EN 573-3 AW‑6082 H111: Food‑Safe, Age‑Hardening Aluminum Alloy
Age-hardenable AlMgSi alloy. The alloy is food safe.
Properties
General
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Density | 2.7 g/cm³ | H111 | EN 573-3, EN 754, EN 755 | Strip, Sheet, Plate, Wire, Forging, Tube, Bar | |
20.0 °C | 2.7 g/cm³ | H111 | EN 573-3 | Profile, Rod, Tube |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Elastic modulus | 70.0 GPa | H111 | EN 573-3, EN 754, EN 755 | Strip, Sheet, Plate, Wire, Forging, Tube, Bar | ||
20.0 °C | 68.0 - 73.0 GPa | H111 | EN 573-3 | Profile, Rod, Tube | ||
Elongation | 12.0 % | H111 | EN 573-3, EN 755 | Strip, Sheet, Plate, Wire, Forging, Tube, Bar | A50 | |
13.0 % | H111 | EN 573-3, EN 754 | Strip, Sheet, Plate, Wire, Forging, Tube, Bar | A50 | ||
14.0 % | H111 | EN 573-3, EN 755 | Strip, Sheet, Plate, Wire, Forging, Tube, Bar | A100 | ||
15.0 % | H111 | EN 573-3, EN 754 | Strip, Sheet, Plate, Wire, Forging, Tube, Bar | A100 | ||
20.0 °C | 12.0 % | H111 | EN 573-3 | Profile, Rod, Tube | A50 | |
20.0 °C | 13.0 % | H111 | EN 573-3 | Rod, Tube | A50 | |
20.0 °C | 14.0 % | H111 | EN 573-3 | Profile, Rod, Tube | ||
20.0 °C | 15.0 % | H111 | EN 573-3 | Rod, Tube | ||
Hardness, Brinell | 20.0 °C | 35.0 [-] | H111 | EN 573-3 | Profile, Rod, Tube | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 6000 Series Aluminium | ||||
Poisson's ratio | 0.33 [-] | Typical for Wrought 6000 Series Aluminium | ||||
Shear modulus | 26.4 GPa | H111 | EN 573-3, EN 754, EN 755 | Strip, Sheet, Plate, Wire, Forging, Tube, Bar | ||
20.0 °C | 26.0 - 27.0 GPa | H111 | EN 573-3 | Profile, Rod, Tube | ||
Tensile strength | 160.0 | H111 | EN 573-3, EN 754, EN 755 | Strip, Sheet, Plate, Wire, Forging, Tube, Bar | ||
20.0 °C | 160.0 | H111 | EN 573-3 | Profile, Rod, Tube |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.3399999999999996e-05 1/K | H111 | EN 573-3, EN 754, EN 755 | Strip, Sheet, Plate, Wire, Forging, Tube, Bar |
100 °C | 2.3399999999999996e-05 1/K | H111 | EN 573-3, EN 754, EN 755 | Strip, Sheet, Plate, Wire, Forging, Tube, Bar | |
Melting point | 585.0 - 650.0 °C | H111 | EN 573-3, EN 754, EN 755 | Strip, Sheet, Plate, Wire, Forging, Tube, Bar | |
Specific heat capacity | 896.0 J/(kg·K) | H111 | EN 573-3, EN 754, EN 755 | Strip, Sheet, Plate, Wire, Forging, Tube, Bar | |
Thermal conductivity | 20.0 °C | 170.0 - 220.0 W/(m·K) | H111 | EN 573-3, EN 754, EN 755 | Profile, Rod, Tube, Strip, Sheet, Plate, Wire, Forging, Bar |
Electrical
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Electrical conductivity | 20.0 °C | 24000000.0 - 32000000.0 S/m | H111 | EN 573-3, EN 754, EN 755 | Profile, Rod, Tube, Strip, Sheet, Plate, Wire, Forging, Bar |
Electrical resistivity | 3.13e-08 - 4.17e-08 Ω·m | H111 | EN 573-3, EN 754, EN 755 | Strip, Sheet, Plate, Wire, Forging, Tube, Bar |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Chromium | 0.25 % | H111 | EN 573-3, EN 754, EN 755 | Profile, Rod, Tube, Strip, Sheet, Plate, Wire, Forging, Bar |
Copper | 0.1 % | H111 | EN 573-3, EN 754, EN 755 | Profile, Rod, Tube, Strip, Sheet, Plate, Wire, Forging, Bar |
Iron | 0.5 % | H111 | EN 573-3 | Profile, Rod, Tube |
0.50 % | H111 | EN 573-3, EN 754, EN 755 | Strip, Sheet, Plate, Wire, Forging, Tube, Bar | |
Magnesium | 0.6 - 1.2 % | H111 | EN 573-3, EN 754, EN 755 | Profile, Rod, Tube, Strip, Sheet, Plate, Wire, Forging, Bar |
Manganese | 0.4 - 1.0 % | H111 | EN 573-3, EN 754, EN 755 | Profile, Rod, Tube, Strip, Sheet, Plate, Wire, Forging, Bar |
Silicon | 0.7 - 1.3 % | H111 | EN 573-3, EN 754, EN 755 | Profile, Rod, Tube, Strip, Sheet, Plate, Wire, Forging, Bar |
Titanium | 0.1 % | H111 | EN 573-3, EN 754, EN 755 | Profile, Rod, Tube, Strip, Sheet, Plate, Wire, Forging, Bar |
Zinc | 0.2 % | H111 | EN 573-3, EN 754, EN 755 | Profile, Rod, Tube, Strip, Sheet, Plate, Wire, Forging, Bar |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | decorative: acceptable, Protective: very good | |
| Brazing | hard brazing (with flux/ without flux): good / sufficient, friction soldering: good, soft brazing with flux: acceptable | |
| Corrosion properties | Seawater: good, weathering: very good | |
| Workability | Bending / Spinning (cold): acceptable (T3, T4) / good (O), Impact extrusion (cold): good (O), Deep drawing / upsetting (Condition) good (O) / good (O) | |
Metal
- AW-6082 T39 Aluminium Alloy – Grade EN 573‑3 for Food‑Safe Applications
- EN 573-3 AW-6082 T89 Aluminum Alloy – Food‑Safe, Age‑Hardenable, High Strength
- EN 573-3 AW-6082 H13: Premium Age‑Hardenable AlMgSi Alloy for Food‑Safe Applications
- AW-6082 H18 Aluminum Alloy – EN 573-3 Certified, Food‑Safe, High‑Strength Age‑Hardenable
- EN 573-3 Grade AW-2014 H111: High-Strength Precipitation-Hardening Aluminum Alloy
- AW-5026 H111 Aluminium Alloy – EN 573‑3 Certified Food‑Safe Grade
- EN 573-3 AW‑5010 H111 Aluminium‑Magnesium Alloy – Technical Specifications & Properties
- AW-5088 H111: Premium EN 573-3 Aluminium Alloy for High-Performance Applications
- AW-6082 T5 Aluminum Alloy – EN 573-3 Certified Grade
- AW-5070 H111 Aluminum Alloy – EN 573-3 Certified Grade