DIN 1725-1 Grade 3.0525 H1x: Premium Aluminum Alloy for Superior Strength & Durability

The alloy AlMn1Mg0,5 is similarly to AlMn1 in its properties. It reaches strength up to F 25. The alloy belongs to the nature-hard aluminum materials. A strength increase can only occure by cold forming. It is very well hot and cold formable and is suitable to the deep-drawing (no lappet formation). The alloy AlMn1Mg0,5 is very well corrosion resistant and is sea water steady. As semi-finished material it is present in accordance with DIN 1788 and DIN 1745 only as sheet metal or strip. Application: Mainly in the packing for cans (lower parts), for menu bowls, for covers. In the building industry for claddings, roofings, for sun protection facilities (roller schutter, lamella net curtain) and for roll gates as well as for flexible pipes and in the construction of vehicles.

Quantity: One truck load – Specialty products on request.Additional services: Via Cindal (the Aludium R&D department): R&D services, benchmarking, chemical audits, material specification, process optimisation, quality monitoring, sample analysis, prototyping, training

Properties

General

Property	Temperature	Value	Condition	Related Standards	Shape
Density	20.0 °C	2.72 g/cm³	H1x	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Flat, Strip

Mechanical

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Elastic modulus	20.0 °C	65.0	H1x	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Flat, Strip
Elongation	20.0 °C	1.0 %	H1x	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Flat, Strip	A10
	20.0 °C	1.0 %	H1x	DIN 1725-1, EN 573-3, EN 573-4	Flat	A100
	20.0 °C	2.0 %	H1x	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Strip
Hardness, Brinell	20.0 °C	80.0 [-]	H1x	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Strip
Plane-Strain Fracture Toughnes		22.0 - 35.0 MPa·√m				Typical for Wrought 3000 Series Aluminium
Poisson's ratio		0.33 [-]				Typical for Wrought 3000 Series Aluminium
Shear modulus	20.0 °C	26.5	H1x	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Flat, Strip
Tensile strength	20.0 °C	235.0 MPa	H1x	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Strip
	20.0 °C	245.0 MPa	H1x	DIN 1725-1, EN 573-3, EN 573-4	Flat

Thermal

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Coefficient of thermal expansion		2.2e-05 - 2.4e-05 1/K				Typical for Wrought 3000 Series Aluminium
Melting point		629.0 - 654.0 °C				Typical for Wrought 3000 Series Aluminium
Specific heat capacity	20.0 °C	893.0 J/(kg·K)	H1x	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Flat, Strip
Thermal conductivity	20.0 °C	200.0	H1x	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Flat, Strip

Electrical

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Electrical conductivity	20.0 °C	28000000.0	H1x	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Flat, Strip
Electrical resistivity		3.4e-08 - 4.2e-08 Ω·m				Typical for Wrought 3000 Series Aluminium

Chemical properties

Property	Value	Condition	Related Standards	Shape
Chromium	0.1	H1x	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Flat, Strip
Copper	0.3	H1x	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Flat, Strip
Iron	0.7	H1x	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Flat, Strip
Magnesium	0.2 - 0.6 %	H1x	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Flat, Strip
Manganese	1.0 - 1.5 %	H1x	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Flat, Strip
Silicon	0.6	H1x	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Flat, Strip
Titanium	0.1	H1x	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Flat, Strip
Zinc	0.25	H1x	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Flat, Strip

Technological properties

Property
Workability	Good workability.

Property

Workability

Good workability.