DIN 1725-1 Grade 3.3547 H12 Aluminium Profile – High Strength, Precision Engineering
Additional services: Cuttings, Parts from drawings
ALUDIUM
MANUFACTURER
Information and services
Quantity: One truck load – Specialty products on request.Additional services: Via Cindal (the Aludium R&D department): R&D services, benchmarking, chemical audits, material specification, process optimisation, quality monitoring, sample analysis, prototyping, trainingProperties
General
| Property | Value | Comment |
|---|---|---|
Density | 2.65 - 2.7 g/cm³ | Typical for Wrought 5000 Series Aluminium |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Elastic modulus | 69.0 - 70.0 GPa | Typical for Wrought 5000 Series Aluminium | ||||
Elongation | 20.0 °C | 14.0 % | H12 | DIN 1725-1 | Sheet | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||||
Poisson's ratio | 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||||
Reduction of area | 20.0 °C | 20.0 % | H12 | DIN 1725-1 | Sheet | |
Shear modulus | 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | ||||
Tensile strength | 20.0 °C | 310.0 MPa | H12 | DIN 1725-1 | Sheet |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 2.2e-05 - 2.5e-05 1/K | Typical for Wrought 5000 Series Aluminium |
Max service temperature | 150.0 °C | Typical for Wrought 5000 Series Aluminium |
Melting point | 560.0 - 655.0 °C | Typical for Wrought 5000 Series Aluminium |
Specific heat capacity | 879.0 - 963.0 J/(kg·K) | Typical for Wrought 5000 Series Aluminium |
Thermal conductivity | 112.0 - 205.0 W/(m·K) | Typical for Wrought 5000 Series Aluminium |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 18000000.0 - 31000000.0 S/m | Typical for Wrought 5000 Series Aluminium |
Electrical resistivity | 3.3e-08 - 5e-08 Ω·m | Typical for Wrought 5000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Chromium | 0.05 - 0.25 % | H12 | DIN 1725-1 | Sheet |
Copper | 0.1 | H12 | DIN 1725-1 | Sheet |
Iron | 0.4 | H12 | DIN 1725-1 | Sheet |
Magnesium | 4.0 - 4.9 % | H12 | DIN 1725-1 | Sheet |
Manganese | 0.3 - 1.0 % | H12 | DIN 1725-1 | Sheet |
Silicon | 0.4 | H12 | DIN 1725-1 | Sheet |
Titanium | 0.15 | H12 | DIN 1725-1 | Sheet |
Zinc | 0.25 | H12 | DIN 1725-1 | Sheet |
Technological properties
| Property | ||
|---|---|---|
| Workability | Good workability. | |
Metal
- DIN 1725-1 Grade 3.4415 – High-Performance Al–Zn Alloy for Corrosion Protection
- DIN 1725-1 Grade 3.3547 H112 Aluminium – Premium 5000 Series with Full R&D & Custom Services
- DIN 1725-1 Grade 3.2315 T5 Aluminum Tube – Technical Specifications
- DIN 1725-1 Grade 3.4365 T5 – High‑Strength 7075 Aluminum Alloy for Aerospace
- DIN 1725‑1 Grade 3.4365 O – Premium High‑Strength Aluminum Alloy for Aerospace
- DIN 1725-1 Grade 3.4335 T5 Aluminum Alloy – High-Performance Wrought Grade
- DIN 1725-1 Grade 3.3547 H18 – Premium Cold-Worked AlMg4.5Mn Alloy with Superior Corrosion Resistance
- DIN 1725-1 Grade 3.3315 H12 AlMg Alloy: Superior Corrosion Resistance & Weldability
- DIN 1725-1 Grade 3.3545 H12 Aluminum Alloy – High Strength & Corrosion Resistance
- DIN 1725-1: Grade 3.0525 H12 Aluminum Alloy – High Strength & Corrosion Resistance