-3, EN 573-4, WL 3.3524-1

Sheet, Strip, Wire

Technological properties

Property
Workability

Good workability.


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. DIN 1725-1 Grade 3.4415 – High-Performance Al–Zn Alloy for Corrosion Protection
    2. DIN 1725-1 Grade 3.2315 T5 Aluminum Tube – Technical Specifications
    3. DIN 1725-1 Grade 3.3523 (H34) – High‑Performance, Corrosion‑Resistant Aluminum Alloy
    4. DIN 1725-1 Grade 3.4365 T5 – High‑Strength 7075 Aluminum Alloy for Aerospace
    5. DIN 1725-1 (Grade 3.3523 G25) – Superior Corrosion-Resistant Aluminum Alloy
    6. DIN 1725‑1 Grade 3.4365 O – Premium High‑Strength Aluminum Alloy for Aerospace
    7. DIN 1725-1 Grade 3.4335 T5 Aluminum Alloy – High-Performance Wrought Grade
    8. DIN 1725-1 Grade 3.3211 T8 Alloy: Superior Corrosion Resistance & Finish
    9. DIN 1725-1 Grade 3.0615 T8: High-Performance Free-Cutting Alloy
    10. DIN 1725-1 Grade 3.1255 T8 Aluminum Alloy – High Strength & Precision Machining