DIN 1725-1 Grade 3.3315 H24: High-Performance AlMg Alloy for Corrosion-Resistant Applications

The AlMg alloy is characterised all by a good corrosion resistance. It is sea water steady and resistant to saline atmosphere. The Mg content increase the strength, the cold forming capacity decreases with it. The alloys of this type are nature hard, i.e. only by a cold forming and not by a purposeful heat treatment a strength increase can be attained. The material is well polishabel and anodisable. The splinter-giving machinability becomes better with increasing Mg content just like the weldability. The alloy AlMg1 reaches strength grades to F 22. Application: Their main field of application is the building industry. In the building industry for claddings, roofing and trim, for transport containers. For metal goods, like building fittings, table-ware, flow pressed parts, reflectors. In food industry, for furniture (incl. camping furniture) as well as for describe and for covers with composite slabs (intermediate layer: Polyethylene).

Properties

General

Property	Temperature	Value	Condition	Related Standards	Shape
Density		2.69 g/cm³	H24	EN 573-3, EN 485
	20.0 °C	2.69 g/cm³	H24	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Strip

Mechanical

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Bending angle 180°		1.5 °/t	H24	EN 573-3, EN 485
		2.0 °/t	H24	EN 573-3, EN 485
Bending angle 90°		0.5 °/t	H24	EN 573-3, EN 485
		1.0 °/t	H24	EN 573-3, EN 485
		2.0 °/t	H24	EN 573-3, EN 485
		2.5 °/t	H24	EN 573-3, EN 485
Elastic modulus		69.5 GPa	H24	EN 573-3, EN 485
	20.0 °C	60.0 - 65.0 GPa	H24	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Strip
Elongation		3.0 %	H24	EN 573-3, EN 485		A50
		4.0 %	H24	EN 573-3, EN 485		A50
		5.0 %	H24	EN 573-3, EN 485		A50
		6.0 %	H24	EN 573-3, EN 485		A50
		8.0 %	H24	EN 573-3, EN 485		A50
	20.0 °C	6.0 %	H24	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Strip	A10
	20.0 °C	8.0 %	H24	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Strip
Hardness, Brinell		47.0 [-]	H24	EN 573-3, EN 485
	20.0 °C	47.0 [-]	H24	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Strip
Plane-Strain Fracture Toughnes		22.0 - 35.0 MPa·√m				Typical for Wrought 5000 Series Aluminium
Poisson's ratio		0.33 [-]				Typical for Wrought 5000 Series Aluminium
Shear modulus		26.1 GPa	H24	EN 573-3, EN 485
	20.0 °C	25.0 GPa	H24	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Strip
Tensile strength	20.0 °C	145.0 - 185.0 MPa	H24	DIN 1725-1, EN 573-3, EN 573-4, EN 485	Sheet, Strip

Thermal

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Coefficient of thermal expansion	-50 °C	2.18e-05 1/K	H24	EN 573-3, EN 485, DIN 1725-1, EN 573-4	Sheet, Strip
	-50.0 °C	2.18e-05 1/K	H24	EN 573-3, EN 485, DIN 1725-1, EN 573-4	Sheet, Strip
	20 °C	2.18e-05 1/K	H24	EN 573-3, EN 485, DIN 1725-1, EN 573-4	Sheet, Strip
	20 °C	2.36e-05 1/K	H24	EN 573-3, EN 485, DIN 1725-1, EN 573-4	Sheet, Strip
	20 °C	2.45e-05 1/K	H24	EN 573-3, EN 485, DIN 1725-1, EN 573-4	Sheet, Strip
	20 °C	2.55e-05 1/K	H24	EN 573-3, EN 485, DIN 1725-1, EN 573-4	Sheet, Strip
	100 °C	2.36e-05 1/K	H24	EN 573-3, EN 485, DIN 1725-1, EN 573-4	Sheet, Strip
	100.0 °C	2.36e-05 1/K	H24	EN 573-3, EN 485, DIN 1725-1, EN 573-4	Sheet, Strip
	200 °C	2.45e-05 1/K	H24	EN 573-3, EN 485, DIN 1725-1, EN 573-4	Sheet, Strip
	200.0 °C	2.45e-05 1/K	H24	EN 573-3, EN 485, DIN 1725-1, EN 573-4	Sheet, Strip
	300 °C	2.55e-05 1/K	H24	EN 573-3, EN 485, DIN 1725-1, EN 573-4	Sheet, Strip
	300.0 °C	2.55e-05 1/K	H24	EN 573-3, EN 485, DIN 1725-1, EN 573-4	Sheet, Strip
Max service temperature		150.0 °C				Typical for Wrought 5000 Series Aluminium
Melting point		630.0 - 650.0 °C	H24	EN 573-3, EN 485
Specific heat capacity	20.0 °C	879.0 J/(kg·K)	H24	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Strip
Thermal conductivity	20.0 °C	160.0 - 220.0 W/(m·K)	H24	DIN 1725-1, EN 573-3, EN 573-4, EN 485	Sheet, Strip

Electrical

Property	Temperature	Value	Condition	Related Standards	Shape
Electrical conductivity	20.0 °C	23000000.0 - 31000000.0 S/m	H24	DIN 1725-1, EN 573-3, EN 573-4, EN 485	Sheet, Strip
Electrical resistivity		3.23e-08 - 4.35e-08 Ω·m	H24	EN 573-3, EN 485

Chemical properties

Property	Value	Condition	Related Standards	Shape
Chromium	0.1 %	H24	DIN 1725-1, EN 573-3, EN 573-4, EN 485	Sheet, Strip
Copper	0.05 %	H24	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Strip
	0.2 %	H24	EN 573-3, EN 485
Iron	0.45 %	H24	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Strip
	0.70 %	H24	EN 573-3, EN 485
Magnesium	0.7 - 1.1 %	H24	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Strip
	1.1 - 1.8 %	H24	EN 573-3, EN 485
Manganese	0.15 %	H24	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Strip
	0.3 %	H24	EN 573-3, EN 485
Silicon	0.3 %	H24	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Strip
	0.4 %	H24	EN 573-3, EN 485
Zinc	0.2 %	H24	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Strip
	0.25 %	H24	EN 573-3, EN 485

Technological properties

Property
Workability	Good workability.

Property

Workability

Good workability.