3005 H25 Aluminum Alloy – Low‑Medium Strength, Corrosion‑Resistant Wrought Grade
A low to medium strength alloy with moderate corrosion resistance.
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 23.0 °C | 2.72 g/cm³ |
Dimension
| Property | Value |
|---|---|
Thickness | 0.18 - 0.3 mm |
Mechanical
| Property | Temperature | Value |
|---|---|---|
Elastic modulus | 23.0 °C | 69 GPa |
Elongation A50 | 23.0 °C | 2 % |
Shear modulus | 23.0 °C | 26 GPa |
Tensile strength | 23.0 °C | 180 - 250 MPa |
Yield strength | 23.0 °C | 160 - 230 MPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 100.0 °C | 2.4E-5 1/K | 20-100°C |
Thermal conductivity | 23.0 °C | 172 W/(m·K) |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical resistivity | 23.0 °C | 3.8E-8 Ω·m |
Chemical properties
| Property | Value |
|---|---|
Chromium | 0.1 % |
Copper | 0.3 % |
Iron | 0.7 % |
Magnesium | 0.2 - 0.6 % |
Manganese | 1 - 1.5 % |
Silicon | 0.6 % |
Zinc | 0.25 % |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | Good | |
| Application areas | Facades: Single sheet, Sheets for composites/ sandwich Panels, Sheets for mechanized panels; Roofing: Single sheet, Sheets for composites/ sandwich Panels; Doors: Sheets for composites/ sandwich Panels, Sheets for mechanized panels; Sun Protection Systems: Single sheet (covering, sun breakers and gutters); Interiors and ceilings: Single sheet, Sheets for composites/ sandwich Panels, Sheets for mechanized panels, Decoration; Electronic devices: Housing of devices; Insulation; Cosmetics: Cosmetics pieces | |
| Brazing | Good | |
| Corrosion properties | Good | |
| Welding | Good | |
| Workability | Good | |
Metal
- 5252-O: High-Purity, Non-Heat-Treatable Aluminum Wrought Alloy for Superior Brightening and Anodizing
- 1350 H19 Non-Heat-Treatable Al Wrought Alloy – High Conductivity & Mechanical Strength
- 8011A O – Non‑Heat Treatable Aluminum Wrought Alloy: Key Properties & Applications
- 8014 H21 – High-Strength Non-Heat-Treatable Aluminum Wrought Alloy
- 1200O Aluminum Wrought Alloy – Superior Corrosion Resistance & Workability
- 3105A H28 Non-Heat-Treatable Aluminum Alloy – Low‑to‑Medium Strength, Superior Corrosion Resistance
- 3005 H28 Aluminium Wrought Alloy – Non-Heat Treatable, Low to Medium Strength
- 5251 O: High-Strength, Formable Non-Heat-Treatable Aluminum Wrought Alloy
- 3005 O Aluminum Wrought Alloy – Non‑Heat Treated, Medium Strength & Corrosion Resistant
- 3103-O: High-Strength, Non-Heat-Treatable Aluminum Alloy for Structural Applications