DIN 1725-1 Grade 3.3545 H12 Aluminum Alloy – High Strength & Corrosion Resistance
Aluminum DIN 3.3545 is structural alloy, which offers users strong corrosion resistance and high electrical conductivity. Offering higher strength levels than 5052 or 5083, DIN 3.3545 becomes stronger with stain hardening and cold working, all while remaining a cost-effective choice. It can be welded with conventional methods, though electric arc welding is preferred.
Properties
General
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Density | 2.66 g/cm³ | H12 | EN 573-3, EN 1592, EN 485, EN 754 | ||
20.0 °C | 2.66 g/cm³ | H12 | DIN 1725-1, EN 573-3, EN 573-4 | Sheet |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Bending Fatigue Strength | 130.0 MPa | H12 | EN 573-3, EN 1592, EN 485, EN 754 | |||
Elastic modulus | 71.0 GPa | H12 | EN 573-3, EN 1592, EN 485, EN 754 | |||
20.0 °C | 72.0 GPa | H12 | DIN 1725-1, EN 573-3, EN 573-4 | Sheet | ||
Elongation | 3.0 % | H12 | EN 573-3, EN 485 | A50 | ||
4.0 % | H12 | EN 573-3, EN 485, EN 754 | A50 | |||
5.0 % | H12 | EN 573-3, EN 754 | A100 | |||
5.0 % | H12 | EN 573-3, EN 485 | A50 | |||
6.0 % | H12 | EN 573-3, EN 485 | A100 | |||
6.0 % | H12 | EN 573-3, EN 485 | A50 | |||
7.0 % | H12 | EN 573-3, EN 485 | A50 | |||
9.0 % | H12 | EN 573-3, EN 1592 | A100 | |||
20.0 °C | 7.0 % | H12 | DIN 1725-1, EN 573-3, EN 573-4 | Sheet | ||
Hardness, Brinell | 81.0 [-] | H12 | EN 573-3, EN 485 | |||
20.0 °C | 80.0 [-] | H12 | DIN 1725-1, EN 573-3, EN 573-4 | Sheet | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||||
Poisson's ratio | 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||||
Shear modulus | 26.7 GPa | H12 | EN 573-3, EN 1592, EN 485, EN 754 | |||
20.0 °C | 27.0 GPa | H12 | DIN 1725-1, EN 573-3, EN 573-4 | Sheet | ||
Tensile strength | 270.0 MPa | H12 | EN 573-3, EN 1592, EN 754 | |||
275.0 - 335.0 MPa | H12 | EN 573-3, EN 485 | ||||
20.0 °C | 275.0 - 330.0 MPa | H12 | DIN 1725-1, EN 573-3, EN 573-4 | Sheet |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Coefficient of thermal expansion | -50 °C | 2.2e-05 1/K | H12 | EN 573-3, EN 1592, EN 485, EN 754, DIN 1725-1, EN 573-4 | Sheet | |
-50.0 °C | 2.2e-05 1/K | H12 | EN 573-3, EN 1592, EN 485, EN 754, DIN 1725-1, EN 573-4 | Sheet | ||
20 °C | 2.2e-05 1/K | H12 | EN 573-3, EN 1592, EN 485, EN 754, DIN 1725-1, EN 573-4 | Sheet | ||
20 °C | 2.38e-05 1/K | H12 | EN 573-3, EN 1592, EN 485, EN 754, DIN 1725-1, EN 573-4 | Sheet | ||
20 °C | 2.4699999999999997e-05 1/K | H12 | EN 573-3, EN 1592, EN 485, EN 754 | |||
20 °C | 2.58e-05 1/K | H12 | EN 573-3, EN 1592, EN 485, EN 754, DIN 1725-1, EN 573-4 | Sheet | ||
100 °C | 2.38e-05 1/K | H12 | EN 573-3, EN 1592, EN 485, EN 754, DIN 1725-1, EN 573-4 | Sheet | ||
100.0 °C | 2.38e-05 1/K | H12 | EN 573-3, EN 1592, EN 485, EN 754, DIN 1725-1, EN 573-4 | Sheet | ||
200 °C | 2.4699999999999997e-05 1/K | H12 | EN 573-3, EN 1592, EN 485, EN 754 | |||
200.0 °C | 2.47e-05 1/K | H12 | DIN 1725-1, EN 573-3, EN 573-4 | Sheet | ||
300 °C | 2.58e-05 1/K | H12 | EN 573-3, EN 1592, EN 485, EN 754, DIN 1725-1, EN 573-4 | Sheet | ||
