AW-5042 H111 Aluminium Alloy – EN 573‑3 Certified for Food Safety
Naturally hard AlMg alloy. The alloy is food safe.
Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.67 g/cm³ | H111 | EN 573-3, EN 485 |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Bending angle 180° | 1.5 °/t | H111 | EN 573-3, EN 485 | |||
2.0 °/t | H111 | EN 573-3, EN 485 | ||||
Elastic modulus | 69.0 - 70.0 GPa | Typical for Wrought 5000 Series Aluminium | ||||
Elongation | 18.0 % | H111 | EN 573-3, EN 485 | |||
18.0 % | H111 | EN 573-3, EN 485 | A50 | |||
20.0 °C | 18.0 % | H111 | EN 573-3 | Flat | A50 Transverse | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||||
Poisson's ratio | 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||||
Shear modulus | 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | ||||
Tensile strength | 240.0 - 350.0 MPa | H111 | EN 573-3, EN 485 | |||
20.0 °C | 240.0 - 350.0 MPa | H111 | EN 573-3 | Flat | Transverse |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 2.2e-05 - 2.5e-05 1/K | Typical for Wrought 5000 Series Aluminium |
Max service temperature | 150.0 °C | Typical for Wrought 5000 Series Aluminium |
Melting point | 560.0 - 655.0 °C | Typical for Wrought 5000 Series Aluminium |
Specific heat capacity | 879.0 - 963.0 J/(kg·K) | Typical for Wrought 5000 Series Aluminium |
Thermal conductivity | 112.0 - 205.0 W/(m·K) | Typical for Wrought 5000 Series Aluminium |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 18000000.0 - 31000000.0 S/m | Typical for Wrought 5000 Series Aluminium |
Electrical resistivity | 3.3e-08 - 5e-08 Ω·m | Typical for Wrought 5000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Chromium | 0.1 % | H111 | EN 573-3, EN 485 | Flat |
Copper | 0.15 % | H111 | EN 573-3, EN 485 | Flat |
Iron | 0.35 % | H111 | EN 573-3 | Flat |
0.35 % | H111 | EN 573-3, EN 485 | ||
Magnesium | 3.0 - 4.0 % | H111 | EN 573-3, EN 485 | Flat |
Manganese | 0.2 - 0.5 % | H111 | EN 573-3, EN 485 | Flat |
Silicon | 0.2 % | H111 | EN 573-3, EN 485 | Flat |
Titanium | 0.1 | H111 | EN 573-3 | Flat |
Zinc | 0.25 % | H111 | EN 573-3, EN 485 | Flat |
Technological properties
| Property | ||
|---|---|---|
| Workability | Good workability. | |
Metal
- EN 573-3 Grade 3.0915 (H111) – Premium Aluminium Alloy
- EN 573-3 Grade 3.3326 H111 – Detailed Mechanical Properties of 5000 Series Aluminium
- EN 573-3 Grade 3.0505 H111 Aluminium Alloy - Technical Specifications
- AW‑5186 H111 Aluminium Alloy – EN 573‑3 Certified for High‑Performance Applications
- EN 573-3 Grade 3.0257 H111 Aluminium Alloy Specifications
- EN 573-3 Grade 3.3549 H111 Aluminium Alloy – Technical Specifications and R&D Services
- EN 573-3 Grade 3.1325 H111 – Aluminium Alloy Properties & Standards
- EN 573-3 Grade 3.2315 H111 – Detailed Aluminium Alloy Specifications
- EN 573-3 Grade 3.0515 H111 Steel – Comprehensive Properties & Compliance
- EN 573-3 Grade 3.0525 H111 – High-Quality Aluminum Alloy for Industrial Applications