EN 10272 X3CrNiMo17-13-3 Solution-Annealed Steel – Superior Corrosion Resistance

The steel grade X3CrNiMo17-13-3 acc. to DIN EN 10272 : 2001-01is used for hot and cold formed rods for pressure vessels. The corrosion behaviour of the steel is similar to 1.4401. Slightly improved resistance to selective attack due to the higher Mo-content. The material is resistant to intercrystalline corrosion (ic) in delivery condition, in sensitized condition for cross sections up to 40 mm resistance to ic for cross sections up to 40 mm if the sensitization treatment of 10 min. has been carried out at 650°C +/- 10°C with subsequent cooling.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

8 - 8.01 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

-100.0 °C

206 GPa

20.0 °C

196 - 200 GPa

100.0 °C

190 - 194 GPa

200.0 °C

182 - 186 GPa

300.0 °C

174 - 179 GPa

400.0 °C

166 - 172 GPa

500.0 °C

158 - 165 GPa

600.0 °C

150 GPa

700.0 °C

142 GPa

800.0 °C

134 GPa

Elongation

20.0 °C

40 %

Elongation, transverse

20.0 °C

30 %

Hardness, Brinell

20.0 °C

215 [-]

Hardness, Brinell, trans

20.0 °C

215 [-]

Poisson's ratio

20.0 °C

0.28 [-]

Shear modulus

20.0 °C

77.3 GPa

Tensile strength

20.0 °C

500 - 700 MPa

100.0 °C

460 MPa

150.0 °C

440 MPa

200.0 °C

420 MPa

250.0 °C

415 MPa

300.0 °C

410 MPa

350.0 °C

410 MPa

400.0 °C

410 MPa

500.0 °C

390 MPa

Tensile strength, transverse

20.0 °C

500 - 700 MPa

Yield strength Rp0.2

20.0 °C

200 MPa

100.0 °C

175 MPa

150.0 °C

158 MPa

200.0 °C

145 MPa

250.0 °C

135 MPa

300.0 °C

127 MPa

350.0 °C

120 MPa

400.0 °C

115 MPa

450.0 °C

112 MPa

500.0 °C

110 MPa

550.0 °C

108 MPa

Yield strength Rp0.2, transverse

20.0 °C

200 MPa

Yield strength Rp1.0

20.0 °C

235 MPa

100.0 °C

210 MPa

150.0 °C

190 MPa

200.0 °C

175 MPa

250.0 °C

165 MPa

300.0 °C

155 MPa

350.0 °C

150 MPa

400.0 °C

145 MPa

450.0 °C

141 MPa

500.0 °C

139 MPa

550.0 °C

137 MPa

Yield strength Rp1.0, transverse

20.0 °C

235 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.49E-5 1/K

20.0 °C

1.61E-5 1/K

100.0 °C

1.6E-5 - 1.67E-5 1/K

200.0 °C

1.65E-5 - 1.72E-5 1/K

300.0 °C

1.7E-5 - 1.77E-5 1/K

400.0 °C

1.75E-5 - 1.81E-5 1/K

500.0 °C

1.8E-5 - 1.84E-5 1/K

600.0 °C

1.88E-5 1/K

700.0 °C

1.91E-5 1/K

800.0 °C

1.94E-5 1/K

900.0 °C

1.97E-5 1/K

1000.0 °C

2E-5 1/K

Melting point

1230 - 1480 °C

Typical for Austenitic Stainless Steel

Specific heat capacity

-100.0 °C

440 J/(kg·K)

20.0 °C

472 - 500 J/(kg·K)

100.0 °C

487 J/(kg·K)

200.0 °C

503 J/(kg·K)

300.0 °C

512 J/(kg·K)

400.0 °C

520 J/(kg·K)

500.0 °C

530 J/(kg·K)

600.0 °C

541 J/(kg·K)

700.0 °C

551 J/(kg·K)

800.0 °C

559 J/(kg·K)

900.0 °C

565 J/(kg·K)

1000.0 °C

571 J/(kg·K)

Thermal conductivity

20.0 °C

13.5 - 15 W/(m·K)

100.0 °C

14.9 W/(m·K)

200.0 °C

16.7 W/(m·K)

300.0 °C

18.3 W/(m·K)

400.0 °C

19.8 W/(m·K)

500.0 °C

21.3 W/(m·K)

600.0 °C

22.7 W/(m·K)

700.0 °C

24.2 W/(m·K)

800.0 °C

25.6 W/(m·K)

Thermal diffusivity

20.0 °C

3.6 mm²/s

100.0 °C

3.7 mm²/s

200.0 °C

4 mm²/s

300.0 °C

4.4 mm²/s

400.0 °C

4.6 mm²/s

500.0 °C

4.7 mm²/s

600.0 °C

4.9 mm²/s

700.0 °C

5.2 mm²/s

800.0 °C

5.5 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

7.5E-7 - 7.75E-7 Ω·m

100.0 °C

8.42E-7 Ω·m

200.0 °C

9.04E-7 Ω·m

300.0 °C

9.62E-7 Ω·m

400.0 °C

1.01E-6 Ω·m

500.0 °C

1.06E-6 Ω·m

600.0 °C

1.1E-6 Ω·m

700.0 °C

1.13E-6 Ω·m

800.0 °C

1.16E-6 Ω·m

Chemical properties

PropertyValue

Carbon

0.05 %

Chromium

16.5 - 18.5 %

Manganese

2 %

Molybdenum

2.5 - 3 %

Nickel

10.5 - 13 %

Nitrogen

0.1 - 0.11 %

Phosphorus

0.05 %

Silicon

1 %

Sulfur

0.015 - 0.03 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10272 X2CrNiN23-4 Duplex Steel – Solution Annealed (+AT) – High Strength, Corrosion Resistance
    2. X2CrNiMoCuN25-6-3 Austenitic Steel – EN 10272 Grade, Solution Annealed + AT for Pressure Vessel Rods
    3. EN 10272 Grade X2CrNiMoCuWN25-7-4 Solution-Annealed Steel – Superior Corrosion Resistance & High Strength
    4. X2CrNiMoN25-7-4 Austenitic Steel – Solution Annealed, High-Performance Cold/Warm Rolled Strips, Sheets, and Profiles
    5. EN 10250-4 X3CrNiMo17-13-3 Solution-Annealed Steel: Superior Corrosion Resistance for Chemical Applications
    6. EN 10217-7 Grade X3CrNiMo17-13-3 – Solution Annealed (AT) – High-Performance Austenitic Steel
    7. EN 10216-5 Grade X3CrNiMo17-13-3: Solution-Annealed Steel for Superior Corrosion Resistance
    8. EN 10028-7 Grade X3CrNiMo17-13-3 Solution-Annealed Steel – Enhanced Corrosion Resistance
    9. EN 10272 Grade X2CrNi18-9 (Solution Annealed) – Corrosion‑Resistant Steel for Pressure Vessels
    10. X2CrNiMo17-12-3 Solution-Annealed Steel (EN 10272) – High-Performance Pressure Vessel Grade