DIN 1712-3 Grade 3.0255 H1x Aluminum Alloy – High Conductivity & Corrosion Resistance

Pure aluminium This material is well anodically oxidizable, and possesses a good electrical and thermal conductivity. The splinter-giving workability is bad because of danger of smearing. Its mechanical strength is low, the plasticity high. The forming capacity and the chemical as well as the weather proofness are excellent. The material is well suitable for welding and braze welding. Application: apparatus engineering, roll bond, z-bond, household devices, camp and transportation containers for the chemical, pharmaceutical and food industry, roofings, linings, arts and crafts, packing, flow pressed parts (tubes, tube, doses, bottles), reflectors, generally metal-describe, large bottles (to 10 l), metal goods, far neck catches, heat exchanger (profiles, gilled pipes), pressure tanks according to AD-W 6/1, liquid air separation, thermal insulation, antennas, parabolic reflector, tank -, silo trucks, body parts, aircraft construction, tools, forms and devices in mechanical engineering.

Quantity: One truck load – Specialty products on request.Additional services: Via Cindal (the Aludium R&D department): R&D services, benchmarking, chemical audits, material specification, process optimisation, quality monitoring, sample analysis, prototyping, training

Properties

General

Property	Temperature	Value	Condition	Related Standards	Shape
Density	20.0 °C	2.7 g/cm³	H1x	DIN 1712-3, EN 573-3, EN 573-4	Sheet, Flat, Strip

Mechanical

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Elastic modulus	-195.0 °C	78.4 GPa	H1x	DIN 1712-3, EN 573-3, EN 573-4	Sheet, Flat, Strip
	-85.0 °C	73.5 GPa	H1x	DIN 1712-3, EN 573-3, EN 573-4	Sheet, Flat, Strip
	-30.0 °C	71.4 GPa	H1x	DIN 1712-3, EN 573-3, EN 573-4	Sheet, Flat, Strip
	20.0 °C	60.0 - 70.0 GPa	H1x	DIN 1712-3, EN 573-3, EN 573-4	Sheet, Flat, Strip
	20.0 °C	70.0 GPa	H1x	DIN 1712-3, EN 573-3, EN 573-4	Sheet, Flat, Strip
	100.0 °C	68.6 GPa	H1x	DIN 1712-3, EN 573-3, EN 573-4	Sheet, Flat, Strip
	150.0 °C	66.5 GPa	H1x	DIN 1712-3, EN 573-3, EN 573-4	Sheet, Flat, Strip
	200.0 °C	63.0 GPa	H1x	DIN 1712-3, EN 573-3, EN 573-4	Sheet, Flat, Strip
	250.0 °C	56.0 GPa	H1x	DIN 1712-3, EN 573-3, EN 573-4	Sheet, Flat, Strip
Elongation	20.0 °C	1.0 %	H1x	DIN 1712-3, EN 573-3, EN 573-4	Flat	A100
	20.0 °C	2.0 %	H1x	DIN 1712-3, EN 573-3, EN 573-4	Sheet, Flat, Strip	A10
	20.0 °C	3.0 %	H1x	DIN 1712-3, EN 573-3, EN 573-4	Sheet, Strip
Hardness, Brinell	20.0 °C	45.0 [-]	H1x	DIN 1712-3, EN 573-3, EN 573-4	Sheet, Strip
Plane-Strain Fracture Toughnes		22.0 - 35.0 MPa·√m				Typical for Wrought 1000 Series Aluminium
Poisson's ratio		0.33 [-]				Typical for Wrought 1000 Series Aluminium
Shear modulus	20.0 °C	25.0 - 26.5 GPa	H1x	DIN 1712-3, EN 573-3, EN 573-4	Sheet, Flat, Strip
Tensile strength	20.0 °C	150.0 MPa	H1x	DIN 1712-3, EN 573-3, EN 573-4	Sheet, Strip
	20.0 °C	150.0 - 190.0 MPa	H1x	DIN 1712-3, EN 573-3, EN 573-4	Flat

Thermal

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Coefficient of thermal expansion	-50.0 °C	2.17e-05 1/K	H1x	DIN 1712-3, EN 573-3, EN 573-4	Sheet, Flat, Strip
	100.0 °C	2.35e-05 1/K	H1x	DIN 1712-3, EN 573-3, EN 573-4	Sheet, Flat, Strip
	200.0 °C	2.44e-05 1/K	H1x	DIN 1712-3, EN 573-3, EN 573-4	Sheet, Flat, Strip
	300.0 °C	2.54e-05 1/K	H1x	DIN 1712-3, EN 573-3, EN 573-4	Sheet, Flat, Strip
Melting point		645.0 - 660.0 °C				Typical for Wrought 1000 Series Aluminium
Specific heat capacity	20.0 °C	900.0 J/(kg·K)	H1x	DIN 1712-3, EN 573-3, EN 573-4	Sheet, Flat, Strip
Thermal conductivity	20.0 °C	210.0 - 220.0 W/(m·K)	H1x	DIN 1712-3, EN 573-3, EN 573-4	Sheet, Flat, Strip

Electrical

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Electrical conductivity	20.0 °C	34800000.0 - 36000000.0 S/m	H1x	DIN 1712-3, EN 573-3, EN 573-4	Sheet, Flat, Strip
Electrical resistivity		2.7e-08 - 3e-08 Ω·m				Typical for Wrought 1000 Series Aluminium

Chemical properties

Property	Value	Condition	Related Standards	Shape
Copper	0.05	H1x	DIN 1712-3, EN 573-3, EN 573-4	Sheet, Flat, Strip
Iron	0.4	H1x	DIN 1712-3, EN 573-3, EN 573-4	Sheet, Flat, Strip
Magnesium	0.05	H1x	DIN 1712-3, EN 573-3, EN 573-4	Sheet, Flat, Strip
Manganese	0.05	H1x	DIN 1712-3, EN 573-3, EN 573-4	Sheet, Flat, Strip
Silicon	0.25	H1x	DIN 1712-3, EN 573-3, EN 573-4	Sheet, Flat, Strip
Titanium	0.05	H1x	DIN 1712-3, EN 573-3, EN 573-4	Sheet, Flat, Strip
Zinc	0.07	H1x	DIN 1712-3, EN 573-3, EN 573-4	Sheet, Flat, Strip

Technological properties

Property
Brazing	Excellent
Workability	Excellent workability.

Property

Brazing

Excellent

Workability

Excellent workability.