EN 10277-2 Grade C10 Cold-Drawn Steel – Low-Strength, Wear-Resistant Parts

Steel C10 is suitable for parts of low core strength in vehicle and machine engineering, that are predominantly wear loaded (e.g. full dog points, levers, compression moldings and stamped parts). Lowest application temperature -25 °C, most favorable application area 5 to 10 mm nominal size. As a bright steel product it is used in the form of bars, bright, straight, in various conditions (see DIN EN 10277 : 1999-10).

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.85 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

210 - 212 GPa

100.0 °C

205 - 207 GPa

200.0 °C

193 - 199 GPa

300.0 °C

185 - 192 GPa

400.0 °C

175 - 184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Elongation

20.0 °C

8 - 12 %

Poisson's ratio

20.0 °C

0.28 [-]

Shear modulus

20.0 °C

81 GPa

Tensile strength

20.0 °C

320 - 760 MPa

Yield strength Rp0.2

20.0 °C

180 - 350 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.08E-5 1/K

20.0 °C

1.19E-5 1/K

100.0 °C

1.1E-5 - 1.25E-5 1/K

200.0 °C

1.18E-5 - 1.3E-5 1/K

300.0 °C

1.36E-5 1/K

400.0 °C

1.32E-5 - 1.41E-5 1/K

500.0 °C

1.45E-5 1/K

600.0 °C

1.49E-5 1/K

Max service temperature

500 °C

Typical for Carbon Steel

Max service temperature, long

-25 - 0 °C

Melting point

1480 - 1526 °C

Typical for Low Carbon Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

460 - 461 J/(kg·K)

100.0 °C

479 - 480 J/(kg·K)

200.0 °C

499 - 520 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

57.5 - 58.7 W/(m·K)

100.0 °C

54.4 - 55.7 W/(m·K)

200.0 °C

50.2 - 51.9 W/(m·K)

300.0 °C

47.6 W/(m·K)

400.0 °C

43.4 - 44 W/(m·K)

500.0 °C

39.6 W/(m·K)

600.0 °C

36 W/(m·K)

Thermal diffusivity

20.0 °C

15.9 mm²/s

100.0 °C

14.3 mm²/s

200.0 °C

12.5 mm²/s

300.0 °C

10.8 mm²/s

400.0 °C

9.2 mm²/s

500.0 °C

7.6 mm²/s

600.0 °C

6.1 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

1.1E-7 Ω·m

100.0 °C

2.3E-7 Ω·m

200.0 °C

3.04E-7 Ω·m

300.0 °C

3.94E-7 Ω·m

400.0 °C

5.01E-7 Ω·m

500.0 °C

6.25E-7 Ω·m

600.0 °C

7.7E-7 Ω·m

Magnetic

PropertyValueComment

Curie temperature

770 °C

Typical for Low Carbon Steel

Chemical properties

PropertyValue

Carbon

0.07 - 0.13 %

Manganese

0.3 - 0.6 %

Phosphorus

0.05 %

Silicon

0.4 %

Sulfur

0.045 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10277-2 Grade E295GC Cold Drawn Steel – High Strength & Wear Resistance
    2. EN 10277‑2 Grade E335GC Cold Drawn Steel – High Strength & Wear Resistance
    3. EN 10277-2 Grade ZSt50-2: Premium Cold-Drawn Steel for High-Performance Applications
    4. EN 10277‑2 Grade ZSt60‑2: Premium Cold‑Drawn Steel for High‑Wear, High‑Strength Applications
    5. EN 10277-2 Grade ZSt70-2: Premium Cold-Drawn High-Carbon Steel for Wear-Resistant Components
    6. EN 10277-2 Grade C35 Cold-Drawn Steel – High Strength, Low Temperature Performance
    7. EN 10277-2 Grade C40 Cold Drawn Steel – High Strength for Vehicle & Machine Engineering
    8. EN 10277-2 Grade C45 Cold Drawn Steel – High-Performance Structural Material
    9. EN 10277-2 Grade C50 Cold Drawn Steel – High Strength & Wear Resistance
    10. EN 10277-2 Grade C60 Cold-Drawn Steel – High Strength & Wear Resistance