EN 573-3 Grade 3.3545 H111 Aluminum Alloy – High Strength & Corrosion Resistance
Aluminum DIN 3.3545 is structural alloy, which offers users strong corrosion resistance and high electrical conductivity. Offering higher strength levels than 5052 or 5083, DIN 3.3545 becomes stronger with stain hardening and cold working, all while remaining a cost-effective choice. It can be welded with conventional methods, though electric arc welding is preferred.
Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.66 g/cm³ | H111 | EN 573-3, EN 14286, EN 485, EN 754, EN 755 |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Bending angle 180° | 1.0 °/t | H111 | EN 573-3, EN 485 | |
1.5 °/t | H111 | EN 573-3, EN 14286, EN 485 | ||
3.0 °/t | H111 | EN 573-3, EN 14286 | ||
Bending angle 90° | 0.5 °/t | H111 | EN 573-3, EN 485 | |
1.0 °/t | H111 | EN 573-3, EN 485 | ||
1.5 °/t | H111 | EN 573-3, EN 485 | ||
2.5 °/t | H111 | EN 573-3, EN 485 | ||
Elastic modulus | 71.0 GPa | H111 | EN 573-3, EN 14286, EN 485, EN 754, EN 755 | |
Hardness, Brinell | 65.0 [-] | H111 | EN 573-3, EN 485 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||
Shear modulus | 26.7 GPa | H111 | EN 573-3, EN 14286, EN 485, EN 754, EN 755 | |
Tensile strength | 240.0 - 310.0 MPa | H111 | EN 573-3, EN 14286, EN 485 | |
240.0 - 320.0 MPa | H111 | EN 573-3, EN 754, EN 755 |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coefficient of thermal expansion | -50 °C | 2.2e-05 1/K | H111 | EN 573-3, EN 14286, EN 485, EN 754, EN 755 | |
20 °C | 2.2e-05 1/K | H111 | EN 573-3, EN 14286, EN 485, EN 754, EN 755 | ||
20 °C | 2.38e-05 1/K | H111 | EN 573-3, EN 14286, EN 485, EN 754, EN 755 | ||
20 °C | 2.4699999999999997e-05 1/K | H111 | EN 573-3, EN 14286, EN 485, EN 754, EN 755 | ||
20 °C | 2.58e-05 1/K | H111 | EN 573-3, EN 14286, EN 485, EN 754, EN 755 | ||
100 °C | 2.38e-05 1/K | H111 | EN 573-3, EN 14286, EN 485, EN 754, EN 755 | ||
200 °C | 2.4699999999999997e-05 1/K | H111 | EN 573-3, EN 14286, EN 485, EN 754, EN 755 | ||
300 °C | 2.58e-05 1/K | H111 | EN 573-3, EN 14286, EN 485, EN 754, EN 755 | ||
Max service temperature | 150.0 °C | Typical for Wrought 5000 Series Aluminium | |||
Melting point | 585.0 - 641.0 °C | H111 | EN 573-3, EN 14286, EN 485, EN 754, EN 755 | ||
585.0 - 640.0 °C | H111 | EN 573-3, EN 14286, EN 485, EN 754, EN 755 | |||
Specific heat capacity | 900.0 J/(kg·K) | H111 | EN 573-3, EN 14286, EN 485, EN 754, EN 755 | ||
Thermal conductivity | 120.0 - 140.0 W/(m·K) | H111 | EN 573-3, EN 14286, EN 485, EN 754, EN 755 | ||
126 W/(m·K) | H111 | EN 573-3, EN 14286, EN 485, EN 754, EN 755 |
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 17000000.0 - 19000000.0 S/m | H111 | EN 573-3, EN 14286, EN 485, EN 754, EN 755 |
18000000.0 S/m | H111 | EN 573-3, EN 14286, EN 485, EN 754, EN 755 | |
Electrical resistivity | 5.26e-08 - 5.88e-08 Ω·m | H111 | EN 573-3, EN 14286, EN 485, EN 754, EN 755 |
5.56e-08 Ω·m | H111 | EN 573-3, EN 14286, EN 485, EN 754, EN 755 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Chromium | 0.05 - 0.25 % | H111 | EN 573-3, EN 14286, EN 485, EN 754, EN 755 |
Copper | 0.1 % | H111 | EN 573-3, EN 14286, EN 485, EN 754, EN 755 |
Iron | 0.50 % | H111 | EN 573-3, EN 14286, EN 485, EN 754, EN 755 |
Magnesium | 3.5 - 4.5 % | H111 | EN 573-3, EN 14286, EN 485, EN 754, EN 755 |
Manganese | 0.2 - 0.7 % | H111 | EN 573-3, EN 14286, EN 485, EN 754, EN 755 |
Silicon | 0.4 % | H111 | EN 573-3, EN 14286, EN 485, EN 754, EN 755 |
Titanium | 0.15 % | H111 | EN 573-3, EN 14286, EN 485, EN 754, EN 755 |
Zinc | 0.25 % | H111 | EN 573-3, EN 14286, EN 485, EN 754, EN 755 |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | decorative: acceptable, Protective: very good | |
| Brazing | hard brazing (with flux/ without flux): poor / sufficient, friction soldering: acceptable, soft brazing with flux: poor | |
| Workability | Bending / Spinning (cold): good / sufficient, Impact extrusion (cold): sufficient, Deep drawing / upsetting (Condition) good (O) / good (O) | |
Metal
- EN 573-3 Grade 3.0915 (H111) – Premium Aluminium Alloy
- EN 573-3 Grade 3.3326 H111 – Detailed Mechanical Properties of 5000 Series Aluminium
- EN 573-3 Grade 3.0505 H111 Aluminium Alloy - Technical Specifications
- AW‑5186 H111 Aluminium Alloy – EN 573‑3 Certified for High‑Performance Applications
- EN 573-3 Grade 3.0257 H111 Aluminium Alloy Specifications
- EN 573-3 Grade 3.3549 H111 Aluminium Alloy – Technical Specifications and R&D Services
- EN 573-3 Grade 3.1325 H111 – Aluminium Alloy Properties & Standards
- EN 573-3 Grade 3.2315 H111 – Detailed Aluminium Alloy Specifications
- EN 573-3 Grade 3.0515 H111 Steel – Comprehensive Properties & Compliance
- EN 573-3 Grade 3.0525 H111 – High-Quality Aluminum Alloy for Industrial Applications