DIN 1725‑1 Grade 3.0515 H16 – High‑Strength, Corrosion‑Resistant Al‑Mn Alloy

The alloy AlMn1 is an Al-Mn alloy, which belongs to the nature-hard aluminum materials. Mn increases the strength compared with pure aluminium, but it does not impair the corrosion resistance. The alloy belongs to the nature-hard aluminum materials. A strength increase can only occur by cold forming. It is very well formable, very well corrosion resistant and weldable. In these characteristics it resembles the pure aluminium, but with the attainable strength it exceeds this. The alloy AlMn1 has a increased heat resistance compared with pure aluminium, as result of the of the Mn-additive (inhibits recrystallisation). Application: In the building industry for roofings, as outer skin of buildings, in the apparatus and tank construction as heat exchanger (bank of tubes, profiles, gilled pipes, sheet metals), for radiators, air conditioning systems, pipings for compressed gas tanks, for tanks according VdTUEV Werkstoffblaetter, as antennas for radio relay link and satellite communication (mirror) for technical flow pressed parts, for solid rivets, for generally metal-describe, in food industry (including commercial devices), in the construction of vehicles (including tank cars) and as packing (sheet metal packings generally).

Properties

General

Property	Temperature	Value	Condition	Related Standards	Shape
Density		2.73 g/cm³	H16	EN 573-3, EN 1592, EN 485, EN 683, EN 754
	20.0 °C	2.73 g/cm³	H16	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4	Rod, Tube

Mechanical

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Bending angle 180°		2.0 °/t	H16	EN 573-3, EN 485
		2.5 °/t	H16	EN 573-3, EN 485
Bending angle 90°		1.0 °/t	H16	EN 573-3, EN 485
		1.5 °/t	H16	EN 573-3, EN 485
		2.0 °/t	H16	EN 573-3, EN 485
Elastic modulus		69.5 GPa	H16	EN 573-3, EN 1592, EN 485, EN 683, EN 754
	20.0 °C	60.0 - 65.0 GPa	H16	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4	Rod, Tube
Elongation		1.0 %	H16	EN 573-3, EN 485, EN 683		A50
		2.0 %	H16	EN 573-3, EN 485		A50
		3.0 %	H16	EN 573-3, EN 1592		A100
		3.0 %	H16	EN 573-3, EN 754		A50
		4.0 %	H16	EN 573-3, EN 754		A100
	20.0 °C	3.0 %	H16	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4	Rod, Tube	A10
	20.0 °C	4.0 %	H16	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4	Rod, Tube
Hardness, Brinell		51.0 [-]	H16	EN 573-3, EN 485
	20.0 °C	40.0 [-]	H16	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4	Tube
	20.0 °C	45.0 [-]	H16	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4	Rod
Plane-Strain Fracture Toughnes		22.0 - 35.0 MPa·√m				Typical for Wrought 3000 Series Aluminium
Poisson's ratio		0.33 [-]				Typical for Wrought 3000 Series Aluminium
Shear modulus		26.1 GPa	H16	EN 573-3, EN 1592, EN 485, EN 683, EN 754
	20.0 °C	24.0 - 26.5 GPa	H16	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4	Rod, Tube
Tensile strength		150.0 - 200.0 MPa	H16	EN 573-3, EN 683
		160.0 - 200.0 MPa	H16	EN 573-3, EN 485, EN 683
		160.0 - 195.0 MPa	H16	EN 573-3, EN 754
		170.0 MPa	H16	EN 573-3, EN 1592
	20.0 °C	160.0 MPa	H16	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4	Rod, Tube

Thermal

Property	Temperature	Value	Condition	Related Standards	Shape
Coefficient of thermal expansion	20 °C	2.35e-05 1/K	H16	EN 573-3, EN 1592, EN 485, EN 683, EN 754
	100 °C	2.35e-05 1/K	H16	EN 573-3, EN 1592, EN 485, EN 683, EN 754
Melting point		645.0 - 655.0 °C	H16	EN 573-3, EN 1592, EN 485, EN 683, EN 754
Specific heat capacity		893.0 J/(kg·K)	H16	EN 573-3, EN 1592, EN 485, EN 683, EN 754
	20.0 °C	893.0 J/(kg·K)	H16	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4	Rod, Tube
Thermal conductivity	20.0 °C	160.0 - 200.0 W/(m·K)	H16	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4, EN 1592, EN 485, EN 683, EN 754	Rod, Tube

Electrical

Property	Temperature	Value	Condition	Related Standards	Shape
Electrical conductivity	20.0 °C	22000000.0 - 28000000.0 S/m	H16	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4, EN 1592, EN 485, EN 683, EN 754	Rod, Tube
Electrical resistivity		3.57e-08 - 4.55e-08 Ω·m	H16	EN 573-3, EN 1592, EN 485, EN 683, EN 754

Chemical properties

Property	Value	Condition	Related Standards	Shape
Chromium	0.1 %	H16	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4, EN 1592, EN 485, EN 683, EN 754	Rod, Tube
Copper	0.1 %	H16	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4, EN 1592, EN 485, EN 683, EN 754	Rod, Tube
Iron	0.7 %	H16	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4	Rod, Tube
	0.70 %	H16	EN 573-3, EN 1592, EN 485, EN 683, EN 754
Magnesium	0.3 %	H16	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4, EN 1592, EN 485, EN 683, EN 754	Rod, Tube
Manganese	0.9 - 1.5 %	H16	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4, EN 1592, EN 485, EN 683, EN 754	Rod, Tube
Silicon	0.5 %	H16	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4, EN 1592, EN 485, EN 683, EN 754	Rod, Tube
Titanium	0.1	H16	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4	Rod, Tube
Zinc	0.2 %	H16	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4, EN 1592, EN 485, EN 683, EN 754	Rod, Tube

Technological properties

Property
Workability	Good workability.

Property

Workability

Good workability.