300.0 °C | 2.58e-05 1/K | H12 | EN 573-3, EN 1592, EN 485, EN 754, DIN 1725-1, EN 573-4 | Sheet | ||
Max service temperature | 150.0 °C | Typical for Wrought 5000 Series Aluminium | ||||
Melting point | 585.0 - 641.0 °C | H12 | EN 573-3, EN 1592, EN 485, EN 754 | |||
585.0 - 640.0 °C | H12 | EN 573-3, EN 1592, EN 485, EN 754 | ||||
Specific heat capacity | 900.0 J/(kg·K) | H12 | EN 573-3, EN 1592, EN 485, EN 754 | |||
20.0 °C | 900.0 J/(kg·K) | H12 | DIN 1725-1, EN 573-3, EN 573-4 | Sheet | ||
Thermal conductivity | 126 W/(m·K) | H12 | EN 573-3, EN 1592, EN 485, EN 754 | |||
20.0 °C | 120.0 - 140.0 W/(m·K) | H12 | DIN 1725-1, EN 573-3, EN 573-4, EN 1592, EN 485, EN 754 | Sheet |
Electrical
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Electrical conductivity | 18000000.0 S/m | H12 | EN 573-3, EN 1592, EN 485, EN 754 | ||
20.0 °C | 17000000.0 - 19000000.0 S/m | H12 | DIN 1725-1, EN 573-3, EN 573-4, EN 1592, EN 485, EN 754 | Sheet | |
Electrical resistivity | 5.26e-08 - 5.88e-08 Ω·m | H12 | EN 573-3, EN 1592, EN 485, EN 754 | ||
5.56e-08 Ω·m | H12 | EN 573-3, EN 1592, EN 485, EN 754 |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Chromium | 0.05 - 0.25 % | H12 | DIN 1725-1, EN 573-3, EN 573-4, EN 1592, EN 485, EN 754 | Sheet |
Copper | 0.1 % | H12 | DIN 1725-1, EN 573-3, EN 573-4, EN 1592, EN 485, EN 754 | Sheet |
Iron | 0.5 % | H12 | DIN 1725-1, EN 573-3, EN 573-4 | Sheet |
0.50 % | H12 | EN 573-3, EN 1592, EN 485, EN 754 | ||
Magnesium | 3.5 - 4.5 % | H12 | DIN 1725-1, EN 573-3, EN 573-4, EN 1592, EN 485, EN 754 | Sheet |
Manganese | 0.2 - 0.7 % | H12 | DIN 1725-1, EN 573-3, EN 573-4, EN 1592, EN 485, EN 754 | Sheet |
Silicon | 0.4 % | H12 | DIN 1725-1, EN 573-3, EN 573-4, EN 1592, EN 485, EN 754 | Sheet |
Titanium | 0.15 % | H12 | DIN 1725-1, EN 573-3, EN 573-4, EN 1592, EN 485, EN 754 | Sheet |
Zinc | 0.25 % | H12 | DIN 1725-1, EN 573-3, EN 573-4, EN 1592, EN 485, EN 754 | Sheet |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | decorative: acceptable, Protective: very good | |
| Brazing | hard brazing (with flux/ without flux): poor / sufficient, friction soldering: acceptable, soft brazing with flux: poor | |
| Workability | Bending / Spinning (cold): good / sufficient, Impact extrusion (cold): sufficient, Deep drawing / upsetting (Condition) good (O) / good (O) | |
Metal
- DIN 1725-1 Grade 3.4415 – High-Performance Al–Zn Alloy for Corrosion Protection
- DIN 1725-1 Grade 3.3547 H12 Aluminium Profile – High Strength, Precision Engineering
- DIN 1725-1 Grade 3.2315 T5 Aluminum Tube – Technical Specifications
- DIN 1725-1 Grade 3.4365 T5 – High‑Strength 7075 Aluminum Alloy for Aerospace
- DIN 1725‑1 Grade 3.4365 O – Premium High‑Strength Aluminum Alloy for Aerospace
- DIN 1725-1 Grade 3.4335 T5 Aluminum Alloy – High-Performance Wrought Grade
- DIN 1725-1 Grade 3.3211 T8 Alloy: Superior Corrosion Resistance & Finish
- DIN 1725-1 Grade 3.0615 T8: High-Performance Free-Cutting Alloy
- DIN 1725-1 Grade 3.1255 T8 Aluminum Alloy – High Strength & Precision Machining
- DIN 1725-1 Grade 3.3315 H12 AlMg Alloy: Superior Corrosion Resistance & Weldability