DIN 1712-3 Grade 3.0275 H18: High-Performance Aluminium for Engineering Applications
Pure aluminium This material is well anodically oxidizable, and possesses a good electrical and thermal conductivity. The splinter-giving workability is bad because of danger of smearing. Its mechanical strength is low, the plasticity high. The forming capacity and the chemical as well as the weather proofness are excellent. The material is well suitable for welding and braze welding. Application: Apparatus engineering, roll bond, z-bond, household devices, camp and transportation containers for the chemical, pharmaceutical and food industry, roofing, linings, arts and crafts, packing, flow pressed parts (tubes, tube, doses, bottles), pressure tanks according to AD-W 6/1
Quantity: One truck load – Specialty products on request.Additional services: Via Cindal (the Aludium R&D department): R&D services, benchmarking, chemical audits, material specification, process optimisation, quality monitoring, sample analysis, prototyping, trainingProperties
General
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Density | 2.7 g/cm³ | H18 | EN 573-3, EN 1301, EN 485 | ||
20.0 °C | 2.7 g/cm³ | H18 | DIN 1712-3, EN 573-3, EN 573-4 | Sheet, Strip |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Bending angle 90° | 1.0 °/t | H18 | EN 573-3, EN 485 | |||
2.0 °/t | H18 | EN 573-3, EN 485 | ||||
2.5 °/t | H18 | EN 573-3, EN 485 | ||||
Elastic modulus | 70.0 GPa | H18 | EN 573-3, EN 1301, EN 485 | |||
20.0 °C | 60.0 - 70.0 GPa | H18 | DIN 1712-3, EN 573-3, EN 573-4 | Sheet, Strip | ||
Elongation | 2.0 % | H18 | EN 573-3, EN 485 | A50 | ||
3.0 % | H18 | EN 573-3, EN 1301 | ||||
20.0 °C | 3.0 % | H18 | DIN 1712-3, EN 573-3, EN 573-4 | Sheet, Strip | A10 | |
20.0 °C | 4.0 % | H18 | DIN 1712-3, EN 573-3, EN 573-4 | Sheet, Strip | ||
Hardness, Brinell | 40.0 [-] | H18 | EN 573-3, EN 485 | |||
20.0 °C | 36.0 [-] | H18 | DIN 1712-3, EN 573-3, EN 573-4 | Sheet, Strip | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 1000 Series Aluminium | ||||
Poisson's ratio | 0.33 [-] | Typical for Wrought 1000 Series Aluminium | ||||
Shear modulus | 20.0 °C | 25.0 - 26.5 GPa | H18 | DIN 1712-3, EN 573-3, EN 573-4 | Sheet, Strip | |
Tensile strength | 125.0 MPa | H18 | EN 573-3, EN 1301, EN 485 | |||
20.0 °C | 120.0 - 160.0 MPa | H18 | DIN 1712-3, EN 573-3, EN 573-4 | Sheet, Strip |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.35e-05 1/K | H18 | EN 573-3, EN 1301, EN 485 | |
100 °C | 2.35e-05 1/K | H18 | EN 573-3, EN 1301, EN 485 | ||
Melting point | 659.0 °C | H18 | EN 573-3, EN 1301, EN 485 | ||
Specific heat capacity | 20.0 °C | 921.0 J/(kg·K) | H18 | DIN 1712-3, EN 573-3, EN 573-4 | Sheet, Strip |
Thermal conductivity | 225 W/(m·K) | H18 | EN 573-3, EN 1301, EN 485 | ||
20.0 °C | 215.0 W/(m·K) | H18 | DIN 1712-3, EN 573-3, EN 573-4 | Sheet, Strip |
Electrical
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Electrical conductivity | 34500000.0 - 35000000.0 S/m | H18 | EN 573-3, EN 1301, EN 485 | ||
20.0 °C | 35800000.0 - 36800000.0 S/m | H18 | DIN 1712-3, EN 573-3, EN 573-4 | Sheet, Strip | |
Electrical resistivity | 2.86e-08 - 2.9e-08 Ω·m | H18 | EN 573-3, EN 1301, EN 485 |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Aluminium | 99.7 % | H18 | EN 573-3, EN 1301, EN 485 | |
Copper | 0.03 % | H18 | DIN 1712-3, EN 573-3, EN 573-4, EN 1301, EN 485 | Sheet, Strip |
Iron | 0.25 % | H18 | DIN 1712-3, EN 573-3, EN 573-4 | Sheet, Strip |
0.25 % | H18 | EN 573-3, EN 1301, EN 485 | ||
Magnesium | 0.03 % | H18 | DIN 1712-3, EN 573-3, EN 573-4, EN 1301, EN 485 | Sheet, Strip |
Manganese | 0.03 % | H18 | DIN 1712-3, EN 573-3, EN 573-4, EN 1301, EN 485 | Sheet, Strip |
Silicon | 0.2 % | H18 | DIN 1712-3, EN 573-3, EN 573-4, EN 1301, EN 485 | Sheet, Strip |
Titanium | 0.03 % | H18 | DIN 1712-3, EN 573-3, EN 573-4, EN 1301, EN 485 | Sheet, Strip |
Zinc | 0.07 % | H18 | DIN 1712-3, EN 573-3, EN 573-4, EN 1301, EN 485 | Sheet, Strip |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | decorative: very good, Protective: very good | |
| Brazing | hard brazing (with flux/ without flux): very good / very good, friction soldering: very good, soft brazing with flux: very good | |
| Workability | Bending / Spinning (cold): very good / very good, Impact extrusion (cold): very good, Deep drawing / upsetting (Condition) very good (H14) / very good (H12) | |
Metal
- DIN 1712-3 Grade 3.0305 H14 – Premium Aluminium for Electrical and Mechanical Applications
- DIN 1712-3 Grade 3.0385 O – Premium Pure Aluminium for High Conductivity
- DIN 1712-3 Grade 3.0255 H1x Aluminum Alloy – High Conductivity & Corrosion Resistance
- DIN 1712-3 Grade 3.0285 F – Premium Pure Aluminium for High Conductivity & Anodization
- DIN 1712-3 Grade 3.0385 H18 – Ultra-Pure Aluminum for High-Conductivity Applications
- DIN 1712-3 Grade 3.0275 H14 – Premium Anodizable Aluminium for Industrial Applications
- DIN 1712-3 Grade 3.0255 F Aluminium Alloy – High Conductivity & Excellent Corrosion Resistance
- DIN 1712-3 Grade 3.0205 F: High-Performance Aluminium Alloy for Engineering Applications
- DIN 1712-3 Grade 3.0285 H18 – Premium Aluminum Alloy for Industrial Use
- DIN 1712-3 Grade 3.0285 H22 – Premium Anodizable Aluminium for Engineering